In this study, the modified preparation method of combining planetary and vibratory ball milling was proposed to prepare Mg based hydrogen storage alloy powders. The comparison of micromorphology and hydrogen storage behaviour between Mg2Ni prepared using the modified and conventional preparation methods were investigated experimentally. The comparison results showed that the combination of first planetary and then vibratory ball milling has more favourable effect on improving both the kinetics and the thermodynamics of ball milled Mg2Ni alloys. The sample synthesised by first planetary milling for 40 h and then vibratory milling for 30 h has faster hydrogen absorption kinetics and lower dehydriding onset temperature than those prepared by the single method of planetary or vibratory milling and hydriding combustion synthesis owing to its popcorn-like microstructure. Moreover, this kind of modified method reduces the reaction enthalpy and activation energy by up to ∼18 and 22% respectively.
ZhuY. F., YangY., WeiL. J., ZhaoZ. L. and LiL. Q.:‘Hydrogen storage properties of Mg–Ni–Fe composites prepared by hydriding combustion synthesis and mechanical milling’, J. Alloys Compd, 2012, 520, 207–212.
2.
SchuthF.:‘Challenges in hydrogen storage’, Eur. Phys. J. Spec. Top., 2009, 176, 155–166.
3.
FelderhoffM., WeidenthalerC., Von HelmoltR. and EberleU.:‘Hydrogen storage: the remaining scientific and technological challenges’, Phys. Chem. Chem. Phys., 2007, 9, 2643–2653.
4.
JainI. P., LalC. and JainA.:‘Hydrogen storage in Mg: a most promising material’, Int. J. Hydrogen Energy, 2010, 35, 5133–5144.
5.
SongM. Y., KwakY. J., LeeS. H. and ParkH. R.:‘Hydriding and dehydriding characteristics of LiBH4 and transition metals-added magnesium hydride’, Mater. Res. Bull., 2013, 48, 2476–2481.
6.
WangY. Q., YangF. S., MengX. Y., GuoQ. F., ZhangZ. X., ParkI. S., KimS. and KimK. J.:‘Simulation study on the reaction process based single stage metal hydride thermal compressor’, Int. J. Hydrogen Energy, 2010, 35, 321–328.
7.
MuthukumarP. and RamanaS. V.:‘Study of heat and mass transfer in MmNi4·6Al0·4 during desorption of hydrogen’, Int. J. Hydrogen Energy, 2010, 35, 10811–10818.
8.
YangF. S., WangG. X., ZhangZ. X. and RudolphV.:‘Investigation on the influences of heat transfer enhancement measures in a thermally driven metal hydride heat pump’, Int. J. Hydrogen Energy, 2010, 35, 9725–9735.
9.
JungS., AhnJ. P., JungH. S. and ParkJ. K.:‘Hydrogenation of Ti–12Mg blending powder during mechanical milling in liquid media containing hydrogen’, Powder Metall., 2006, 49, 57–61.
10.
WuZ., YangF. S., BaoZ. W., NyamsiS. N. and ZhangZ. X.:‘Improvement in hydrogen storage characteristics of Mg-based metal hydrides by doping nonmetals with high electronegativity: a first-principle study’, Comput. Mater. Sci., 2013, 78, 83–90.
11.
YaoX. D., WuC. Z., DuA. J., ZouJ., ZhuZ. H., WangP., ChengH. M., SmithS. and LuG. Q.:‘Metallic and carbon nanotube-catalyzed coupling of hydrogenation in magnesium’, J. Am. Chem. Soc., 2007, 129, 15650–15654.
12.
WuC. Z., YaoX. D. and ZhangH.:‘Hydriding/dehydriding properties of MgH2/5 wt.%Ni coated CNFs composite’, Int. J. Hydrogen Energy, 2012, 35, 247–252.
13.
LiC. Y. V., WangZ. M., LiuS. and ChanS. L. I.:‘Electrochemical characteristics of La–Ni–Al thin films’, J. Alloys Compd, 2008, 456, 407–412.
14.
TeresiakA., UhlemannM., GebertA., ThomasJ., EckertJ. and SchultzL.:‘Formation of nanostructured LaMg2Ni by rapid quenching and intensive milling and its hydrogen reactivity’, J. Alloys Compd, 2009, 481, 144–151.
15.
ChaiY. J., LiuZ. Y., GaoH. N., ZhaoZ. Y., WangN. and HouD. L.:‘Microstructure and hydrogen storage properties of porous Ni@Mg’, Int. J. Hydrogen Energy, 2011, 36, 14484–14487.
16.
HuotJ., RavnsbakD. B., ZhangJ., CuevasF., LatrocheM. and JensenT. R.:‘Mechanochemical synthesis of hydrogen storage materials’, Prog. Mater. Sci., 2013, 58, 30–75.
17.
HakimiM., KameliP., SalamatiH. and MazaheriY.:‘Evolution of microstructural and mechanical properties of nanocrystalline Co2FeAl Heusler alloy prepared by mechanical alloying’, Powder Metall., 2013, 56, 111–116.
18.
PolanskiM., BystrzyckiJ. and PlocinskiT.:‘The effect of milling conditions on microstructure and hydrogen absorption/desorption properties of magnesium hydride (MgH2) without and with Cr2O3 nanoparticles’, Int. J. Hydrogen Energy, 2008, 33, 1859–1867.
19.
HuotJ., LiangG., BoilyS., Van NesteA. and SchulzR.:‘Structural study and hydrogen sorption kinetics of ball-milled magnesium hydride’, J. Alloys Compd, 1999, 293–295, 495–500.
