Laser surface melting has been conducted on the surface of prior cold worked and aged AISI type 316 L(N) stainless steel specimens to homogenise the composition and as a result improve the corrosion resistance. Although the top layers of surface melted specimens did not show a marked improvement in corrosion resistance, the subsequent layers exposed after mild polishing showed a dramatic increase in pitting corrosion resistance and an appreciable improvement in intergranular and general corrosion. This is attributed to the dissolution of secondary phases in the melted and heat affected zones.
ParvathavarthiniN., Subba RaoR. V., KumarS., DayalR. K. and KhatakH. S.: J. Mater. Eng. Perform., 2001, 10, 5–13.
15.
PaulC. P., KumarH., ReghuT., BhargavaP. and NathA. K.: Proc. DAE-BRNS National Laser Symposium, Indore, India, December2001, Allied Publishers Ltd, pp. 51–52.
GrayR. J., SikkaV. K. and KingR. T.: J. Met., 1978, 30, 18–26.
18.
‘Standard test method for electrochemical reactivation (EPR) for detecting sensitization of AISI type 304 and 304L stainless steels’, ASTM standard G-108-94, ASTM, Philadelphia, PA, USA, 1999.
19.
RaviR.: ‘Sensitization studies on Nitrogen added 316 stainless steel and desensitization by Laser surface melting’, M Tech thesis, Department of Metallurgical and Materials Engineering, Karnataka Regional Engineering College, Surathkal, India, 2000.
20.
WeissB. and SticklerR.: Metall Trans., 1972, 3, 851–865.
21.
ShankarP., ShaikhH., SivakumarS., VenugopalS., SundararamanD. and KhatakH. S.: J. Nucl. Mater., 1999, 264, 29.
22.
CovinoB. S., CramerS. D., RusselJ. H. and SimmonsW. J.: Corrosion, 1997, 53, 525.
23.
SasikalaG.: Creep deformation and fracture behaviour of AISI type 316 L(N) stainless steel and its weld metal, PhD thesis, University of Madras, Chennai, India, 2001, p. 72.
24.
DayalR. K., ParvathavarthiniN. and RajB.: Int. Mater. Rev., 2005, 50, 129–155.
25.
CihalV. and StefecR.: Electrochem. Acta, 2001, 46, 3867–3877.
26.
ParvathavarthiniN., DayalR. K., RaviR. and KhatakH. S.: Trans. Ind Inst. Met, 2003, 56, 499–504.
27.
DongareS. T.: ‘Microstructural changes during thermal ageing of indigenous AISI 316 L(N) SS at 973K — A study using Electrochemical Potentiokinetic and Potentiostatic reactivation techniques’, MTech thesis, VNIT, Nagpur, India, 2005.
28.
CondeA., GarciaI. and de DamboreneaJ. J.: Corros. Sci., 2001, 43, 817–828.
29.
ColsonJ. C. and LarpinJ. P.: MRS Bull., 23 October1994.
30.
CihalV.: ‘Intergranular corrosion of steels and alloys’; 1984, Elsevier, Amsterdam.
31.
PanQ. Y., HuangW. D., SongR. G., ZhouY. H. and ZhangG. L.: Surf Coat. Technot, 1998, 102, 245–255.
32.
Curley-FlorinoM. E. and SchmidG. M.: Corros. Sci., 1980, 20, 313–329.
33.
FerreiraM. G. S. and DawsonJ. L.: J. Electrochem. Soc., 1985, 132, 760–765.
34.
OkamotoG. and ShibataT.: in ‘Passivity of metals’ (ed. FrankenthalR. P. and KrugerJ.), 646; 1978, Princeton, New York, The Electrochemical Society.
35.
AzzerriN.: Corros. Sci., 1982, 22, 867–876.
36.
YangW., ZhaoG., ZhangM. and CongletonJ.: Corros. Sci., 1992, 33, 89–102.
37.
PetitJ. A. and DabosiF.: Corros. Sci., 1980, 20, 745–760.