Metal droplet losses in slags are an important issue in copper industry. One significant aspect that promotes the entrainment of metal droplets in the slag is their attachment to spinel solids. In the present study, the wetting behaviour of copper alloys on spinel substrates has been investigated in the presence and absence of a slag phase. At first, the attachment was investigated using a synthetic slag containing spinel particles. Microstructural analysis of quenched slag reveals the presence of microdroplets sticking onto a surface of the spinel particles. Second, the metal–spinel interaction was investigated using the sessile drop technique. Wetting angle measurements were performed between Cu–Ag alloys and MgAl2O4 substrates. A non-wetting behaviour between the alloys and substrates was observed. The results suggest that the oxygen partial pressure and the amount of Ag in the alloy both influence the wetting behaviour.
DegelR., OterdoomH., KunzeJ., WarczokA. and RiverosG.: ‘Latest results of the slag cleaning reactor for copper recovery and its potential for the PGM industry’, in ‘Proc. Conf. 3rd Int. Platinum Conf.: ‘Platinum in transformation’, Sun City, South Africa, October 2008’, The Southern African Institue of Mining and Metallurgy, Paper 7197–202.
2.
SuhI.-K., WasedaY. and YazawaA.: ‘Some interesting aspects of non-ferrous metallurgical slags’, High Temp. Mater. Processes, 1988, 8, (1), 65–88. doi: 10.1515/HTMP.1988.8.1.65
3.
LiowJ. L., JuuselaM., GrayN. B. and SutaloI. D.: ‘Entrainment of a two-layer liquid through a taphole’, Metall. Mater. Trans. B, 2003, 34, (6), 821–832. doi: 10.1007/s11663-003-0088-8
4.
CardonaN., HernandezL., AranedaE. and ParraR.: ‘Evaluation of copper losses in the slag cleaning circuits from two Chilean smelters’, in ‘Proc. Conf. Copper 2010, Hamburg, Germany, June 2010’7, 2637–2654, GMDB.
5.
CardonaN., CoursolP., MackeyP. J. and ParraR.: ‘Physical chemistry of copper smelting slags and copper losses at the Paipote smelter. Part 1 – thermodynamic modelling’, Can. Metall. Q., 2011, 50, (4), 318–329. doi: 10.1179/000844311X13112418194761
6.
ImrisI., SanchezM. and AchurraG.: ‘Copper losses to slags obtained from the El Teniente process’, in ‘Proc. 7th Int. Conf. on ‘Molten slags, fluxes and salts’, Johannesburg, South Africa, January 2004’, 177–182; 2004.
7.
SridharR., ToguriJ. and SimeonovS.: ‘Copper losses and thermodynamic considerations in copper smelting’, Metall. Mater. Trans. B, 1997, 28, (2), 191–200. doi: 10.1007/s11663-997-0084-5
8.
MintoR. and DavenportW. G.: ‘Entrapment and flotation of matte in molten slags’, Can. Min. Metall. Bull., 1972, 65, (720), C36–C42.
9.
IpS. W. and ToguriJ. M.: ‘Entrainment behavior of copper and copper matte in copper smelting operations’, Metall. Trans. B, 1992, 23, (3), 303–311. doi: 10.1007/BF02656285
10.
MaruH. C., WasanD. T. and KintnerR. C.: ‘Behavior of a rigid sphere at a liquid-liquid interface’, Chem. Eng. Sci., 1971, 26, (10), 1615–1628. doi: 10.1016/0009-2509(71)86051-7
11.
AndrewsL.: ‘Base metal losses to furnace slag during processing of platinum-bearing concentrates’, PhD thesis; 2008, Pretoria, South Africa, University of Pretoria.
12.
MalflietA., LotfianS., ScheunisL., PetkovV., PandelaersL., JonesP. T. and BlanpainB.: ‘Degradation mechanisms and use of refractory linings in copper production processes: a critical review’, J. Eur. Ceram. Soc., 2014, 34, (3), 849–876. doi: 10.1016/j.jeurceramsoc.2013.10.005
13.
LauC., MukasyanA. S. and VarmaA.: ‘Materials synthesis by reduction-type combustion reactions: influence of gravity’, Proc. Combust. Inst., 2002, 29, 1101–1108. doi: 10.1016/S1540-7489(02)80139-0
14.
KucharskiM. and FimaP.: ‘The surface tension and density of Cu–Pb–Fe alloys’, Arch. Metall. Mater., 2004, 49, (3), 565–573.
15.
LeeJ., TanakaT., AsanoY. and HaraS.: ‘Oxygen adsorption behavior on the surface of liquid Cu–Ag alloys’, Mater. Trans., 2004, 45, (8), 2719–2722. doi: 10.2320/matertrans.45.2719
16.
NexhipC., DavidsonR. and SunS.: ‘Surface tension of Cu–O alloys at 1400 K’, in ‘Proc. 7th Int. Conf. on ‘Molten slags fluxes and slags‘, Johannesburg, South Africa, January 2004’, 271–276.
17.
SiwiecG., OleksiakB., SmalcerzA. and WieczorekJ.: ‘Surface tension of Cu–Ag alloys’, Arch. Metall. Mater., 2013, 58, (1), 193–195.
