Effect of particle size ratio and particle clustering on sintering and stiffness of aluminium matrix composite

Abstract

A metal matrix composite with a matrix composition of Al–3·8Cu–1Mg–0·75Si–0·5Sn was fabricated by sintering a particulate ceramic reinforcement with elemental metal powders. The sintering characteristics were examined as a function of reinforcement volume fraction, particle size and particle size ratio. At high volume fractions of reinforcement, densification ceased completely and the compacts expanded during sintering. Coarse reinforcement particles, not large particle size ratios, maximised the sintering response. Clustering of the ceramic was studied using Dirichelet tessellations of sintered microstructures. While clustering is evident in the sintered microstructures, it does not correlate to sintered density through the particle size ratio because the ceramic particles appear to rearrange in the presence of a large volume of sintering liquid. The effect of particle size is not due to clustering but maybe due to ceramic particle surface area.

Keywords

ALUMINIUM SINTERING COMPOSITES PARTICLE CLUSTERING

Get full access to this article

View all access options for this article.

References

Singh

B. N.

: Powder Metall., 1972, 15, 216–227.

DeJonghe

L. C.

, Rahaman

M. N.

and Hsueh

C. H.

: Acta Metall., 1986, 34, 1467–1471.

Scherer

G. W.

: J. Am. Ceram. Soc., 1987, 70, 719–725.

Bordia

R. K.

and Scherer

G. W.

: Acta Metall., 1988, 36, 2411–2416.

Weiser

M. W.

and DeJonghe

L. C.

: J. Am. Ceram. Soc., 1988, 71, C125—C127.

Sudre

and Lange

F. F.

: J. Am. Ceram. Soc., 1992, 75, 519–524.

Fan

C. L.

and Rahaman

M. N.

: J. Am. Ceram. Soc., 1992, 75, 2056–2065.

Kimura

, Kajiyama

, Yazaki

and Yamaguchi

: J. Mater. Set, 1996, 31, 4149–4157.

Nakada

and Kimura

: J. Am. Ceram. Soc., 1997, 80, 401–406.

10.

Sundaresan

and Aksay

I. A.

: J. Am. Ceram. Soc., 1990, 73, 54–60.

11.

Lange

F. F.

: J. Mater. Res., 1987, 2, 59–65.

12.

Sudre

, Bao

, Fan

, Lange

F. F.

and Evans

A. G.

: J. Am. Ceram. Soc., 1992, 75, 525–531.

13.

Boyd

J. D.

and Lloyd

D. J.

: in ‘Comprehensive composite materials’, (ed. Clyne

T. W.

), 139–149; 2000, Amsterdam, Elsevier.

14.

Slipenyuk

, Kuprin

, Yu. Milman, J. E. Spowart and D. B. Miracle: Mater. Sci. Eng. A, 2004, 381A, 165–170.

15.

Campbell

G. T.

, Raman

and Fields

: Proc. Powder Metallurgy Aluminum and Light Alloys for Automotive Applications Conf., Dearbon, MI, USA, November 1998, MPIF, pp. 35–42.

16.

Weber

M. D.

, Ankem

, Fields

R. J.

, Quinn

G. D.

and Shim

: Proc. Conf. on ‘Powder metallurgy aluminum and light alloys for automotive applications’, Troy, MI, November 2000, MPIF, pp. 59–68.

17.

Prasad

V. V. B.

, Bhat

B. V. R.

, Mahajan

Y. R.

and Ramakrishnan

: Mater. Sci. Eng. A, 2002, 337A, 179–186.

18.

Slipenyuk

, Kuprin

, Milman

, Goncharuk

and Eckert

: Acta Mater., 2006, 54, 157–166.

19.

Bouvard

and Lange

F. F.

: Acta Metall. Mater., 1991, 39, 3083–3090.

20.

Schwarz

and Exner

H. E.

: J. Microsc., 1983, 129, 155–169.

21.

Stearns

L. C.

, Harmer

M. P.

and Chan

H. M.

: J. Am. Ceram. Soc., 1990, 73, 2740–2742.

22.

Stearns

L. C.

, Harmer

M. P.

and Chan

H. M.

: J. Am. Ceram. Soc., 1991, 74, 2175–2179.

23.

Miller

D. N.

: ‘The sintering of reinforced aluminium alloy matrix composites’, PhD thesis, The University of Queensland, Brisbane, Australia, 2004.