The sintering behaviour of a titanium aluminide alloy (Ti–45Al–5Nb–0.2B–0.2C in at.-%) with variations in the aluminium content was investigated. Additions of pure titanium to prealloyed powder of the starting composition were used to decrease the aluminium content to 43 and 44 at.-%, while additions of elemental aluminium increased it to 46 and 47 at.-%. Although the microstructures obtained were always fully lamellar, the porosity levels were different indicating a change in the sintering behaviour induced by the additions of elemental powders. Titanium additions lowered the optimum sintering temperatures, while aluminium additions shifted it to higher values. A reaction between the titanium aluminide prealloyed powder and pure aluminium was found to critically affect the sintering process.
TetsuiT.: ‘Development of a TiAl turbocharger for passenger vehicles’, Mater. Sci. Eng. A, 2002, A329–A331, 582–588. doi: 10.1016/S0921-5093(01)01584-2
2.
WuX.: ‘Review of alloy and process development of TiAl alloys’, Intermetallics, 2006, 14, 1114–1122. doi: 10.1016/j.intermet.2005.10.019
FroesF. H., SuryanarayanaC. and EliezerD.: ‘Synthesis, properties and applications of titanium aluminides’, J. Mater. Sci., 1992, 27, 5113–5140. doi: 10.1007/BF02403806
LeyensC. and PetersM. ‘in Titanium and titanium alloys’, (ed.); 2003, Wiley-VCH Verlag GmbH & Co. KGaA.
7.
LimbergW., EbelT., PyczakF., OehringM. and SchimanskyF. P.: ‘Influence of the sintering atmosphere on the tensile properties of MIM-processed Ti 45Al 5Nb 0.2B 0.2C’, Mater. Sci. Eng. A, 2012, A552, 323–329. doi: 10.1016/j.msea.2012.05.047
8.
ZhangH., HeX., QuX. and ZhaoL.: ‘Microstructure and mechanical properties of high Nb containing TiAl alloy parts fabricated by metal injection molding’, Mater. Sci. Eng. A, 2009, A526, 31–37. doi: 10.1016/j.msea.2009.07.003
PaulJ. D. H., AppelF. and WagnerR.: ‘The compression behaviour of niobium alloyed γ-titanium alumindes’, Acta Mater., 1998, 46, 1075–1085. doi: 10.1016/S1359-6454(97)00332-7
11.
HuangS.-C. and HallE. L.: ‘Plastic deformation and fracture of binary TiAl-base alloys’, Metall. Trans. A, 1991, 22A, 427–439. doi: 10.1007/BF02656810
12.
ImayevR. M., ImayevV. M., OehringM. and AppelF.: ‘Alloy design concepts for refined gamma titanium aluminide based alloys’, Intermetallics, 2007, 15, 451–460. doi: 10.1016/j.intermet.2006.05.003
13.
JinY., WangJ. N., YangJ. and WangY.: ‘Microstructure refinement of cast TiAl alloys by ß solidification’, Scr. Mater., 2004, 51, 113–117. doi: 10.1016/j.scriptamat.2004.03.044
14.
WangY., LiuY., YangG., LiH. and TangB.: ‘Microstructure of cast γ-TiAl based alloy solidified from β phase region’, Trans. Nonferr. Met. Soc. China, 2011, 21, 215–222. doi: 10.1016/S1003-6326(11)60702-4
15.
MirjaliliM., SoltaniehM., MatsuuraK. and OhnoM.: ‘On the kinetics of TiAl3 intermetallic layer formation in the titanium and aluminum diffusion couple’, Intermetallics, 2013, 32, 297–302. doi: 10.1016/j.intermet.2012.08.017
16.
MichaelsenC., WöhlertS. and BormannR.: ‘Phase formation and microstructural development during solid-state reactions in Ti–Al multilayer films’, MRS Proc., 1994, 343, 205–210. doi: 10.1557/PROC-343-205
17.
WohlertS. and BormannR.: ‘Phase selection governed by different growth velocities in the early stages of the Ti/Al phase reaction’, J. Appl. Phys., 1999, 85, 825–832. doi: 10.1063/1.369167
18.
DahmsM., LeitnerG., PoessneckerW., SchultrichS. and SchmelzerF.: ‘Pore formation during reactive sintering of extruded titanium aluminum powder mixtures’, Z. Metallkd, 1993, 84, 351–357.
19.
RawersJ. C. and WrzesinskiW. R.: ‘Reaction-sintered hot-pressed TiAl’, J. Mater. Sci., 1992, 27, 2877–2886. doi: 10.1007/BF01154095
20.
WangG.-X. and DahmsM.: ‘Reaction sintering of cold-extruded elemental powder mixture Ti-48Al’, Metall. Trans. A, 1993, 24A, 1517–1526. doi: 10.1007/BF02646592
21.
LeeT., KimJ. and HwangS. K.: ‘Direct consolidation of γ-TiAl–Mn–Mo from elemental powder mixtures and control of porosity through a basic study of powder reactions’, Metall. Mater. Trans. A, 1997, 28A, 2723–2729. doi: 10.1007/s11661-997-0029-2
22.
LeeT. K., MosunovE. I. and HwangS. K.: ‘Consolidation of a gamma TiAl–Mn–Mo alloy by elemental powder metallurgy’, Mater. Sci. Eng. A, 1997, A239–A240, 540–545. doi: 10.1016/S0921-5093(97)00628-X
23.
WangG.-X. and DahmsM.: ‘An effective method for reducing porosity in the titanium aluminide alloy Ti52Al48 prepared by elemental powder metallurgy’, Scr. Metall. Mater., 1992, 26, 1469–1474. doi: 10.1016/0956-716X(92)90668-5
24.
OhJ., PyoS. G., LeeS. and KimN. J.: ‘Fabrication of multilayered titanium aluminide sheets by self-propagating high-temperature synthesis reaction using hot rolling and heat treatment’, J. Mater. Sci., 2003, 38, 3647–3651. doi: 10.1023/A:1025637600400
25.
YiH. C., PetricA. and MooreJ. J.: ‘Effect of heating rate on the combustion synthesis of Ti–Al intermetallic compounds’, J. Mater. Sci., 1992, 27, 6797–6806. doi: 10.1007/BF01165971