This paper is focused on the influence of Ni addition on the microstructure and fracture toughness of structural steels after tempering. Nickel is known to increase the resistance to cleavage fracture of steel and decrease a ductile–brittle transition temperature. The medium carbon, low alloy martensitic steels attain the best combination of properties in low tempered condition, with tempered martensite, retained austenite and transition carbides in the microstructure. In the present research, four model alloys of different Ni contents (from 0·35 to 4·00) were used. All samples were in as quenched and tempered condition. Quenching was performed in oil at room temperature. After quenching, samples were tempered at 200°C for 2 h. An increase in nickel content in the investigated model structural steels causes a decrease in ε carbide volume fraction in their microstructure. Cementite nucleates independently in the boundaries of martensite laths and in the twin boundaries in the areas where the ε carbide has been dissolved. It was stated that stress intensity factor KIc significantly decreases in the case of the presence of dispersive elongated cementite precipitations at the boundaries of the prior austenite grains.
LeeS., KimS., HwangB., LeeB. S. and LeeC. G.: ‘Effect of carbide distribution on the fracture toughness in the transition temperature region of an SA 508 steel’, Acta Mater., 2002, 50, 4755–4762.
2.
TanguyB., BessonJ. and PineauA.: ‘Comment on “Effect of carbide distribution on the fracture toughness in the transition temperature region of an SA 508 steel”’, Scr. Mater., 2003, 49, 191–197.
3.
NorrisS. D. and ParkerJ. D.: ‘The effect of microstructure on fracture mechanisms of 2·25Cr1Mo low alloy steel, part B: the influence of carbides’, Int. J. Pres. Ves. Pip., 1996, 67, 329–337.
4.
CurryD. A. and KnottJ. F.: ‘Effect of microstructure on the cleavage fracture stress in steel’, Met. Sci., 1978, 12, 511–514.
5.
PetchN. J.: ‘The influence of grain boundary carbide and grain size on the cleavage strength and impact transition temperature of steel’, Acta Metall., 1986, 34, 1387–1393.
6.
CasellasD., CaroJ., MolasS., PradoJ. M. and VallsI.: ‘Fracture toughness of carbides in tool steels evaluated by nanoindentation’, Acta Mater., 2007, 55, 4277–4286.
7.
KroonM. and FaleskogJ.: ‘Influence of crack deflection into the carbide/ferrite interface on cleavage fracture initiation in ferritic steels’, Mech. Mater., 2008, 40, 695–707.
8.
KroonM. and FaleskogJ.: ‘Micromechanics of cleavage fracture initiation in ferritic steels by carbide cracking’, J. Mech. Phys. Solids, 2005, 53, 171–196.
9.
HongS., LeeJ., LeeB. J., KimH. S., KimS. K., ChinK. G. and LeeS.: ‘Effects of intergranular carbide precipitation on delayed fracture behavior in three Twinning Induced Plasticity (TWIP) steels’, Mater. Sci. Eng. A, 2013, 587, 85–99.
10.
KrawczykJ., BałaP. and PacynaJ.: ‘The effect of carbide precipitate morphology on fracture toughness in low-tempered steels containing Ni’, J. Microsc.-Oxford, 2010, 237, 411–415.
11.
KrawczykJ., BałaP. and PacynaJ.: ‘TEM studies of tempered structural steel with Ni’, JAMME, 2007, 21, 59–62.
12.
Zaja˛cG. and PacynaJ.: ‘The kinetics of phase transformations during tempering in structural steels with nickel’, J. Mater. Process. Technol., 2005, 162–163, 442–446.
13.
Zaja˛cG. and PacynaJ.: ‘The effect of nickel on mechanical properties of structural steels model alloys’, in ‘Proc. Conf. on ‘Contemporary achievements in mechanics, manufacturing and materials science’, Gliwice–Zakopane, Poland, December 2005’, 1061–1065, International Organising Committee of the Scientific Conferences AMME World Press.
14.
NorströmL. -Å. and VingsboO.: ‘Influence of nickel on toughness and ductile–brittle transition in low-carbon martensite steels’, Met. Sci., 1979, 13, 677–684.
15.
DuX. -D., WangK., WangY. -F., WangR. -J., WangL. and DingH. -F.: ‘Structure and properties of manganese series low carbon high alloyed liner steel’, Mater. Sci. Technol., 2007, 22, 173–176.
16.
KeehanE., KarlssonL. and AndrénH. -O.: ‘Influence of carbon, manganese and nickel on microstructure and properties of strong steel weld metals. Part 1: effect of nickel content’, Sci. Technol. Weld. Join., 2006, 11, 1–8.
17.
LacazeJ., LarrañagaP., AsenjoI., SuarezR. and SertuchaJ.: ‘Influence of 1 wt- addition of Ni on structural and mechanical properties of ferritic ductile irons’, Mater. Sci. Technol., 2012, 28, 603–608.
18.
NamW. -J. and ChoiH. -C.: ‘Effects of silicon, nickel, and vanadium on impact toughness in spring steels’, Mater. Sci. Technol., 1997, 13, 568–574.
19.
GarrisonW. M.: ‘The effect of silicon and nickel additions on the sulfide spacing and fracture toughness of a 0·4 carbon low alloy steel’, Metall. Trans. A, 1986, 17, 669–678.
20.
WuS. J. and CaoL. W.: ‘Effect of intergranular failure on the critical fracture stress and the fracture toughness of degraded reactor pressure vessel steel’, Int. J. Pres. Ves. Pip., 2013, 101, 23–29.
21.
BaronA. A.: ‘The generalized diagram of fracture toughness for pipeline steels’, Int. J. Pres. Ves. Pip., 2012, 98, 26–29.
22.
VeidtM. and SchindlerH. J.: ‘On the effect of notch radius and local friction on the mode I and mode II fracture toughness of a high-strength steel’, Eng. Fract. Mech., 1997, 58, 223–231.
23.
SaidG. and TasgetirenS.: ‘An express technique for the determination of static and dynamic fracture toughness (KIc, KId) of bcc metals and alloys’, Mech. Mater., 2004, 36, 1129–1142.
24.
LeeY. and PrakashV.: ‘Dynamic brittle fracture of high strength structural steels under conditions of plane strain’, Int. J. Solids Struct., 1999, 36, 3293–3337.
25.
KarpJ. and Pofelska-FilipI.: ‘X-ray diffraction (RIAF)’, Metallurgist, 1979, 6, 253–269, (in Polish).
26.
Zaja˛cG. and PacynaJ.: ‘The transformations of undercooled austenite in variable Ni content steels’, Metallurgist, 2004, 7–8, 443–445.
27.
BałaP., PacynaJ. and KrawczykJ.: ‘The microstructure changes in high-speed steels during continuous heating from as-quenched state’, Kovove Mater., 2011, 49, 125–130.
28.
BałaP., KrawczykJ. and HancA.: ‘The mössbauer spectroscopy studies of (to cementite carbides transformation during isothermal heating from as-quenched state of high carbon tool steel’, Acta Phys. Pol. A, 2008, 114, 1641–1650.
29.
KrawczykJ., BałaP. and HancA.: ‘The Mössbauer spectroscopy studies of cementite precipitations during continuous heating from as-quenched state of high carbon Cr–Mn–Mo steel’, Acta Phys. Pol. A, 2008, 114, 1651–1657.
30.
BałaP., PacynaJ. and KrawczykJ.: ‘The influence of the kinetics of phase transformations during tempering on the structure development in a high carbon steel’, Arch. Metall. Mater., 2007, 52, 113–120.