Aluminium alloy AA 5083 [Al–4·4Mg–0·7Mn–0·15Cr (wt-%)], powder was ball milled in liquid nitrogen via the cryomilling method to obtain a nanocrystalline (NC) structure. Samples of the powder were hot vacuum degassed to remove interstitial contaminants, then consolidated by hot isostatic pressing (HIPing) at six temperatures (from 0·46Tm to 0·89Tm), before being high strain rate forged (HSRF) to produce plate material. The microstructure was analysed at the different processing stages. The compressive properties of the as HIPed material, plus tensile properties of the final product were studied. Despite grain growth during HIPing, an ultrafine grain (UFG) structure was retained in the consolidated material, which consequently had increased strength over conventionally processed AA 5083. As the HIP temperature was increased, the density increased. Strength changes were minimal in compression and tension with varying HIP temperature, once near full density was attained at 275°C (∼0·64TM). Yield strength data indicate negligible variation in the grain size of the materials.
KochC. C.:‘Synthesis of nanostructured materials by mechanical milling: Problems and opportunities’, Nanostruct. Mater., 1997, 9, (1–8), 13–22.
2.
WitkinD. B. and LaverniaE. J.:‘Synthesis and mechanical behavior of nanostructured materials via cryomilling’, Prog. Mater. Sci., 2006, 51, (1), 1–60.
3.
LiE. K. H. and FunkenbuschP. D.:‘Hot isostatic pressing (Hip) of powder mixtures and composites – packing, densification, and microstructural effects’, Metall. Trans. A: Phys. Metall. Mater. Sci., 1993, 24, (6), 1345–1354.
‘ASM handbooks online’, ‘Powder metal technologies and applications’, Vol. 7; 2002, Materials Park, OH, ASM International.
7.
TellkampV. L., MelmedA. and LaverniaE. J.:‘Mechanical behavior and microstructure of a thermally stable bulk nanostructured Al alloy’, Metall. Mater. Trans. A: Phys. Metall. Mater. Sci., 2001, 32, (9), 2335–2343.
8.
WitkinD., LeeZ., RodriguezR., NuttS. and LaverniaE.:‘Al–Mg alloy engineered with bimodal grain size for high strength and increased ductility’, Scr. Mater., 2003, 49, (4), 297–302.
9.
NewberyA.P., AhnB., ToppingT. D., PaoP. S., NuttS. R. and LaverniaE. J.:‘Large UFG Al alloy plates from cryomilling’, J. Mater. Process. Technol., 2008, 203, (1–3), 37–45.
10.
NewberyA. P., AhnB., PaoP., NuttS. R. and LaverniaE. J.:‘A ductile UFG Al alloy via cryomilling and quasi-isostatic forging’, Adv. Mater. Res., 2007, 29–30, 21–29.
11.
TangF., HagiwaraA. and SchoenungJ. A.:‘Microstructure and tensile properties of bulk nanostructured Al-5083/SiCp composites prepared by cryomilling’, Mater. Sci. Eng. A: Struct. Mater. Prop. Microstr. Process., 2005, 407, (1–2), 306–314.
12.
TangF., HagiwaraM. and SchoenungJ. M.:‘Formation of coarse-grained inter-particle regions during hot isostatic pressing of nanocrystalline powder’, Scr. Mater., 2005, 53, (6), 619–624.
13.
VogtR. G., ZhangZ., ToppingT. D., LaverniaE. J. and SchoenungJ. M.:‘Cryomilled aluminum alloy and boron carbide nano-composite plate’, J. Mater. Process. Technol., 2009, 209, (11), 5046–5053.
14.
NewberyA. P., NuttS. R. and LaverniaE. J.:‘Multi-scale Al 5083 for military vehicles with improved performance’, Jom, 2006, 58, (4), 56–61.
15.
ZhangZ. H., HanB. Q., ChungK. H. and LaverniaE. J.:‘Degassing behavior of nanostructured Al and its composites’, Metall. Mater. Trans. A: Phys. Metall. Mater. Sci., 2010, 41, (2), 532–541.
16.
TangF., LiaoC. P., AhnB., NuttS. R. and SchoenungJ. M.:‘Thermal stability in nanostructured Al-5083/SiCp composites fabricated by cryomilling’, Powder Metall., 2007, 50, (4), 307–312.
17.
‘Standard test methods of compression testing of metallic materials at room temperature’, ASTM, Philadelphia, PA, USA, 2000.
‘ASM handbooks online’, ‘Properties and selection: nonferrous alloys and special-purpose materials’, ‘Properties of wrought aluminum and aluminum alloys’, Vol. 2, 2002.
20.
TellkampV. L. and LaverniaE. J.:‘Processing and mechanical properties of nanocrystalline 5083 Al alloy’, Nanostr. Mater., 1999, 12, (1–4), 249–252.
21.
HallE. O.:‘The deformation and ageing of mild steel. 3. discussion of results’, Proc. Phys. Soc. Lond. B, 1951, 64B, (381), 747–753.
22.
PetchN. J.:‘The cleavage strength of polycrystals’, J. Iron Steel Inst., 1953, 174, (1), 25–28.
23.
HosfordW. F.:‘Mechanical behavior of materials’, 188–206; 2005, Cambridge, Cambridge University Press.
24.
MarcA. and MeyersK. K. C.:‘Mechanical behavior of materials’; 1999, Englewood Cliffs, NJ, Prentice-Hall.
25.
HayesR. W., WitkinD., ZhouF. and LaverniaE. J.:‘Deformation and activation volumes of cryomilled ultrafine-grained aluminum’, Acta Mater., 2004, 52, (14), 4259–4271.
26.
ToppingT., AhnB., LiY., NuttS. R. and LaverniaE. J.:‘Influence of process parameters on the mechanical behavior of an ultrafine-grained Al alloy’, Metall. Mater. Trans. A, 2012, 43A, (2), 505–519.
27.
HanB. Q., MohamedF. A. and LaverniaE. J.:‘Tensile behavior of bulk nanostructured and ultrafine grained aluminum alloys’, J. Mater. Sci., 2003, 38, (15), 3319–3324.
28.
LiY., LiuW., OrtalanV., LiW. F. and ZhangZ.:‘HRTEM and EELS study of aluminum nitride in nanostructured Al 5083/B4C processed via cryomilling’, Acta Mater., 2010, 58, (5), 1732–1740.
29.
LiY., ZhaoY. H., OrtalanV., LiuW. and ZhangZ. H.:‘Investigation of aluminum-based nanocomposites with ultra-high strength’, Mater. Sci. Eng. A, 2009, A527, (1–2), 305–316.
30.
LucadamoG., YangN. Y. C., San MarchiC. and LaverniaE. J.:‘Microstructure characterization in cryomilled Al 5083’, Mater. Sci. Eng. A: Struct. Mater. Prop. Microstr. Process., 2006, 430, (1–2), 230–241.
31.
TellkampV. L., DallekS., ChengD. and LaverniaE. J.:‘Grain growth behavior of a nanostructured 5083 Al–Mg alloy’, J. Mater. Res., 2001, 16, (4), 938–944.
32.
KimY. W., GriffithW. M. and FroesF. H.:‘Surface oxides in P/M aluminum-alloys’, J. Met., 1985, 37, (8), 27–33.