Mechanical properties of a 2024 aluminium alloy laminated structure produced by the ultrasonic consolidation were investigated. In comparison with the monolithic aluminium alloy, the existence of laminated structure gave different fatigue and fracture mechanisms that associated with the layer interfaces. The Al/Al laminated specimens had the lower tensile strength but much higher fracture toughness than the monolithic Al specimens due to the exit of interface delaminations around the crack tip. The fatigue life of the laminated specimens was comparable to that of the monolithic Al specimens, though the initiation and propagation of the crack in the laminated specimens depended strongly on the microstructure of each material. The interface between layers could arrest the fatigue crack and impede the further propagation.
LesuerD. R., SynC. K., SherbyO. D., WadsworthJ., LewandowskiJ. J. and HuntW. H.: ‘Mechanical behaviour of laminated metal composites’, Int. Mater. Rev., 1996, 41, (5), 169–197. doi: 10.1179/imr.1996.41.5.169
2.
WadsworthJ. and LesuerD. R.: ‘Ancient and modern laminated composites—from the Great Pyramid of Gizeh to Y2K’, Mater. Charact., 2000, 45, (4–5), 289–313. doi: 10.1016/S1044-5803(00)00077-2
3.
McLellandA. R. A., AtkinsonH. V. and AndersonP. R. G.: ‘Thixoforming of a novel layered metal matrix composite’, Mater. Sci. Technol., 1999, 15, (8), 939–945. doi: 10.1179/026708399101506616
4.
LiuC. Y., WangQ., JiaY. Z., JingR., ZhangB., MaM. Z. and LiuR. P.: ‘Microstructures and mechanical properties of Mg/Mg and Mg/Al/Mg laminated composites prepared via warm roll bonding’, Mater. Sci. Eng. A, 2012, A556, 1–8.
5.
Cepeda-JimenezC. M., CarrenoF., RuanoO. A., SarkeevaA. A., KruglovA. A. and LutfullinR. Y.: ‘Influence of interfacial defects on the impact toughness of solid state diffusion bonded Ti–6 Al–4 V alloy based multilayer composites’, Mater. Sci. Eng. A, 2013, A563, 28–35. doi: 10.1016/j.msea.2012.11.052
6.
Cepeda-JimenezC. M., Garcia-InfantaaJ. M., PozueoM., RuanoO. A. and CarrenoF.: ‘Impact toughness improvement of high-strength aluminium alloy by intrinsic and extrinsic fracture mechanisms via hot roll bonding’, Scr. Mater., 2009, 61, (4), 407–410. doi: 10.1016/j.scriptamat.2009.04.030
7.
Cepeda-JimenezC. M., PozueloM., Garcia-InfantaJ. M., RuanoO. A. and CarrenoF.: ‘Interface effects on the fracture mechanism of a high-toughness aluminum-composite laminate’, Metall. Mater. Trans. A, 2009, 40A, (1), 69–79. doi: 10.1007/s11661-008-9679-y
8.
WhiteD. R.: ‘Ultrasonic consolidation of aluminum tooling’, Adv. Mater. Process., 2003, 161, (1), 64–65.
9.
YangY., RamG. D. J. and StuckerB. E.: ‘Bond formation and fiber embedment during ultrasonic consolidation’, J. Mater. Process. Technol., 2009, 209, (10), 4915–4924. doi: 10.1016/j.jmatprotec.2009.01.014
10.
YangY., RamG. D. J. and StuckerB. E.: ‘An experimental determination of optimum processing parameters for Al/SiC metal matrix composites made using ultrasonic consolidation’, J. Eng. Mater. Technol., 2007, 129, (4), 538–549. doi: 10.1115/1.2744431
11.
TsujinoJ., UeokaT., KashinoT. and SugaharaF.: ‘Transverse and torsional complex vibration systems for ultrasonic seam welding of metal plates’, Ultrasonics, 2000, 38, (1–8), 67–71. doi: 10.1016/S0041-624X(99)00174-2
12.
RamG. D. J., RobinsonC., YangY. and StuckerB. E.: ‘Use of ultrasonic consolidation for fabrication of multi-material structures’, Rapid Prototype J., 2007, 13, (4), 226–235. doi: 10.1108/13552540710776179
13.
KongC. Y., SoarR. C. and DickensP. M.: ‘Ultrasonic consolidation for embedding SMA fibres within aluminium matrices’, Compos. Struct., 2004, 66, (1–4), 421–427. doi: 10.1016/j.compstruct.2004.04.064
14.
KongC. Y. and SoarR. C.: ‘Fabrication of metal–matrix composites and adaptive composites using ultrasonic consolidation process’, Mater. Sci. Eng. A, 2005, A412, (1–2), 12–18. doi: 10.1016/j.msea.2005.08.041
15.
ChengX., DattaA., ChoiH., ZhangX. and LiX.: ‘Study on embedding and integration of microsensors into metal structures for manufacturing applications’, J. Manuf. Sci. Eng., 2007, 129, (2), 416–424. doi: 10.1115/1.2515456
16.
KongC. Y., SoarR. C. and DickensP. M.: ‘Characterisation of aluminium alloy 6061 for the ultrasonic consolidation process’, Mater. Sci. Eng. A, 2003, A363, (1–2), 99–106. doi: 10.1016/S0921-5093(03)00590-2
17.
KongC. Y., SoarR. C. and DickensP. M.: ‘Optimum process parameters for ultrasonic consolidation of 3003 aluminium’, J. Mater. Process. Technol., 2004, 146, (2), 181–187. doi: 10.1016/j.jmatprotec.2003.10.016
18.
