In this work, organoclay reinforced high density polyethylene (HDPE) nanocomposites were prepared at laboratory scale using a batch mixer. Processing conditions, maleic anhydride modified polyethylene (MAPE) type and MAPE/clay weight ratio were optimised. The microstructure of the resultant nanocomposites was analysed by X-ray diffraction and melt rheology tests, and flexural properties and thermal stability were evaluated. Three types of MAPEs with different melt flow indices (MFI) and maleic anhydride contents all improved the interaction between HDPE and clay and promoted clay dispersion. Nanocomposites where the MAPE with MFI most similar to HDPE was used showed the best exfoliation of clay and the strongest HDPE/clay interface. Mechanical properties were slightly improved, while thermal stability was distinctly enhanced in these HDPE nanocomposites compared with neat HDPE and HDPE nanocomposite without MAPE. The prepared HDPE nanocomposites show the potential to improve the thermal stability of wood–plastic composites for structural applications.
LeiY, WuQ, ClemonsCM, YaoF, XuY: ‘Influence of nanoclay on properties of HDPE/wood composite’, J. Appl. Polym. Sci., 2007, 106, 3958–3966.
2.
ZhongY, PolosoT, HetzerM, KeeDD: ‘Enhancement of wood/polyethylene composites via compatibilization and incorporation of organoclay particles’, Polym. Eng. Sci., 2007, 47, 797–803.
3.
HemmasiAH, Khademi-EslamH, TalaiepoorM, KordB: ‘Effect of nanoclay on the mechanical and morphological properties of wood polymer nanocomposite’, J. Reinf. Plast. Compos., 2010, 29, 964–971.
4.
HietalaM, NiinimäkiL, OksmanK: ‘Processing of wood chip-plastic composites: effect on wood particle size, microstructure and mechanical properties’, Plast. Rubber Compos., 2011, 40, 49–56.
5.
GuoG, ParkCB, LeeYH, KimYS, SainM: ‘Flame retarding effects of nanoclay on wood-fiber composites’, Polym. Eng. Sci., 2007, 4, 330–336.
6.
LeeYH, KubokiT, ParkCB, SainM, KontopoulouM: ‘The effect of clay dispersion on the mechanical, physical, and flame-retarding properties of wood fiber/polyethylene/clay nanocomposites’, J. Appl. Polym. Sci., 2010, 118, 452–461.
7.
LiaoB, HuangY, CongG: ‘Influence of modified wood fibers on the mechanical properties of wood fiber-reinforced polyethylene’, J. Appl. Polym. Sci., 1997, 66, 1561–1568.
8.
OksmanK, LindbergH: ‘Influence of thermoplastic elastomers on adhesion in polyethylene–wood flour composites’, J. Appl. Polym. Sci., 1998, 68, 1845–1855.
9.
BalasuriyaPW, YeL, MaiYW, WuJ: ‘Mechanical properties of wood flake-polyethylene composites. II. Interface modification’, J. Appl. Polym. Sci., 2002, 83, 2505–2521.
10.
RaziPS, RamanA: ‘Studies on impact fracture properties of wood–polymer composites’, J. Compos. Mater., 2000, 34, 980–997.
11.
le BrasM, WilkieCA, BourbigotS, DuquesneS, JamaC: ‘Fire retardancy of polymers: new applications of mineral fillers’, Chap. 2; 2005, Cambridge, Royal Society of Chemistry.
12.
GuR, KoktaBV, MichalkovaD, DimzoskiB, FortelnyI, SloufM, KrulisZ: ‘Characteristics of wood–plastic composites reinforced with organo-nanoclays’, J. Reinf. Plast. Compos., 2010, 29, 3566–3586.
13.
FarukO, MatuanaLM: ‘Nanoclay reinforced HDPE as a matrix for wood–plastic composites’, Compos. Sci. Technol., 2008, 68, 2073–2077.
14.
EteläahoP, NevalainenK, SuihkonenR, VuorinenJ, HanhiK, JärveläP: ‘Effects of direct melt compounding and masterbatch dilution on the structure and properties of nanoclay-filled polyolefins’, Polym. Eng. Sci., 2009, 49, 1438–1446.
15.
DurmusA, KasgozA, MacoskoCW: ‘Linear low density polyethylene (LLDPE)/clay nanocomposites. Part I: structural characterization and quantifying clay dispersion by melt rheology’, Polymer, 2007, 48, 4492–4502.
16.
ZhaoC, QinH, GongF, FengM, ZhangS, YangM: ‘Mechanical, thermal and flammability properties of polyethylene/clay nanocomposites’, Polym. Degrad. Stab., 2005, 87, 183–189.
17.
GopakumarTG, LeeJA, KontopoulouM, ParentJS: ‘Influence of clay exfoliation on the physical properties of montmorillonite/polyethylene composites’, Polymer, 2002, 43, 5483–5491.
18.
NaderJ, DagherH, GardnerD, DuguayA, ParentJ, KiziltasA: ‘Effect of compounding method on the thermal, mechanical, and morphological properties of polypropylene–nanoclay nanocomposites’, NSTI-Nanotech., 2010, 1, 91–94.
19.
HottaS, PaulDR: ‘Nanocomposites formed from linear low density polyethylene and organoclays’, Polymer, 2004, 4, 7639–7654.
20.
ChrissopoulouK, AltintziI, AnastasiadisSH, GiannelisEP, PitsikalisM, HadjichristidisN, TheophilouN: ‘Controlling the miscibility of polyethylene/layered silicate nanocomposites by altering the polymer/surface interactions’, Polymer, 2005, 46, 12440–12451.
21.
EteläahoP, NevalainenK, SuihkonenR, VuorinenJ, JärveläP: ‘Effects of two different maleic anhydride-modified adhesion promoters (PP-g-MA) on the structure and mechanical properties of nanofilled polyolefins’, J. Appl. Polym. Sci., 2009, 114, 978–992.
22.
LeeJH, JungD, HongCE, RheeKY, AdvaniSG: ‘Properties of polyethylene-layered silicate nanocomposites prepared by melt intercalation with a PP-g-MA compatibilizer’, Compos. Sci. Technol., 2005, 65, 1996–2002.
23.
OsmanMA, AtallahA: ‘Interparticle and particle-matrix interactions in polyethylene reinforcement and viscoelasticity’, Polymer, 2005, 46, 9476–9488.
24.
WangK, LiangS, DengJ, YangH, ZhangQ, FuQ, DongX, WangD, HanCC: ‘The role of clay network on macromolecular chain mobility and relaxation in isotactic polypropylene/organoclay nanocomposites’, Polymer, 2006, 47, 7131–7144.