A flow formed C-250 maraging steel tubing was welded by electron beam welded (EBW) process and subsequently age hardened. Conventional EB welding with high energy input had resulted in seriously inadequate percentage elongation of the weldment. With an additional prewelding stress relief treatment and EBW with a lower energy input, the elongation of the weldment showed significant improvement after being treated with age hardening. It was found that the tensile strength was increased by 12% and the percentage elongation was remarkably increased by 92%.
LinnertG. E.: ‘Welding metallurgy’, 3rd edn, 517–570; 1967, New York, NY, American Welding Society.
2.
FloreenS.: ‘Metals handbook’, 9th edn, Vol. 1, 445–52; 1978, Metals Park, OH, American Society for Metals.
3.
AhmedM., AyubH., NasimI., HashmiF. H. and KhanA. Q.: Mater. Sci. Technol., 1995, 11, 1281–1286.
4.
HallA. M. and SlunderC. J.: ‘The metallurgy, behavior, and application of the 18-percent nickel maraging steels’, NASA Report SP-5051, Washington, DC, 1968.
5.
PepeJ. J. and SavageW. F.: Weld. Res. Suppl., 1967, 9, 411s–22s.
6.
LeeI. K.: ‘The effect of heat treatment on microstructure and mechanical properties of flow-formed maraging steel weldment by EBW’, PhD thesis, National Chiao Tung University, Hsinchu, Taiwan, 2002.
7.
LeeI. K., ChouC. P., ChengC. M. and KuoI. C.: Sci. Technol. Weld. Join., 2003, 8, 221–228.
8.
LeeY. J.: ‘The effect of lath microstructures on mechanical properties of flow-formed maraging steel weldment by electron beam welding’, Master's dissertation, National Chiao Tung University, Hsinchu, Taiwan, 2004.
9.
LeeY. J., LeeI. K., WuS. C., KungM. C. and ChouC. P.: Sci. Technol. Weld. Join., 2007, 12, 266–273(8).
10.
ChouC. P., TsaiP. C. and KuoI. C.: ‘Welding engineering’, 1st edn, 67–73; 1991, Taipei, Chuan Hwa Technology Publishing Company.