RamG. D. J., YangY. and StuckerB. E.: ‘Effect of process parameters on bond formation during ultrasonic consolidation of aluminum alloy 3003’, J. Manuf. Syst., 2006, 25, (3), 221–238. doi: 10.1016/S0278-6125(07)80011-2
19.
ZhangC., DeceusterA. and LiL.: ‘A method for bond strength evaluation for laminated structures with application to ultrasonic consolidation’, J. Mater. Eng. Perform., 2009, 18, (8), 1124–1132. doi: 10.1007/s11665-008-9342-1
20.
LiD. and SoarR. C.: ‘Characterization of process for embedding SiC fibers in Al 6061 O matrix through ultrasonic consolidation’, J. Eng. Mater. Technol., 2009, 131, (2), 1–6. doi: 10.1115/1.3030946
21.
HopkinsC. D., DapinoM. J. and FernandezS. A.: ‘Statistical characterization of ultrasonic additive manufacturing Ti/Al composites’, J. Eng. Mater. Technol., 2010, 132, (4), 1–9. doi: 10.1115/1.4002073
22.
GonzalezR. and StuckerB.: ‘Experimental determination of optimum parameters for stainless steel 316L annealed ultrasonic consolidation’, Rapid Prototype J., 2012, 18, (2), 172–183. doi: 10.1108/13552541211212159
23.
HopkinsC. D., WolcottP. J., DapinoM. J., TruogA. G., BabuS. S. and FernandezS. A.: ‘Optimizing ultrasonic additive manufactured Al 3003 properties with statistical modeling’, J. Eng. Mater. Technol., 2012, 134, (1) doi: 10.1115/1.4005269
24.
WolcottP. J., HehrA. and DapinoM. J.: ‘Optimized welding parameters for Al 6061 ultrasonic additive manufactured structures’, J. Mater. Res., 2014, 29, (17), 2055–2065. doi: 10.1557/jmr.2014.139
25.
WolcottP. J., HehrA. and DapinoM. J.: ‘Optimal welding parameters for very high power ultrasonic additive manufacturing of smart structures with aluminum 6061 matrix’, Proc. SPIE, 2014, 9059.
26.
LiD. and SoarR.: ‘Influence of sonotrode texture on the performance of an ultrasonic consolidation machine and the interfacial bond strength’, J. Mater. Process. Technol., 2009, 209, (4), 1627–1634. doi: 10.1016/j.jmatprotec.2008.04.018
27.
FrielR. J., JohnsonK. E., DickensP. M. and HarrisR. A.: ‘The effect of interface topography for ultrasonic consolidation of aluminium’, Mater. Sci. Eng. A, 2010, A527, (16–17), 4474–4483. doi: 10.1016/j.msea.2010.03.094
28.
FujiiH. T., SriramanM. R. and BabuS. S.: ‘Quantitative evaluation of bulk and interface microstructures in Al-3003 alloy builds made by very high power ultrasonic additive manufacturing’, Metall. Mater. Trans. A, 2011, 42A, (13), 4045–4055. doi: 10.1007/s11661-011-0805-x
29.
JiH. J., WangJ. Z. and LiM. Y.: ‘Microstructure evolution of 1100 Al alloy multi-foils during ultrasonic additive manufacturing’, 13th International Conference on Electronic Packaging Technology & High Density Packaging (Icept-Hdp 2012), 1586–1589; 2012.
30.
SchickD. E., HahnlenR. M., DehoffR., CollinsP., BabuS. S., DapinoM. J. and LippoldJ. C.: ‘Microstructural characterization of bonding interfaces in aluminum 3003 blocks fabricated by ultrasonic additive manufacturing’, Weld. J., 2010, 89, (5), 105s–115s.
31.
ShimizuS., FujiiH. T., SatoY. S., KokawaH., SriramanM. R. and BabuS. S.: ‘Mechanism of weld formation during very-high-power ultrasonic additive manufacturing of Al alloy 6061’, Acta Mater., 2014, 74, 234–243. doi: 10.1016/j.actamat.2014.04.043
32.
SriramanM. R., BabuS. S. and ShortM.: ‘Bonding characteristics during very high power ultrasonic additive manufacturing of copper’, Scr. Mater., 2010, 62, (8), 560–563. doi: 10.1016/j.scriptamat.2009.12.040
33.
HahnlenR., DapinoM. J., ShortM. and GraffK.: ‘Aluminum–matrix composites with embedded Ni–Ti wires by ultrasonic consolidation’, Proc. SPIE, 2009, 7290, 1–12.
34.
FosterD. R., DapinoM. J. and BabuS. S.: ‘Elastic constants of ultrasonic additive manufactured Al 3003-H18’, Ultrasonics, 2013, 53, (1), 211–218. doi: 10.1016/j.ultras.2012.06.002
35.
KaufmanJ. G.: ‘Fracture toughness of 7075-T6 and -T651 sheet, plate and multilayered adhesive-bonded panels’, J. Basic Eng., 1967, 89, (3), 503–507. doi: 10.1115/1.3609649
36.
HeX.-H., ShiH.-J., ZhangY.-D., FuW.-X., YangZ.-G. and WilkinsonC. E.: ‘In-situ scanning electron microscopy studies of small fatigue crack growth in ultrasonic consolidation bonded aluminum 2024 laminated structure’, Mater. Lett., 2013, 112, (0), 47–50. doi: 10.1016/j.matlet.2013.08.093