Effect of initial temper on mechanical properties of friction stir welded Al-2024 alloy

Abstract

The microstructural evolution and resultant mechanical properties during the friction stir welding (FSW) of precipitation strengthened aluminium alloys depend on initial temper as well as FSW process parameters. Al-2024 alloy under two different initial tempers, T3 and T8, was used in the present study. FSW bead-on-plate runs were performed at different values of process parameters (tool rotation rate and tool traverse speed). Microstructure and mechanical properties of the nugget region and heat affected zone (HAZ) were evaluated. Differential scanning calorimetry (DSC) revealed that in the nugget region, presence of Guinier–Preston–Bagaryatskii (GPB) zone results from the partial dissolution of Al₂CuMg phase. The microstructure and tensile properties were found to be independent of the initial temper of the material in the nugget region. In the HAZ region, tensile properties increased at higher heat index values for T3 condition, and decreased monotonically for T8 condition.

Keywords

ALUMINIUM ALLOYS WELDING DIFFERENTIAL SCANNING CALORIMETRY MICROSTRUCTURAL EVOLUTION TENSILE STRENGTH

Get full access to this article

View all access options for this article.

References

Thomas

W. M.

: ‘Friction stir butt welding’, International Patent App. No. PCT/GB92/02203 and GB Patent App. No. 9125978·8, US Patent No. 5460317, 1991.

Arbegast

W. J.

: ‘Modeling friction stir joining as a metal working process’, 313; 2003, Warrendale, PA, TMS.

Sellars

C. M.

and Mc

W. J.

Tegart

: Int. Met. Rev., 1972, 17, 1.

Arbegast

W. J.

: ‘Technology gaps that are stand in the place in taking Friction stir to a standard’, Presentation Proc. SAE Friction Stir Welding Symposium, Albuquerque, NM, USA, June 2004, SAE.

Silcock

M. J.

: J. Inst. Metal., 1960, 89, 203.

Ringer

S. P.

, Sakurai

and Polmear

I. J.

: Acta Mater., 1997, 45, 3731.

Wang

S. C.

and Starink

M. J.

: Mater. Sci. Eng. A, 2004, A386, 56.

Radmilovic

, Thomas

, Shiflet

G. J.

and Starke

E. A.

: Scr. Mater., 1989, 23, 1141.

Reich

, Ringer

S. P.

and Hono

: Philos. Mag. Lett., 1999, 79, (9), 639.

10.

Wang

S. C.

, Starink

M. J.

and Gao

: Scr. Mater., 2006, 54, 287.

11.

Genevois

, Deschamps

, Denquin

and Doisneau-cottignies

: Acta Mater., 2005, 53, 2447.

12.

Starink

M. J.

, Wang

S. C.

and Sinclair

: ‘Friction stir welding and processing III’, 233; 2005, San Francisco, CA, TMS.

13.

Karlsen

, Frigaard

Ø.

, Hjelen

, Grong

Ø.

and Norum

: Mater. Sci. Forum, 2003, 426–432, 2861.

14.

Jones

M. J.

, Heurtier

, Desrayaud

, Montheillet

, Allehaux

and Driver

J. H.

: Scr. Mater., 2005, 52, 693.

15.

Ehrström

J. C.

, Bigot

, Cervi

and Gerard

: Mater. Sci. Forum, 2003, 426–432, 2941.

16.

Heurtier

, Jones

M. J.

, Desrayaud

, Driver

J. H.

and Montheillet

: Mater. Sci. Forum, 2003, 426–432, 2927.

17.

Starink

M. J.

, Gao

, Davin

, Yan

and Cerezo

: Philos. Mag., 2005, 85, (13), 1395.

18.

Mishra

R. S.

and Ma

Z.Y.

: Mater. Sci. Eng. R, 2005, R50, (8), 1.

19.

Starink

M. J.

and Yan

: Proc. 1st Int. Symp. on ‘Metallurgical modeling for aluminum alloys’, 119, October 2003, Pittsburgh, PA, ASM.

20.

Starink

M. J.

and Gregson

P. J.

: Scr. Mater., 1995, 33, (6), 893.

21.

Gao

, Davin

, Wang

, Cerezo

and Starink

M. J.

: Mater. Sci. Forum, 2002, 396–402, 923.

22.

Starink

M. J.

, Gao

, Furukawa

, Horita

, Xu

and Langdon

T. G.

: Rev. Adv. Mater. Sci., 2004, 7, 1.

23.

Badini

, Mario

and Verne

: Mater. Sci. Eng. A, 1995, A191, 185.

24.

Starink

M. J.

: Int. Mater. Rev., 2004, 49, 191.