Ordered B2-NiAl intermetallic compound powder was successfully synthesised by mechanical alloying after 20 h in an attritor mill, starting from elemental Ni and Al powders and without subsequent heat treatment. NiAl powder obtained was homogenous and had a nanocrystalline microstructure. It was consolidated by field assisted hot pressing (FAHP), in a novel configuration with a Gleeble 3800 thermomechanical simulator. The powder was also processed by hot isostatic pressing (HIP) in order to compare both methods. The consolidation was successful by both methods obtaining above 98% of NiAl theoretical density (5·86 g cm−3). The results showed that the consolidation process by FAHP technique is effective and uniform throughout the sample as indicated by homogenous hardness values, obtaining microstructure and properties similar to those obtained with HIP technique, with certain advantages over it. The achieved room temperature yield strength of 850 MPa and fracture strain 26–28% corresponds to the bulk values of NiAl intermetallic.
GodinT, HarveyS and StouffsP: ‘Theoretical analysis of environmental and energetic performance of very high temperature turbo-jet engines’, Int. J. Therm. Sci., 1999, 38, 442–451.
2.
BewlayBP, LewandowksiJJ and JacksonMR: ‘Refractory metal-intermetallic in-situ composites for aircraft engines’, JOM, 1997, 44–67.
3.
StoloffNS, LiuCT and DeeviSC: ‘Emerging applications of intermetallics’, Intermetallics, 2000, 8, 1313–1320.
4.
LiuCT and StieglerJO: ‘Ordered intermetallics’, in ‘ASM handbook’, 10th edn, Vol. 2, ‘Properties and selection: nonferrous alloys and special-purpose materials’, 2555–2615; 1992, Materials Park, OH, ASM International.
5.
MiracleDB: ‘The physical and mechanical properties of NiAl’, Acta Metall. Mater., 1993, 41, (3), 649–684.
6.
NoebeRD, BowmanRR and NathalMV: ‘Physical and mechanical properties of the B2 compound NiAl’, Int. Mater. Rev., 1993, 38, (4), 193.
7.
FanQX, JiangSM, WuDL, GongJ and SunC: ‘Preparation and hot corrosion behavior of two Co modified NiAl coatings on a Ni–based superalloy’, Corros. Sci., 2013, 76, 373–381.
8.
HuL, HuW, GottsteinG, BognerS, HolladS and Bührig-PolaczekA: ‘Investigation into microstructure and mechanical properties of NiAl–Mo composites produced by directional solidification’, Mater. Sci. Eng. A, 2012, A539, 211–222.
9.
MilenkovicS, SchneiderA and FrommeyerG: ‘Constitutional and microstructural investigation of the pseudobinary NiAl-W system’, Intermetallics, 2011, 19, 342–349.
10.
BognerS, HuL, HolladS, HuW, GottsteinG and Bührig-PolaczekA: ‘Microstructure of a eutectic NiAl–Mo alloy directionally solidified using an industrial scale and a laboratory scale Bridgman furnace’, Int. J. Mater. Res. (formerly Z. Metallkd.), 2012, 103, 1.
11.
MilenkovicS and CaramR: ‘Microstructure of the microalloyed NiAl–V eutectics’, Mater. Lett., 2002, 55, 126–131.
12.
PalmM, PreuhsJ and SauthoffG: ‘Production-scale of a new intermetallic NiAl–Ta–Cr alloy for high temperature application, Part I’, J. Mater. Process. Technol., 2003, 136, 105–113.
13.
ShengL, WangL, XiT, ZhengY and YeH: ‘Microstructure, precipitates and compressive properties of various holmium doped NiAl/Cr(Mo, Hf) eutectic alloys’, Mater. Des., 2011, 32, 4810–4817.
14.
GuoJT, HuaiKW, GaoQ, RenWL and LiGS: ‘Effects of rare earth elements on the microstructure and mechanical properties of NiAl–based eutectic alloy’, Intermetallics, 2007, 15, 727–733.
15.
SchulsonEM and BarkerDR: ‘A brittle to ductile transition in NiAl of a critical grain size’, Scr. Metall., 1983, 17, 519.
16.
ChoudryMS, EastmanJA, DiMelfiRJ and DollarM: ‘Evidence of room temperature ductility in nanocrystalline NiAl from biaxial disk bend tests’, Scr. Mater., 1997, 37, (6), 843–849.
17.
BohnR, HauboldT, BirrinqerR and GleiterH: ‘Nanocrystalline intermetallic compounds – an approach to ductility?’, Scr. Metall. Mater., 1991, 25, 811–816.
18.
ChoudryMS, DollarM and EastmanJA: ‘Nanocrystalline NiAl–processing, characterization and mechanical properties’, Mater. Sci. Eng. A, 1998, A256, 25–33.
