Effects of in situ nickel particle addition on the microstructure and microhardness of Sn–Ag solder

Abstract

In this study, various amounts of Ni particles were added in situ to Sn–3·5 wt-%Ag lead free solder to form new composite solders. Copper substrates were then dipped into these solders and aged at 150°C for 0, 25, 225, or 1000 h. The microstructure and microhardness of the as solidified solder and the aged solder/copper couples were investigated. Experimental results revealed that the addition of Ni particles increased the microhardness of the composite solder. Ni additions of less than 3 wt-% yielded a microstructure of β-Sn grains surrounded by a eutectic mixture of Ag₃Sn and a Sn rich matrix. An intermetallic compound of Ni₃Sn₄ particles was dispersed throughout the eutectic. For 5 wt-%Ni addition, the Ni₃Sn₄ phase and the remaining Ni particles were agglomerated. In the case of copper substrate dipped with a thick layer of composite solder, water quenched and then aged at 150°C, the induced (Ni, Cu)₃Sn₄ particles coarsened and agglomerated. Additionally, the intermetallic (Cu, Ni)₆Sn₅ compound layer formed at the solder/Cu interface thickened with increasing Ni content.