Studies are performed to enhance low temperature sintering of Ti–6Al–4V. High energy ball milling is found to be effective in lowering the sintering temperature through the mechanisms of particle size reduction and nanograin formation. The former reduces the diffusion distance for densification, whereas the latter introduces an additional densification mechanism allowing mass transport from the interior of the particle to the neck zone. Together, these two effects can reduce the onset temperature for densification by about 300°C. Spark plasma sintering can further improve low temperature sintering when compared with radiant heat sintering and microwave sintering. The enhanced densification is discussed on the basis of the applied pressure (50 MPa) and the intrinsic joule effect that leads to increase in the local temperature at the contact point between particles.
NiinomiM.:‘Recent metallic materials for biomedical applications’, Metall. Mater. Trans. A, 2002, 33A, 477–486.
2.
NiinomiM.:‘Mechanical biocompatibilities of titanium alloys for biomedical applications’, J. Mech. Behav. Biomed. Mater., 2008, 1, 30–42.
3.
HuX., ShenH., ChengY., XiongX., WangS., FangJ. and WeiS.:‘One-step modification of nano-hydroxyapatite coating on titanium surface by hydrothermal method’, Surf. Coat. Technol., 2010, 205, 2000–2006.
4.
DewidarM. M. and KimJ. K.:‘Properties of solid core and porous surface Ti–6Al–4V implants manufactured by powder metallurgy’, J. Alloys Compd, 2008, 454, 442–446.
5.
WeiM., RuysA. J., SwainM. V., MilthorpeB. K. and SorrellC. C.:‘Hydroxyapatite-coated metals: interfacial reactions during sintering’, J. Mater. Sci.: Mater. Med., 2005, 16, 101–106.
6.
GuoS. B., QuX. H., HeX. B., ZhouT. and DuanB. H.:‘Powder injection molding of Ti–6Al–4V alloy’, J. Mater. Process. Technol., 2006, 173, 310–314.
7.
JoY. J., LeeC. M., JangH. S., LeeN. S., SukJ.-H. and LeeW. H.:‘Mechanical properties of fully porous and porous-surfaced Ti–6Al–4V implants fabricated by electro-discharge-sintering’, J. Mater. Process. Technol., 2007, 194, 121–125.
8.
KimK. T. and YangH. C.:‘Densification behavior of titanium alloy powder during hot pressing’, Mater. Sci. Eng. A, 2001, A313, 46–52.
9.
TasdemirciA., HızalA., AltındisM., HallI. W. and GudenM.:‘The effect of strain rate on the compressive deformation behavior of a sintered Ti6Al4V powder compact’, Mater. Sci. Eng. A, 2008, A474, 335–341.
10.
LeeW. H. and HyunC. Y.:‘Fabrication of fully porous and porous-surfaced Ti–6Al–4V implants by electro-discharge-sintering of spherical Ti–6Al–4V powders in an one-step process’, J. Mater. Process. Technol., 2007, 189, 219–223.
11.
DewidarM. M. and LimJ. K.:‘Properties of solid core and porous surface Ti–6Al–4V implants manufactured by powder metallurgy’, J. Alloys Compd, 2008, 454, 442–446.
12.
NiculaR., LuthenF., StirM., NebeB. and BurkelE.:‘Spark plasma sintering synthesis of porous nanocrystalline titanium alloys for biomedical applications’, Biomol. Eng., 2007, 24, 564–567.
13.
BautistaA., MoralC., BlancoG. and VelascoF.:‘Influence of sintering on the corrosion behavior of a Ti–6Al–4V alloy’, Mater. Corros., 2005, 56, 98–103.
14.
GudenM., CelikT. E., AkarE. and CetinerS.:‘Compression testing of a sintered Ti6Al4V powder compact for biomedical applications’, Mater. Charact., 2005, 54, 399– 408.
15.
KlugH. P. and AlexanderL. E.:‘X-ray diffraction procedures for polycrystalline and amorphous materials’; 1954, London, John Wiley & Sons, Inc.
16.
ShawL., VillegasJ., LuoH. and MiracleD.:‘Thermal stability of nanostructured Al93Fe3Ti2Cr2 alloys prepared via mechanical alloying’, Acta Mater., 2003, 51, 2647–2663.
17.
AikinBJM and CourtneyT. H.:‘The Kinetics of composite particle formation during mechanical alloying’, Metall. Trans. A, 1993, 24A, 647–657.
18.
ZawrahM. and ShawL.:‘Microstructure and hardness of nanostructured Al–Fe–Cr–Ti alloys through mechanical alloying’, Mater. Sci. Eng. A, 2003, A355, 37–49.
