Laser pressure welding of Al alloy and low C steel

Abstract

This study was performed to obtain fundamental knowledge concerning the development of laser pressure welding technology for the joining of dissimilar metals. Laser pressure welding of Al alloy A6061 and low C steel SPCC sheets was carried out to investigate the effects of the roller pressure, laser beam scanning speed and irradiation position on the tensile shear and peel strength of welded joints. The interfaces of the joints were observed and analysed by SEM and EDX, and the formation phases on the peeled surfaces were identified with XRD. It was revealed that prevention and suppression of oxidation during welding was extremely important to the production of a sound joint with good mechanical properties. The highest tensile strength and the highest peel strength of joints were obtained at a laser power of 1·8 kW, laser scanning speed of 30 Hz, laser irradiation position at the centreline, roller pressure of more than 245 MPa and welding speed of 0·5 m min⁻¹ in an Ar atmosphere. The fracture occurred not in the welded zone but in the A6061 base alloy specimen.

Keywords

Get full access to this article

View all access options for this article.

References

Sepold

, Schubert

and Zerner

: ‘Laser beam joining of dissimilar materials’, 1–10; 1999, Lisbon, IIW.

Hiraga

, Fukatsu

, Ogawa

, Nakayama

and Mutoh

: Q. J. JWS, 2001, 19, (4), 717–726 (in Japanese).

Kutsuna

, Rathod

and Ammar

: Proc

ICALEO

2002, Scottdale, Arizona, USA, October 2002, Laser Institute of America, Section C, 14–17 (CD ROM).

Rathod

and Kutsuna

: Q. J. JWS, 2003, 21, (2), 282–294 (in Japanese).

Sepold

and Kreimeyer

: Proc. SPIE, 2003, 4831, 526–533.

Katayama

, Usui

and Matsunawa

: in Proc. 5th Int. Conf. ‘Trends in welding research’, (ed. J. M. Vitek, et al.), 467–472; 1998, Materials Park, OH, ASM International.

Katayama

and Mizutani

: in Proc. ICALEO 2003, Jacksonville, USA, October 2003, Laser Institute of America, Section E, 1401 (CD ROM).

Spold

, Rothe

and Teske

: Proc. Int. Congr. on ‘Laser advanced materials processing’, Osaka, Japan, May 1987, High Temperature Society of Japan, 151–156.

Yasuyama

, Ogawa

and Taka

: Q. J. JWS, 1996, 14, (2), 314–320 (in Japanese).

10.

Oikawa

, Saito

, Nagase

and Kiriyama

: J. Iron Steel Inst., 1997, 83, (10), 629–634 (in Japanese).