20.
SchimmelH. G., JohnsonM. R., KearleyG. J., Ramirez-CuestaA. J., HuotJ. and MulderF. M.:‘Structural information on ball milled magnesium hydride from vibrational spectroscopy and ab-initio calculations’, J. Alloys Compd, 2005, 393, 1–4.
21.
DoppiuS., SchultzL. and GutfleischO.:‘In situ pressure and temperature monitoring during the conversion of Mg into MgH2 by high-pressure reactive ball milling’, J. Alloys Compd, 2007, 427, 204–208.
22.
SinghA. K., SinghA. K. and SrivastavaO. N.:‘On the synthesis of the Mg2Ni alloy by mechanical alloying’, J. Alloys Compd, 1995, 227, 63–68.
23.
WuZ., CaoX. X. and ZhangZ. X.:‘Identifying the influences of external parameters on the kinetics of Mg2Ni prepared by ball milling’, Proc. 12th China Hydrogen Energy Conf. & 4th Mainland, Taiwan and Hong Kong Symp. on ‘Hydrogen energy’, Wuhan, China, October 2011, China Association for Hydrogen Energy, 172.
24.
CullityB. D. and CohenM. (eds.) ‘The structure of polycrystalline aggregates’, in‘Elements of X-ray diffraction’, Reading, MA, Addison-Wesley, 1st edn, Chap. 9, 1956, 259–296.
25.
VijayR., SundaresanR., MaiyaM. P. and MurthyS. S.:‘Comparative evaluation of Mg–Ni hydrogen absorbing materials prepared by mechanical alloying’, Int. J. Hydrogen Energy, 2005, 30, 501–508.
26.
SpassovT., SolsonaP., SurinachS and BaroM. D.:‘Optimisation of the ball-milling and heat treatment parameters for synthesis of amorphous and nanocrystalline Mg2Ni-based alloys’, J. Alloys Compd, 2003, 349, 242–254.
27.
BobetJ. L., CastroF. J. and ChevalierB.:‘Effects of reactive mechanical milling conditions on the physico-chemical properties of Mg+Cr2O3 mixtures’, J. Alloys Compd, 2004, 376, 205–210.
28.
BarabaszováK. C. and ValáškováM.:‘Characterization of vermiculite particles after different milling techniques’, Powder Technol., 2013, 239, 277–283.
29.
ZaluskaA., ZaluskiL. and Strom-OlsenJ. O.:‘Nanocrystalline magnesium for hydrogen storage’, J. Alloys Compd, 1999, 288, 217–225.
30.
VyasD., JainP., AgarwalG., JainA. and JainI. P.:‘Hydrogen storage properties of Mg2Ni affected by Cr catalyst’, Int. J. Hydrogen Energy, 2012, 37, 16013–16017.
31.
ZhangD. L.:‘Processing of advanced materials using high-energy mechanical milling’, Prog. Mater. Sci., 2004, 49, 537–560.
32.
ChengH. H.:‘Special hydrogen storage materials and the measurement apparatus’, PhD thesis, Institute of Metal Research, Chinese Academic of Sciences, Shenyang, China, 2007, 20–25.
33.
FlanaganT. B. and ClewleyJ. D.:‘Hysteresis in metal hydrides’, J. Less-Common Met., 1982, 83, 127–141.
34.
ReillyJ. J. and WiswallR. H.:‘The reaction of hydrogen with alloys of magnesium and nickel and the formation of Mg2NiH4’, Inorg. Chem., 1968, 7, 2254–2256.
35.
LiQ., LiuJ., LiuY. and ChouK. C.:‘Comparative study on the controlled hydriding combustion synthesis and the microwave synthesis to prepare Mg2Ni from micro-particles’, Int. J. Hydrogen Energy, 2010, 35, 3129–3135.
36.
JacobsM. H. G. and SpencerP. J.:‘Thermodynamic evaluation of the systems Cu–Si, Mg–Ni, Si–Sn and Si–Zn’, J. Chim. Phys., 1993, 90, 167–173.
37.
ZengK. J., KlassenT., OelerichW. and BormannR.:‘Thermodynamic analysis of the hydriding process of Mg–Ni alloys’, J. Alloys Compd, 1999, 283, 213–224.
38.
XieL., LiuY., ZhangX. Z., QuJ. L., WangY. T. and LiX. G.:‘Catalytic effect of Ni nanoparticles on the desorption kinetics of MgH2 nanoparticles’, J. Alloys Compd, 2009, 482, 388–392.
39.
IsmailM., ZhaoY. and DouS. X.:‘An investigation on the hydrogen storage properties and reaction mechanism of the destabilized MgH2–Na3AlH6 (4∶1) system’, Int. J. Hydrogen Energy, 2013, 38, 1478–1483.
FriedlmeierG. and GrollM.:‘Experimental analysis and modeling of the hydriding kinetics of Ni-doped and pure Mg’, J. Alloys Compd, 1997, 253–254, 550–555.
42.
ChungC. A. and LinC. S.:‘Prediction of hydrogen desorption performance of Mg2Ni hydride reactors’, Int. J. Hydrogen Energy, 2009, 34, 9409–9423.
43.
GuzmanD., OrdonezS., FernandezJ. F., SanchezC., SerafiniD., RojasP. A., AguilarC. and TapiaP.:‘Effect of amorphous Mg50Ni50 on hydriding and dehydriding behavior of Mg2Ni alloy’, Mater. Charact., 2011, 62, 442–450.