Evaluation of TIG flux welding on the characteristics of stainless steel

Abstract

The aim of the present study was to investigate the effect of specific oxide fluxes on the surface appearance, weld morphology, retained δ ferrite content, hot cracking susceptibility, angular distortion and mechanical properties obtained with the tungsten inert gas (TIG) process applied to the welding of 5 mm thick austenitic stainless steel plates. An autogenous gas tungsten arc welding process was applied to stainless steels through a thin layer of activating flux to produce a bead on plate welded joint. The MnO₂ and ZnO fluxes used were packed in powdered form. The experimental results indicated that the 80% MnO₂–20% ZnO mixture can give full penetration and also a satisfactory surface appearance for type 304 stainless steel TIG flux welds. TIG welding with MnO₂ and/or ZnO can increase the measured ferrite number in welds, and tends to reduce hot cracking susceptibility in as welded structures. It was also found that TIG flux welding can significantly reduce the angular distortion of stainless steel weldments.

Keywords

ANGULAR DISTORTION DELTA FERRITE HOT CRACKING SUSCEPTIBILITY STAINLESS STEEL TIG FLUX

Get full access to this article

View all access options for this article.

References

Lucas

and Howse

: Weld. Met. Fabr., 1996, 64, (1), 11–17.

Paskell

, Lundin

and Castner

: Weld. J., 1997, 76, (4), 57–62.

Tanaka

, Shimizu

, Terasaki

, Ushio

, Koshi-ishi

and Yang

C.-L.

: Sci. Technol. Weld. Joining, 2000, 5, (6), 397–402.

Kuo

, Sun

and Pan

: Sci. Technol. Weld. Joining, 2001, 6, (1), 17–22.

Dinechin

, Chagnot

, Castillan

, Blanchot

and Baude

: Weld. Int., 2002, 16, (9), 720–728.

Anderson

P. C. J.

and Wiktorowicz

: Weld. Met. Fabr., 1996, 64, (3), 108–109.

Paskell

, Lundin

and Castner

: Weld. J., 1997, 76, (4), 57–62.

Gurevich

S. M.

and Zamkov

V. M.

: Avt. Svarka, 1966, 12, 13–16.

Ogawa

and Tsunetomi

: Weld. J., 1982, 61, (3), 82–93.

10.

Brook

J. A.

: Weld. J., 1974, 53, (11), 517–523.

11.

Turner

P. W.

and Lundin

C. D.

: Weld. J., 1970, 49, (12), 579–587.

12.

Heiple

C. R.

and Roper

J. R.

: Weld. J., 1981, 60, (8), 143–145.

13.

Heiple

C. R.

and Roper

J. R.

: Weld. J., 1982, 61, (4), 97–102.

14.

Heiple

C. R.

, Roper

J. R.

, Stagner

R. T.

and Aden

R. J.

: Weld. J., 1983, 62, (3), 72–77.

15.

Heiple

C. R.

and Burgardt

: Weld. J., 1985, 64, (6), 159–162.

16.

Burgardt

and Heiple

C. R.

: Weld. J., 1986, 65, (6), 150–155.

17.

Tseng

K. H.

and Chou

C. P.

: Sci. Technol. Weld. Joining, 2001, 6, (3), 149–153.

18.

Tseng

K. H.

and Chou

C. P.

: J. Mater. Process. Technol., 2002, 123, 346–353.

19.

Tseng

K. H.

and Chou

C. P.

: Sci. Technol. Weld. Joining, 2002, 7, (1), 57–62.

20.

Long

C. J.

and Delong

W. T.

: Weld. J., 1973, 52, (7), 281–297.

21.

Pavlovsky

V. I.

and Masubuchi

: Weld. Res. Counc. Bull., 1994, 388, 44–48.