Dilatometry experiments have been carried out to investigate the shrinkage kinetics on cold isostatic pressed iron specimens in the 550–730°C temperature range, showing that dimensional contraction is much higher than that predictable on the basis of the shrinkage kinetics models, which neglect the effect of the prior cold compaction. The greater shrinkage is due to an enhanced diffusivity which may be attributed to the large density of structural defects accumulated in the powder particles during compaction (structural activity). A time depending effective lattice diffusion coefficient was determined, with an Arrhenius type dependence on temperature.
CristofoliniI., PillaM., MolinariA., MenapaceC. and LarssonM.:Int. J. Powder. Metall., 2012, 48, (4), 37–43.
4.
MolinariA., MenapaceC., TorresaniE., CristofoliniI. and LarssonM.:Powder Metall., 2013, 56, 189–195.
5.
MenapaceC., LarssonM., TorresaniE., CristofoliniI. and MolinariA.:Proceedings PM2012, 2012 Powder Metallurgy World Congress & Exhibition, Yokohama (Japan) 14–18 October 2012, CD-room, Japan Society of Powder and Powder Metallurgy, ISBN: 978-4-9900214-9-8
6.
GermanR. M.:‘Powder metallurgy of iron and steel’, 148; 1998, New York, John Wiley & Sons.
7.
VermaA., SundararamanM., SinghJ. B. and NalawadeS. A.:Mater. Sci. Technnol., 2010, 21, 1–10.