Statistical optimisation of trivalent chromium bath and characterisation of coating defects

Abstract

The influences of chemicals used in the Cr electrodeposition bath on the brightness and efficiency of Cr coating were studied using fractional factorial design of experimental method. Cr coating defects that emerged during the coating were investigated using a scanning electron microscope (SEM). Analysis of variance test was performed to check the accuracy of each effect in the statistical studies. The statistical results show that boric acid enhances the efficiency and thickness of Cr coating the most. The stability of Cr coating is dependent on two parameters: pH and Cr⁺³ ion concentration in the Cr III bath. SEM images and energy dispersive spectroscopy measurements showed that the blackness and dullness defects on Cr coating are due to the emergence of chromium (III) sulphide (Cr₂S₃) and fast hydrogen evolution on Cr coating.

Keywords

Trivalent chromium coating Saccharin Malonic acid Chromium coating defects Electroplating

Get full access to this article

View all access options for this article.

References

Giovanardi

and Orlando

: ‘Chromium electrodeposition from Cr(III) aqueous solutions’, Surf. Coat. Technol., 2011, 205, 3947–3955.

Zeng

, Zhang

, Zhao

and Zhang

: ‘Role of complexing ligands in trivalent chromium electrodeposition’, Surf. Coat. Technol., 2011, 205, 4771–4775.

Phuong

, Kwon

, Lee

, Shin

, Huy

and Lee

: ‘Mechanistic study on the effect of PEG molecules in a trivalent chromium electrodeposition process’, Microchem. J., 2011, 99, 7–14.

Lee

, Kim

and Kwon

: ‘Effect of polyethylene glycol on electrochemically deposited trivalent chromium layers’, Trans. Nonferrous Met. Soc. China, 2009, 19, 819–823.

Phuong

, Kwon

, Lee

and Lee

: ‘The effects of pH and polyethylene glycol on the Cr(III) solution chemistry and electrodeposition of chromium’, Surf. Coat. Technol., 2012, 206, 4349–4355.

Survilien

, Nivinskien

, Unien

and Selkis

: ‘Effect of Cr(III) solution chemistry on electrodeposition of chromium’, J. Appl. Electrochem., 2006, 36, 649–654.

Katırcı

: ‘A chrome coating from a trivalent chromium bath containing extremely low concentration of Cr3+ ions’, Int. J. Surf. Sci. Eng., 2014.

Zeng

, Suna

and Zhanga

: ‘The electrochemical reduction mechanism of trivalent chromium in the presence of formic acid’, Electrochem. Commun., 2009, 11, 331–334.

Kim

, Lee

and Park

: ‘Effects of organic additives on zinc electrodeposition at iron electrodes studied by EQCM and in situ STM’, Langmuir, 2004, 20, (2), 459–466.

10.

Rashkov

, Monev

and Atanassov

: ‘A possibility to obtain microdiscontinuous chromium coatings by cathodic treatment in acidic media’, Surf. Technol., 1983, 18, (3), 201–207.

11.

Etminanfar MR and Hydarzadeh Sohi

: ‘Corrosion resistance of multilayer coatings of nanolayered Cr/Ni electrodeposited from Cr(III)-Ni(II) bath’, Thin Solid Films, 2012, 520, 5322–5327.

12.

http://en.wikipedia.org/wiki/Glossmeter

13.

http://en.wikipedia.org/wiki/Chromium(III)_sulfide