The effect of organic modified montmorillonite (OMMT) on the ablative property, fire retardancy, thermal stability and charring capability of the ethylene propylene diene rubber (EPDM) composite was studied. Experimental data show that 33% decrease in the linear ablation rate of EPDM composite was obtained at a loading of 2.5 wt-% OMMT, and the peak heat release rate of EPDM composite in the middle stage of a cone calorimeter (CONE) combustion was also decreased. It is mainly attributed to the formation of char residue during combustion of EPDM composites at high temperature as revealed by scanning electron microscopy and CONE tests. It is worth noting that char formed during the ablation of EPDM composites containing 2.5% OMMT gave better structural stability and thermal stability.
ZhangH. Y.: ‘The properties and application of EPDM’, Explosive & Propellants, 1993, 4, 26–33.
2.
GaoG., ZhangZ., LiX., MengQ., ZhengY. and JinZ.: ‘Study on mechanical and ablative properties of EPDM/OMMT thermal insulating nanocomposites’, J. Nanosci. Nanotechnol., 2010, 10, 7031–7035.
3.
JuniorK. E., ByrdJ. D.Jr, HightowerJ. O., 1986;. US4600732.
4.
DeuriA. S., BhowmickA. K., GhoshR., JohnB., SriramT. and DeS. K.: ‘Thermal and ablative properties of rocket insulator compound based on EPDM’, Polym. Degrad. Stab., 1988, 21, 21–28.
5.
GaoG., ZhangZ., LiX., MengQ. and ZhengY.: ‘An excellent ablative composite based on PBO reinforced EPDM’, Polym. Bull., 2010, 64, 607–622.
6.
JiangY., ZhangX., HeJ., YuL. and YangR.: ‘Effect of polyphenylsilsesquioxane on the ablative and flame-retardation properties of ethylene propylene diene monomer (EPDM) composite’, Polym. Degrad. Stab., 2011, 96, 949–954.
7.
JiaX., LiG., YuY., SuiG., LiuH., LiY., LiP. and YangX.: ‘Ablation and thermal properties of ethylene-propylene-diene elastomer composites reinforced with polysulfonamide short fibers’, J. Appl. Polym. Sci., 2009, 113, 283–289.
8.
LiP., YinL., SongG., SunJ., WangL. and WangL.: ‘High-performance EPDM/organoclay nanocomposites by melt extrusion’, Appl. Clay Sci., 2008, 40, 38–44.
9.
ChangY. W., YangY., RyuS. and NahC.: ‘Preparation and properties of EPDM organomontmorillonite hybrid nanocomposites’, Polym. Int., 2002, 51, 319–324.
10.
AcharyaH., PramanikM, SrivastavaS. K. and BhowmickA. K.: ‘Synthesis and evaluation of high-performance ethylene-propylene-diene terpolymer/organoclay nanoscale composites’, Appl. Polym. Sci., 2004, 93, 2429–2436.
11.
GatosK. G., ThomannR. and Karger-KocsisJ.: ‘Characteristics of ethylene propylene diene monomer rubber/organoclay nanocomposites resulting from different processing conditions and formulations’, Polym. Int., 2004, 53, 1191–1197.
12.
UsukiA., TukigaseA. and KatoM.: ‘Preparation and properties of EPDM-clay hybrids’, Polymer, 2002, 43, 2185–2189.
13.
NahC., RyuH. J., HanS. H., RheeJ. M and LeeM. -H.: ‘Fracture behaviour of acrylonitrile-butadiene rubber/clay nanocomposite’, Polym. Int., 2001, 50, 1265–1268.
14.
GatosK. G., SawanisN. S., ApostolovA. A., ThomannR. and Karger-KocsisJ.: ‘Nanocomposite formation in hydrogenated nitrile rubber (HNBR)/organo-montmorillonite as a function of the intercalant type’, Macromol. Mater. Eng., 2004, 289, 1079–1086.
15.
PramanikM., SrivastavaS. K., SamantarayB. K. and BhowmickA. K.: ‘Rubber-clay nanocomposite by solution blending’, J. Appl. Polym. Sci., 2003, 87, 2216–2220.
16.
WangZ. and PinnavaiaThomas J.: ‘Nanolayer reinforcement of elastomeric polyurethane’, Chem. Mater., 1998, 10, 3769–3771.
17.
ZhangL., WangY., WangY., et al., ‘Morphology and mechanical properties of clay/styrene-butadiene rubber nanocomposites’, J. Appl. Polym. Sci., 2000, 78, 1873—1878.
18.
BalaP., SamantarayB. K., SrivastavaS. K., et a1., ‘Effect of alkylammonium intercalated montmorillonite as filler on natural rubber’, J. Mater. Sci. Lett., 2001, 20, 563–564.
19.
OkadaA., FukumoriK., UsukiA., et al., ‘Molecular-weight and heating rate dependence of the cloud points of polystyrene poly(2-chlorostyrene) blends’, Polym. Preprints, 1991, 32, 540–541.
20.
MousaA. and Karger-KocsisJ.: ‘Rheological and thermodynamical behavior of styrene/butadiene rubber-organoclay nanocomposites’, Macromol. Mater. Eng., 2001, 286, 260–266.
21.
VaiaR. A., PriceG., RuthP. N., NguyenH. T. and LichtenhanJ.: ‘Polymer/layered silicate nanocomposites as high performance ablative materials’, Appl. Clay Sci., 1999, 15, 67–92.
22.
ByrdJ. D., JuniorK. E., 1985;. US4492779.
23.
FrancesA.: EP, 1998, 0272459.
24.
RayS. S. and OkamotoM.: ‘Polymer/layered silicate nanocomposites: a review from preparation to processing’, Prog. Polym. Sci., 2003, 28, 1539–1641.
25.
LeszczynskaA., NjugunaJ. and BanerjeeJ. R.: ‘Polymer/montmorillonite nanocomposites with improved thermal properties. Part I. Factors influencing thermal stability and mechanisms of thermal stability improvement’, Thermochim. Acta, 2007, 453, 75–96.
26.
ZanettiM., KashiwagiT., FalquiL. and CaminoG.: ‘Cone calorimeter combustion and gasification studies of polymer layerd silicate nanocomposites’, Chem. Mater., 2002, 14, 881.
27.
QinH. L., ZhangS. M., ZhaoC. G., HuG. J. and YangM. S.: ‘Flame retardant mechanism of polymer/clay nanocomposites based on polypropylene’, Polymer, 2005, 46, 8386.
28.
JangB. N., CostacheM. and WilkieC. A.: ‘The relationship between thermal degradation behavior of polymer and the fire retardancy of polymer/clay nanocomposites’, Polymer, 2005, 46, 10678.
29.
SongR., WangZ., MengX., ZhangB. and TangT.: ‘Influences of catalysis and dispersion of organically modified montmorillonite on flame retardancy of polypropylene nanocomposites’, J. Appl. Polym. Sci., 2007, 106, 3488–3494.
30.
Lopez CuestaJ. M. and LaoutidF.: ‘Fire retardancy of polymeric materials’, (ed. WilkieC. A. and MorganA. B.., 301–328; 2009, New York, CRC Press Inc.
31.
GilmanJ. W.: ‘Flammability and thermal stability studies of polymer layered-silicate (clay) nanocomposites’, Appl. Clay Sci., 1999, 15, 31–49.
32.
WangZ., DuX., YuH., JiangZ., LiuJ. and TangT.: ‘Mechanism on flame retardancy of polystyrene/clay composites-The effect of surfactants and aggregate state of organoclay’, Polymer, 2009, 50, 5794–5802.