Liquidus relationships of calcium ferrite and ferrous calcium silicate slag in continuous copper converting

Abstract

While calcium ferrite slags have been successfully used in continuous copper converting for the past 30 years, ferrous calcium silicate slag was proposed ∼8 years ago as an additional alternative for copper smelting. Although these slags are normal extensions of each other, their phase relations have not been completely clarified. In this paper, liquidus relations for both slags have been quantified in some regions of common composition. Existing experimental data are reviewed and discussed in relation to the solidification procedure. An original physical model is then used to predict diagrams of the liquidus surface of both slags. It is shown that the ternary liquidus diagrams normally used for FeO_x–SiO₂–CaO system are not suitable for industrial slags. The new model diagrams of Fe/CaO versus SiO₂ and Fe/SiO₂ versus CaO, as well as Fe/CaO versus temperature and Fe/SiO₂ versus temperature are proven much more convenient for ferrite and ferrous calcium silicate slags. Based on these diagrams, the effect of SiO₂ and CaO on the melting temperature is quantified. The effect of Cu₂O is also quantified through the model. Fe/CaO versus Cu₂O and Fe/SiO₂ versus CaO relationships at various copper contents are predicted. The results show good agreement with the experimental data. It is also shown that, in the presence of liquid copper, Cu₂O is dissolved in the slag to an extent depending on the oxidation degree of the system, which may lower the liquidus temperature. Discussions are presented taking into account plant observations, and important conclusions are drawn for copper smelting and converting.

Keywords

CALCIUM FERRITE SLAG FERROUS CALCIUM SILICATE SLAG FEOX CAO SIO2 CU2O COPPER SMELTING COPPER CONVERTING

Get full access to this article

View all access options for this article.

References

Kongoli

: Proc. Yazawa Int. Symp. on ‘Metallurgical and materials processing: principles and technologies’, (ed. Kongoli

), Vol. 1, 199–210; 2003, Warrendale, PA, TMS.

Kongoli

, McBow

and Llubani

: Proc. Conf. Sulfide Smelting 2002, (ed. Stephens

R. L.

and Sohn

H. Y.

), 487–498; 2002, Warrendale, PA, TMS.

Kongoli

and McBow

: Proc. EPD Cong. 2000, (ed. Taylor

), 97–108; 2000, Warrendale, PA, TMS.

Kongoli

, Kozlowski

, Berryman

R. A.

and Stubina

N. M.

: Proc. James M. Toguri Symp. on ‘Fundamentals of metallurgical processing’, (ed. Kaiura

et al), 107–121; 2000, Ottawa, The Canadian Institute of Mining, Metallurgy and Petroleum.

Kongoli

and McBow

: Proc. Int. Conf. Copper ‘99, (ed. Diaz

et al), Vol. VI, 613–625; 1999, Warrendale, PA, TMS.

Kongoli

: Proc. Conf. EPD Cong. 1999, (ed. Mishra

), 945–963; 1999, Warrendale, PA, TMS.

Kongoli

, McBow

and Llubani

: unpublished research; Montreal, Que., FLOGEN Technologies Inc.

Kongoli

, McBow

and Yazawa

: Mater. Trans., 2003, 44, 2136–2140.

Kongoli

, McBow

and Yazawa

: Proc. Yazawa Int. Symp. on ‘Metallurgical and materials processing: principles and technol-ogies’, (ed. Kongoli

et al), Vol. 2, 227–238; 2003, Warrendale, PA, TMS.

10.

Yazawa

, Takeda

and Nakazawa

: Proc. Int. Conf. Copper 99, (ed. Diaz

et al), Vol. VI, 587–599; 1999, Warrendale, PA, TMS.

11.

Kongoli

and Yazawa

: Proc. 6th Int. Conf. on ‘Molten slags, fluxes and salts’, (ed. Seetharaman

and Sichen

), CD-ROM, 016.pdf; 2000, Stockholm, KTH.

12.

Kongoli

, Nakazawa

and Yazawa

: Proc. MMIJ Fall Meeting 2000, (ed. Koike

), Vol. D, 105; 2000, Akita, MMIJ.

13.

Kongoli

, Nakazawa

and Yazawa

: Proc. MMIJ Fall Meeting 2000, (ed. Koike

), Vol. D, 107-108; 2000, Akita, MMIJ.

14.

Kongoli

and Yazawa

: Proc. James M. Toguri Symp. on ‘Fundamentals of metallurgical processing’, (ed. Kaiura

, Pickles

, Utigard

and Vahed

), 365–377; 2000, Ottawa, The Canadian Institute of Mining, Metallurgy and Petroleum.

15.

Kongoli

and Yazawa

: MetalL Mater. Trans. B, 2001, 32B, (4), 583–592.

16.

Yazawa

and Kongoli

: High Temp. Mater. Process., 2001, 20, (3-4), 201–207.

17.

Kongoli

and Yazawa

: Proc. Conf. Sulfide Smelting 2002, (ed. Stephens

R. L.

and Sohn

H. Y.

), 499–509; 2002, Warrendale, PA, TMS.

18.

Kongoli

, McBow

and Yazawa

: Proc. Yazawa Int. Symp. on ‘Metallurgical and materials processing: principles and technol-ogies’, (ed. Kongoli

et al), Vol. 1, 917–925; 2003, Warrendale, PA, TMS.

19.

Kongoli

, McBow

and Yazawa

: Proc. Sohn Int. Symp. on ‘Advanced processing of metals and materials’; 2006, Warrendale, PA, TMS.

20.

Yazawa

and Eguchi

: in ‘Extractive metallurgy of copper’, (ed. Yannopoulos

J. C.

and Agarwel

J. C.

), 3–20; 1976, New York, AIME.

21.

Hino

, Itagaki

and Yazawa

: J. Min. Mater. Process. Inst. Jpn, 1989, 106, 315–320.

22.

Takeda

: Proc. Yazawa Int. Symp., (ed. Kongoli

et al), Vol. 1, 211–225; 2003, Warrendale, PA, TMS.

23.

Tanaka

, Iida

and Takeda

: Proc. Yazawa Int. Symp., (ed. Kongoli

et al), Vol. 2; 2003, Warrendale, PA, TMS.

24.

Schurmann

and Kraume

: Arch. Eisenhutenwes., 1976, 47, (8), 471–476.

25.

Shigaki

, Sawada

, Tsichiya

, Yoshioka

, Takahashi

: Tetsu-to-Hagane, 1984, 70, (16), 2208–2215.

26.

Takeda

, Nakazawa

and Yazawa

: Can. MetalL Q., 1980, 19, 297–305.

27.

Takeda

: in ‘Metallurgical processes for the early twenty-first century’, (ed. Sohn

H. Y.

), 453–466; 1994, Warrendale, PA, TMS.

28.

Tsukihashi

: ‘Advanced approach to intelligent agglomeration’, 135-145; 1999, Tokyo, Iron and Steel Institute of Japan.

29.

Henao

H. M.

, Kongoli

and Itagaki

: Mater. Trans., 2005, 46, (4), 812–819.

30.

Acuna

C. M.

and Yazawa

: JOM, 1997, 49, (10).

31.

Yazawa

: Proc. John Floyd Int. Symp. on ‘Sustainable developments in metals processing’, Melbourne, Vic., Australia, July 2005, CSIRO, 321–329.