Ti–CrNi alloy coatings with 20, 40, 60 and 80 at-%Ni were prepared on Ti6Al4V alloy surface by double glow plasma surface alloying technique. The cyclic oxidation behaviour of the coatings was investigated at 750, 850 and 950°C. The results show that each coating has a complete structure of settled layer, mutual diffusion layer and sputtering affected zone. When the Ni content was 40 at-%, the Ti–CrNi alloy coating showed the best cyclic oxidation resistance. The oxide scale with ‘Cr2O3 film+NiO film’ structure showed the best resistance to peeling.
TurnerMW, CrousePL, LiL, . Investigation into CO2 laser cleaning of titanium alloys for gas-turbine component manufacture. Appl Surf Sci. 2006;252:4798–4802.
2.
HudaZ, EdiP.Materials selection in design of structures and engines of supersonic aircrafts: A review. Mater Des. 2013;46:552–560.
3.
ShoesmithDW, NoëlJJ.3.10 – corrosion of titanium and its alloys, in Shreir's Corrosion, 2042–2052. Oxford: Elsevier; 2010.
4.
ParthasarathyTA, PorterWJ, BooneS, . Life prediction under tension of titanium alloys that develop an oxygenated brittle case during use. Scr Mater. 2011;65:420–423.
5.
ZhaoYQ, ZhouL, DengJ.The role of interface in the burning of titanium alloys. Mater Sci Eng A. 1999;A267:167–170.
YankovRA, KolitschA, von BoranyJ, . Surface protection of titanium and titanium–aluminum alloys against environmental degradation at elevated temperatures. Surf Coat Technol. 2012;206:3595–3600.
8.
MajumdarJD, MannaI.21 – laser surface engineering of titanium and its alloys for improved wear, corrosion and high-temperature oxidation resistance. Woodhead Publishing Series in Electronic and Optical Materials; LawrenceJ & WaughDG, (eds). Oxford
: Woodhead Publishing; 2015. pp. 483–521.
AttardB, MatthewsA, LeylandA, . Enhanced surface performance of Ti–6Al–4V alloy using a novel duplex process combining PVD-Al coating and triode plasma oxidation. Surf Coat Technol. 2014;257:154–164.
11.
LeyensC, PetersM, HovsepianPEh, . Novel coating systems produced by the combined cathodic arc/unbalanced magnetron sputtering for environmental protection of titanium alloys. Surf Coat Technol. 2002;155:103–111.
12.
XuJ, LiZ, ZhuW, . The comparative study of thermal fatigue behavior of laser deep penetration spot cladding coating and brush plating Ni–W–Co coating. Appl Surf Sci. 2006;253:2618–2624.
13.
YaoJ, HeY, WangD, . High-temperature oxidation resistance of (Al2O3–Y2O3)/(Y2O3-stabilized ZrO2) laminated coating on 8Nb–TiAl alloy prepared by a novel spray pyrolysis. Corros Sci. 2014;80:19–27.
14.
SarkarS, DattaS, DasS, . Oxidation protection of gamma-titanium aluminide using glass–ceramic coatings. Surf Coat Technol. 2009;203:1797–1805.
LiX, TangB, YeJ.Fabrication of Zr and Zr–N surface alloying layers and hardness improvement of Ti–6Al–4V alloy by plasma surface alloying technique. Appl Surf Sci. 2012;258:1981–1984.
17.
WeiDB, ZhangPZ, YaoZJ, . Oxidation of double-glow plasma chromising coating on TC4 titanium alloys. Corros Sci. 2013;66:43–50.
18.
WeiDB, ZhangPZ, YaoZJ, . Cyclic oxidation behavior of plasma surface chromising coating on titanium alloy Ti–6Al–4V. Appl Surf Sci. 2012;261:800–806.
19.
PengXM, XiaCQ, DaiXY, . Ablation behavior of NiCrAlY coating on titanium alloy muzzle brake. Surf Coat Technol. 2013;232:690–694.
20.
DoğanÖN, SongX, ChenS, . Microstructural study of high-temperature Cr–Ni–Al–Ti alloys supported by first-principles calculations. Intermetallics. 2013;35:33–40.
UnocicKA, PintBA.Oxidation behavior of co-doped NiCrAl alloys in dry and wet air. Surf Coat Technol. 2013;237:8–15.
23.
WangQ, ZhangP-Z, WeiD-B, . Microstructure and corrosion resistance of pure titanium surface modified by double-glow plasma surface alloying. Mater Des. 2013;49:1042–1047.
24.
BentzBL, HarrisonWW.Negative ions of sputtered cathode species in a glow discharge. Int J Mass Spectrom Ion Phys. 1981;37:167–176.
25.
ZaporozchenkoVI, StepanovaMG.Preferential sputtering in binary targets. Prog Surf Sci. 1995;49:155–196.
26.
MasonRS, AndersonPDJ, FernandezMT.Observation and lifetime of autoionising states of Ar produced in a glow discharge ion source. Int J Mass Spectrom Ion Processes. 1993;128:99–105.
27.
BradyMP, SmialekJL, SmithJ.The role of Cr in promoting protective alumina scale formation by γ-based Ti–Al–Cr alloys – I. Compatibility with alumina and oxidation behavior in oxygen. Acta Mater. 1997;45:2357–2369.