Nickel laterite Part 1 – microstructure and phase characterisations during reduction roasting and leaching

Abstract

Detailed microstructure and phase characterisations of processed nickel laterite ore feed, reduced ore and leached ore have been carried out using scanning electron microscope, synchrotron X-ray powder diffraction and electron probe X-ray microanalysis as a part of study aimed to increase Ni recovery from the laterite ores. The majority of the nickel in the ore feed were found to be associated with fine grained goethite (Fe rich matrix of limonite composite) and serpentine particles. These phases were transformed to magnetite and olivine respectively upon reduction roasting. Nanosize metallic particles were also observed on the free surface of limonite composite particles following reduction roasting. Upon leaching, >90% of the nickel in the Fe rich matrix was leached out, while <50% was removed from the olivine and its composites. The characterisation results from this study were used to assist the analysis of thermodynamic and phase changes during reduction roasting and leaching described in Part 2 of the paper.

Keywords

NICKEL LATERITE CARON PROCESS LATERITE REDUCTION LATERITE LEACHING NICKEL PROCESSING

Get full access to this article

View all access options for this article.

References

Bergman

R. A.

: CIM Bull., 2003, 96, 127–138.

Valix

, Tang

J. Y.

and Cheung

W. H.

: Miner. Eng., 2001, 14, 1629–1635.

Pazour

D. A.

: World Min., July 1979, 50-5 4.

Caron

M. H.

: Trans. AIME, 1950, 188, 67–90.

Reid

J. G.

and Fittock

J. E.

: Proc. Int. Symp. on ‘Laterite nickel’, Charlotte, NC, USA, March 2004, TMS, Paper 44, 599–618.

Chen

T. T.

, Dutrizac

J. E.

, Krause

and Osborne

: Proc. Int. Symp. on ‘Laterite nickel’, Charlotte, NC, USA, March 2004, TMS, Paper 8, 79–99.

Gleeson

S. A.

, Herrington

R. J.

, Durango

and Velasquez

C. A.

: Econ. Geol., 2004, 99, 1197–1213.

Sen

, Takahashi

, Fortin

, Spottiswood

D. J.

and Yarar

: Int. J. Min. Proc., 1987, 19, 43–67.

Manceau

and Calas

: Am. Miner., 1985, 70, 549–558.

10.

Manceau

, Calas

and Decarreau

: Clay Miner., 1985, 20, 367–387.

11.

Maquet

, Cervelle

B. D.

and Gouet

: Miner. Deposita, 1981, 16, 357–373.

12.

de Graaf

J. E.

: Hydrometallurgy, 1979, 5, 47–65.

13.

de Graaf

J. E.

: Hydrometallurgy, 1979, 5, 255–271.

14.

Hayashi

: ‘Effect of phase transition on reductive roasting of nickel-bearing serpentine’, MA thesis, University of Utah, Salt Lake City, UT, USA, 1971.

15.

Valix

and Cheung

W. H.

: Miner. Eng., 2002, 15, 523–530.

16.

Valix

and Cheung

W. H.

: Miner. Eng., 2002, 15, 607–612.

17.

Kawahara

, Toguri

J. M.

and Bergman

R. A.

: Metall. Trans. B, 1988, 19B, 181–186.

18.

Mitsutomi

, D. Atmowidjojo and Yusuf: Int. J. Miner. Process., 1987, 19, 297–309.

19.

Mehrotra

S. P.

and Srinivasan

: Trans. Inst. Min. Metall. C, 1994, 103C, 97–104.

20.

Jandova

and Pedlik

: Kovove Mater., 1991, 6, 439–449.

21.

Chandra

, Siemens

R. E.

and Ruud

C. O.

: J. Met., May 1980, 26-3 3.

22.

Antola

, Holappa

and Paschen

: Min. Proc. Extr. Metall. Re v., 1995, 15, 169–179.

23.

Dungan

M. A.

: Am. Miner., 1977, 62, 1018–1029.

24.

Wilson

M. J.

: Clay Miner., 2004, 39, 233–266.