18.
NovakovicR., RicciE., GiurannoD. and PasseroneA.: ‘Surface and transport properties of Ag–Cu liquid alloys’, Surf. Sci., 2005, 576, (1-3), 175–187. doi: 10.1016/j.susc.2004.12.009
19.
OleksiakB., SiwiecG., BlachaA. and LipartJ.: ‘Influence of iron on the surface tension of copper’, Arch. Mater. Sci. Eng., 2010, 44, (1), 39–42.
20.
EustathopoulosN. and DrevetB.: ‘Determination of the nature of metal–oxide interfacial interactions from sessile drop data’, Mater. Sci. Eng. A, 1998, 249, (1–2), 176–183. doi: 10.1016/S0921-5093(98)00521-8
21.
EustathopoulosN., NicholasM. G. and DrevetB.: ‘Wettability at high temperatures’, in ‘Pergamon materials series’, (ed. CahnR. W.., 420. 1st edn; 1999, Amsterdam, Pergamon.
22.
AbdeyazdanH., DoganN., RhamdhaniM. A., ChapmanM. and MonaghanB.: ‘Dynamic wetting of CaO–Al2O3–SiO2–MgO liquid oxide on MgAl2O4 spinel’, Metall. Mater. Trans. B, 2015, 46, 1–12. doi: 10.1007/s11663-014-0207-8
23.
KozlovaO. B. and SuvorovS. A.: ‘The wetting of refractories of the MgO–Al2O3–ZrO2 system with metal melts’, Refractories, 1976, 17, (11–12), 763–767. doi: 10.1007/BF01319887
24.
WangC. and ZhaoZ.: ‘Transparent MgAl2O4 ceramic produced by spark plasma sintering’, Scr. Mater., 2009, 61, (2), 193–196. doi: 10.1016/j.scriptamat.2009.03.039
25.
FrageN., CohenS., MeirS., KalabukhovS. and DarielM. P.: ‘Spark plasma sintering (SPS) of transparent magnesium-aluminate spinel’, J. Mater. Sci., 2007, 42, (9), 3273–3275. doi: 10.1007/s10853-007-1672-0
26.
MoritaK., KimB. N., HiragaK. and YoshidaH.: ‘Fabrication of transparent MgAl2O4 spinel polycrystal by spark plasma sintering processing’, Scr. Mater., 2008, 58, (12), 1114–1117. doi: 10.1016/j.scriptamat.2008.02.008
27.
BellemansI.: ‘Towards a methodolgy to study the interaction between Cu droplets and spinels’; 2013, Ghent, Ghent University.
28.
StalderA. F., MelchiorT., MullerM., SageD., BluT. and UnserM.: ‘Low-bond axisymmetric drop shape analysis for surface tension and contact angle measurements of sessile drops’, Colloids Surf. A, 2010, 364, (1–3), 72–81. doi: 10.1016/j.colsurfa.2010.04.040
29.
BashforthF. and AdamsJ. C.: ‘An attempt to test the theories of capillary action by comparing the theoretical and measured forms of drops of fluid’; 1883, Cambridge, Cambridge University Press.
30.
RotenbergY., BoruvkaL. and NeumannA. W.: ‘Determination of surface-tension and contact-angle from the shapes of axisymmetric fluid interfaces’, J. Colloid Interface Sci., 1983, 93, (1), 169–183. doi: 10.1016/0021-9797(83)90396-X
31.
SiwiecG., OleksiakB., FolegaP. and MatulaT.: ‘Wettability in the liquid Cu–Ag alloy – fireproof material–gas phase system’, Metalurgija, 2013, 52, (3), 334–336.
32.
FimaP. and SobczakN.: ‘Thermophysical properties of Ag and Ag–Cu liquid alloys at 1098 K to 1573 K’, Int. J. Thermophys., 2010, 31, (6), 1165–1174. doi: 10.1007/s10765-010-0798-5
33.
RicciE., AratoE., PasseroneA. and CostaP.: ‘Oxygen tensioactivity on liquid–metal drops’, Adv. Colloid Interface Sci., 2005, 117, (1–3), 15–32. doi: 10.1016/j.cis.2005.05.007
34.
MoritaZ. and KasamaA.: ‘Effect of a slight amount of dissolved oxygen on the surface-tension of liquid copper’, Trans. Jpn Inst. Met., 1980, 21, (8), 522–530. doi: 10.2320/matertrans1960.21.522
35.
MeierA., BaldwinM. D., ChidambaramP. R. and EdwardsG. R.: ‘The effect of large oxygen additions on the wettabiity and work of adhesion of copper–oxygen alloys on polycrystalline alumina’, Mater. Sci. Eng. A, 1995, 196, (1–2), 111–117. doi: 10.1016/0921-5093(94)09685-6
36.
FimaP. and SobczakN.: ‘Thermophysical properties of Ag and Ag–Cu liquid alloys at 1098 K to 1573 K’, Int. J. Thermophys., 2010, 31, (6), 1165–1174. doi: 10.1007/s10765-010-0798-5