19.
MollJH and McTiernanBJ: ‘Powder metallurgy superalloys’, in‘ASM handbook’, 9th edn, Vol. 7, ‘Powder metal technologies and applications’, 2230–2272; 1998, Materials Park, OH, ASM International.
PabiSK, JordarJ, MannaI and MurtyBS: ‘Nanocrystalline phases in Cu–Ni, Cu–Zn and Ni–Al systems by mechanical alloying’, Nanostruct. Mater., 1997, 9, 149–152.
22.
KubaskiET, CinthoOM, AntoniassiJL, KahnH and CapocchiJDT: ‘Obtaining NiAl intermetallic compound using different milling devices’, Adv. Powder Technol., 2012, 23, 667–672.
23.
LiuE, JiaJ, BaiY, WangW and GaoY: ‘Study on preparation and mechanical property of nanocrystalline NiAl intermetallic’, Mater. Des., 2014, 53, 596–601.
24.
EnayatiMH, KarimzadehF and AnvariSZ: ‘Synthesis of nanocrystalline NiAl by mechanical alloying’, J. Mater. Process. Technol., 2008, 200, 312–315.
25.
XuGH, ZhangKF and HuangZQ: ‘The synthesis and characterization of ultrafine grain NiAl intermetallic’, Adv. Powder Technol., 2012, 23, 366–371.
26.
ZhouLZ, GuoJT and FanGJ: ‘Synthesis of NiAl-TiC nanocomposite by mechanical alloying elemental powders’, Mater. Sci. Eng. A, 1998, A249, 103–108.
27.
MaoSX, McMinnNA and WuNQ: ‘Processing and mechanical behaviour of TiAl/NiAl intermetallic composites produced by cryogenic mechanical alloying’, Mater. Sci. Eng. A, 2003, A363, 275–289.
28.
PalmM, PreuhsJ and SauthoffG: ‘Production-scale of a new intermetallic NiAl–Ta–Cr alloy for high temperature application, Part II’, J. Mater. Process. Technol., 2003, 136, 114–119.
29.
NovakP, SotkaD, MichalcovaA, SerakJ and VojtechD: ‘Production of NiAl–matrix composites by reactive sintering’, Powder Metall., 2011, 54, (3), 308–313.
30.
CammarotaGP and CasagrandeA: ‘Effect of ternary additions of iron on microstructure and microhardness of the intermetallic NiAl in reactive sintering’, J. Alloys Compd, 2004, 381, 208–214.
31.
BourellDL and GrozaJR: ‘Consolidation of ultrafine and nanocrystalline powder’, in‘ASM handbook’, 9th edn, Vol. 7, ‘Powder metal technologies and applications’, 1176–1209; 1998, Materials Park, OH, ASM International.
32.
GrozaJR: ‘Field-activated sintering’, in‘ASM handbook’, 9th edn, Vol. 7, ‘Powder metal technologies and applications’, 1176–1209; 1998, Materials Park, OH, ASM International.
33.
UdhayabanuV, RaviKR and MurtyBS: ‘Development of in situ NiAl–Al2O3 nanocomposite by reactive milling and spark plasma sintering’, J. Alloys Compd, 2011, 509S, S223–S228.
34.
YaoM, ZhangjianZ, JunT and MingL: ‘Fabrication of ultra-fine grain tungsten by combining spark plasma sintering with resistance sintering under ultra high pressure’, Rare Met. Mater. Eng., 2011, 40, (1), 4–8.
35.
OrrùR, LicheriR, LocciAM, CincottiA and CaoG: ‘Consolidation/synthesis of materials by electric current activated/assisted sintering’, Mater. Sci. Eng. R, 2009, R63, 127–287.
36.
Muñoz-MorenoR, SrinivasaraoB, SabirovI, Ruiz-NavasEM and TorralbaJM: ‘Analysis of the temperature effect on the lamellar microstructure transformation of g-TiAl intermetallics processed by field assisted hot pressing’, Proc. Euro PM2012 Cong. Exhibit., Basel, Switzerland, September 2012, Proceeding-Oral.
37.
Muñoz-MorenoR, Ruiz-NavasEM, SrinivasaraoB and TorralbaJM: ‘Microstructural development of PM Ti-45Al-2Nb-2Mn-0·8 vol.%TiB2 processed by field assisted hot pressing’, J. Mat. Sci. Technol., 2014, in press.
38.
CullityBD: ‘Elements of X-ray diffraction’, 363–377; 1956, Reading, MA, Addison-Wesley Publishing Company, Inc.
39.
ZhaoH, QiuF, JinS and JiangQ: ‘High work-hardening effect of the pure NiAl intermetallic compound fabricated by the combustion synthesis and hot pressing technique’, Mater. Lett., 2011, 65, 2604–2606.