19.
ShawL., ZawrahM., VillegasJ., LuoH. and MiracleD.:‘Effects of process control agents on mechanical alloying of nanostructured aluminum alloys’, Metall. Mater. Trans. A, 2003, 34A, 159–170.
20.
FechtH. J., HellsternE., FuZ. and JohnsonW. L.:‘Nanocrystalline metals prepared by high-energy ball milling’, Metall. Trans. A, 1990, 21A, 2333–2337.
21.
BelyakovA., SakaiT., MiuraH. and TsuzakiK.:‘Grain refinement in copper under large strain deformation’, Philos. Mag. A, 2001, 81A, 2629–2643.
22.
KochC. C.:‘The synthesis and structure of nanocrystalline materials produced by mechanical attrition: a review’, Nanostruct. Mater., 1993, 2, 109–129.
23.
SuryanarayanaC.:‘Mechanical alloying and milling’, Prog. Mater. Sci., 2001, 46, 1–184.
24.
UmemotoM., TodakaK. and TsuchiyaK.:‘Formation of nanocrystalline structure in carbon steels by ball drop and particle impact techniques’, Mater. Sci. Eng. A, 2004, A375–A377, 899–904.
25.
HerringC.:‘Effect of change of scale on sintering phenomena’, J. Appl. Phys., 1950, 21, 301–303.
BrooksC. R.:‘Heat treatment, structure and properties of nonferrous alloys’; 1990, Materials, ParkOH, American Society for Metals.
28.
HerzigC., WilgerT., PrzeorskiT., HiskerF. and DivinskiS.:‘Titanium tracer diffusion in grain boundaries of α-Ti, α2-Ti3Al, and γ-TiAl and in α2/γ interphase boundaries’, Intermetallics, 2001, 9, 431–442.
29.
VolanteM., FubiniB., GiamelloE. and BolisV.:‘Reactivity induced by grinding in silicon nitride’, J. Mater. Sci., 1989, 8, 1076–78.
30.
LinI. J. and NadivS.:‘Review of the phase transformation and synthesis of inorganic solids obtained by mechanical treatment (mechanochemical reactions)’, Mater. Sci. Eng., 1979, 39, 193–209.
31.
ButyaginPYu:‘Mechanochemical reactions of solids with gases’, React. Solids, 1986, 1, 345–359.
32.
RenR.-M., YangZ.-G. and ShawL.:‘Synthesis of nanostructured silicon carbide through integrated mechanical and thermal activation process’, J. Am. Ceram. Soc., 2002, 85, 819–827.
33.
ShawL., YangZ.-G. and RenR.-M.:‘Mechanically enhanced reactivity of Si for the formation of Si3N4 composites’, J. Am. Ceram. Soc., 1998, 81, 760–764.
34.
GreshovichC. and RosolowskiJ. H.:‘Sintering of covalent solids’, J. Am. Ceram. Soc., 1976, 59, 336–343.
35.
ComleyP.:‘Multi-rate superplastic forming of fine grain Ti–6Al–4V titanium alloy’, J. Mater. Eng. Perform., 2007, 16, 150–154.
36.
SongX., LiuX. and ZhangJ.:‘Neck formation and self-adjusting mechanism of neck growth of conducting powders in spark plasma sintering’, J. Am. Ceram. Soc., 2006, 89, 494–500.
37.
ChaimR., LevinM., ShlayerA. and EstournèsC.:‘Sintering and densification of nanocrystalline ceramic oxide powders: a review’, Adv. Appl. Ceram., 2008, 27, 159–169.
38.
OrrùR., LicheriR., LocciA. M., CincottiA. and CaoG.:‘Consolidation/synthesis of materials by electric current activated/assisted sintering’, Mater. Sci. Eng. R, 2009, R63, 127–287.
39.
MunirZ. A., QuachD. V. and OhyanagiM.:‘Electric current activation of sintering: a review of the pulsed electric current sintering process’, J. Am. Ceram. Soc., 2011, 94, 1–19.
40.
ErikssonE., ShenZ. and NygrenM.:‘Fast densification and deformation of titanium powder’, Powder Metall., 2005, 48, 231–236.
41.
ZadraM., CasariF., GirardiniL. and MolinariA.:‘Microstructure and mechanical properties of cp-titanium produced by spark plasma sintering’, Powder Metall., 2008, 51, 59–65.
42.
CarrG. L., PerkowitzS. and TannerD. B.:‘Far-infrared properties of inhomogeneous materials’, in ‘Infrared and millimeter waves’, Chap. 6, 184; 1985, Orlando, FL, Academic Press.