The mechanical behaviour of AZ31 magnesium alloy sheets were evaluated at different directions tilting 0, 45 and 90° to rolling direction. A suitable critical point of pre-stretching has been investigated through the work hardening curve of the magnesium alloy sheets. The microstructure and mechanical properties were examined and compared. The results indicated that the average yield strength of the 0, 45 and 90° pre-hardened 4 specimens followed by annealing decreased 30 MPa and the average uniform elongation increased up to 38 compared with the as received sheet. Pre-hardening process is suggested as a potential technique to improve the ductility and anisotropy of magnesium alloy sheets.
YangQS, JiangB, ZhouGY, HeJJ and PanFS: ‘Enhancing strength and ductility of AZ31 magnesium alloy sheets by the trapezoid extrusion’, Mater. Sci. Technol., 2014, 30, (2), 227–230.
2.
KimN: ‘Magnesium sheet alloys: viable alternatives to steels?’, Mater. Sci. Technol., 2014, to be published.
3.
WangH, WuPD and GharghouriMA: ‘Effects of basal texture on mechanical behaviour of magnesium alloy AZ31B sheet’, Mater. Sci. Eng. A, 2010, A527(15), 3588–3594.
4.
YangQ, JiangB, TianY, LiuW and PanF: ‘A tilted weak texture processed by an asymmetric extrusion for magnesium alloy sheets’, Mater. Lett., 2013, 100, 29–31.
5.
YangQS, JiangB, DaiJH, XiangQ, ZhouGY and PanFS: ‘Microstructure and mechanical behaviour of asymmetric extrued Mg-3Al-1Zn alloy sheets’, Mater. Sci. Technol., 2013, 29, 710–714.
6.
ChinoY, LeeJ.-S, SassaK, KamiyaA and MabuchiM: ‘Press formability of a rolled AZ31 Mg alloy sheet with controlled texture’, Mater. Lett., 2006, 60, (2), 173–176.
7.
GongX, LiH, KangSB, ChoJH and LiS: ‘Microstructure and mechanical properties of twin-roll cast Mg–4·5Al–1·0Zn sheets processed by differential speed rolling’, Mater. Des., 2010, 31, (3), 1581–1587.
8.
WangL, QiaoQ, LiuY and SongX: ‘Formability of AZ31 Mg alloy sheets within medium temperatures’, J. M. Alloys, 2013, 1, (4), 312–317.
9.
ChinoY, KimuraK and MabuchiM: ‘Deformation characteristics at room temperature under biaxial tensile stress in textured AZ31 Mg alloy sheets’, Acta Mater., 2009, 57, (5), 1476–1485.
10.
ZhangH, HuangG, WangL and LiJ: ‘Improved formability of Mg–3Al–1Zn alloy by pre-stretching and annealing’, Scr. Mater., 2012, 67, (5), 495–498.
11.
BallEA and PrangnellPB: ‘Tensile-compressive yield asymmetries in high strength wrought magnesium alloys’, Scr. Metal. Mater., 1994, 31, (2), 111–116.
12.
HeJJ, LiuTM, ChenHB, LuLW and PanFS: ‘Effects of prior compression on ductility and yielding behaviour in extruded magnesium alloy AZ31’, Mater. Sci. Technol., 2014, 30, (12), 1488–1494.
13.
Al-SammanT and GottsteinG: ‘Room temperature formability of a magnesium AZ31 alloy: Examining the role of texture on the deformation mechanisms’, Mater Sci Eng. A, 2008, A488, (1–2), 406–414.
14.
ZhangH, JinW, FanJ, ChengW, Jørgen RovenH, XuB and DongH: ‘Grain refining and improving mechanical properties of a warm rolled AZ31 alloy plate’, Mater. Lett., 2014, 135, 31–34.
15.
ZhangH, LiuY, FanJ, RovenHJ, ChengW, XuB and DongH: ‘Microstructure evolution and mechanical properties of twinned AZ31 alloy plates at lower elevated temperature’, J Alloy Compd, 2014, 615, 687–692.
16.
del ValleJA, CarreñoF and RuanoOA: ‘Influence of texture and grain size on work hardening and ductility in magnesium-based alloys processed by ECAP and rolling’, Acta Mater., 2006, 54, (16), 4247–4259.
17.
MohriT, MabuchiM, SaitoN and NakamuraM: ‘Microstructure and mechanical properties of a Mg-4Y-3RE alloy processed by thermo-mechanical treatment’, Mater. Sci. Eng. A, 1998, A257, (2), 287–294.
18.
ZhangH, HuangG, FanJ, RovenHJ, XuB and DongH: ‘Deep drawability and drawing behaviour of AZ31 alloy sheets with different initial texture’, J Alloy Compd, 2014, 615, 302–310.