An attempt was made to improve the localised corrosion resistance of AISI type 304 stainless steel by modifying the surface with duplex coating (titania over ceria). Simple chemical immersion method was adopted for ceria coating, whereas sol–gel route with dip coating method was followed for titania coating. The adherence of the coating was evaluated by ASTM D3359 standard, and the composition of the duplex coatings was evaluated by X-ray photoelectron spectroscopy. The experimental parameters, namely, bath composition, temperature, immersion time and withdrawal speed of the specimens, were optimised to get homogeneous adherent coating. The localised corrosion resistance of ceria, titania and duplex coatings in sea water was studied by potentiodynamic anodic polarisation experiments. These coatings were characterised also by optical and scannning electron microscopes for analysing their pit morphologies. Duplex coated 304 SS exhibited superior corrosion resistance, and the probable reason for the improvement is discussed in detail in this investigation.
John SedriksA: ‘Corrosion of stainless steels’, 2nd edn; 1996, New York, John Wiley & Sons.
2.
ShankarP and Kamachi MudaliU: ‘Surface modification for corrosion protection of austenitic stainless steels’, in ‘Corrosion of austenitic stainless steel’, (ed. KhatakH S and RajB), 340; 2002, New Delhi, Narosa Publishers.
3.
RajB and Kamachi MudaliU: ‘Surface science and engineering relevant to fast breeder reactor and fuel cycle technologies’, in ‘Surface modification technologies’, (ed. SudarshanT S et al.), Vol. 23, 3–12; 2010, Chennai, Valardocs.
4.
PadhyN: ‘Role of passivity and surface modification on the corrosion behaviour of AISI 304L SS in nitric acid medium’, PhD thesis, HBNI, Mumbai, India, 2010, 116.
5.
XuJ, ZhouC, ChenZ, WangY and JiangS: J. Alloys Compd, 2010, 496, (1–2), 429–432.
6.
Kamachi MudaliU, SridharTM and RajendranN: Surf. Eng., 2007, 23, 267–272.
7.
Kamachi MudaliU, NingshenS and Ravi ShankarA: Pure Appl. Chem., 2011, 83, (11), 2079–2087.
CheraghiH, ShahmiriM and SadeghianZ: Thin Solid Films, 2012, 522, 289–296.
12.
BamoulidL, MauretteMT, De CaroD, GuenbourA, Ben BachirA, AriesL, El HajjajiS, Benoit-MarqueF and AnsartF: Surf. Coat. Technol., 2008, 202, (20), 5020–5026.
GhasemiA, ShahrabiT, OskuieAA, HasannejadH and SanjabiS: J. Alloys Compd, 2010, 504, (1), 237–242.
32.
HintonBRW, PolloackWJ, TrathenPN and CroskyA: Corros. Australas., 1987, 13, 12–17.
33.
WangC, JiangF and WangF: Corros. Sci., 2004, 46, 75–89.
34.
EyringJ: ‘Handbook on the physics and chemistry of rare earth’, Vol. 3, 337; 1979, North-Holland Publishing Company, Amsterdam, The Netherlands.
35.
YaholomJ, IvesLK and KrugerJ: J. Electrochem. Soc., 1973, 130, 384.
36.
IsaacsHS and KisselG: J. Electrochem. Soc., 1972, 119, 1628.
37.
FrankelGS, StockertL, HunkelerF and BoehniH: Corrosion, 1987, 43, 429.
38.
MankowskiJ and Szklarska-SmialowskaZ: Corros. Sci., 1975, 15, 493.
39.
SchwenkW: Corrosion, 1964, 20, 129
40.
SatoN, NakagawaT, KudoK and SakashitaM: ‘Chloride pitting dissolution of rotating SS electrode in acid solution’, Proc. U. R. Evans Conf. on ‘Localized corrosion’, (ed. StaehleR W et al.), 447; 1971, NACE, Houston, TX, USA.