Cast Ti46Al8Nb with coarse lamellar microstructures was subject to fatigue crack propagation test at 650°C with R = 0·1. The notch region of each testpiece contains one or one dominant lamellar colony. A strong dependence of fatigue crack propagation threshold on lamellar orientation was found and the lamellar colonies with their interfaces parallel to the stress axis have the highest threshold and those 40–65° off the stress axis have the lowest threshold. It is elucidated that slip or twinning parallel to lamellar interface may interact with cross-lamella slip or twinning to help open up microcracks in front of the main crack.
SoboyejoWO, DeffeyesJE and AswathPB: ‘Investigation of room- and elevated-temperature fatigue crack growth in Ti-48A1’, Mater. Sci. Eng. A, 1991, A138, 95–101.
2.
DavidsonDL and CampbellJB: ‘Fatigue crack growth through the lamellar microstructure of an alloy based on TiAl at 25°C and 800°C’, Metall. Trans. A, 1993, 24A, 1555–1574.
3.
JamesAW and BowenP: ‘Elevated temperature crack growth resistance of TiAl under monotonic and cyclic loading’, Mater. Sci. Eng. A, 1992, A153, 486–492.
4.
BowenP, ChavelRA and JamesAW: ‘Cyclic crack growth in titanium aluminides’, Mater. Sci. Eng. A, 1995, A192/193, 443–456.
5.
HenaffG, BittarB, MabruC, PetitJ and BowenP: ‘Fatigue crack propagation resistance of a Ti-48A1-2Mn-2Nb alloy in the as-cast condition’, Mater. Sci. Eng. A, 1996, A219, 212–220.
6.
TsutsumiM, TakanoS, KitamuraT and OhtaniR: ‘Fatigue crack propagation in a cast TiAl intermetallic compound at high temperature’, Intermetallics, 1996, 4, 577–583.
7.
CampbellJP, Venkateswara RaoKT and RitchieRO: ‘On the role of microstructure in fatigue-crack growth of γ-based titanium aluminides’, Mater. Sci. Eng. A, 1997, A239–A240, 722–728.
8.
KruzicJJ, CampbellJP and RitchieRO: ‘On the fatigue behavior of γ-based titanium aluminides: role of small cracks’, Acta Mater., 1999, 47, (3), 801–816.
9.
PippanR, HagenederP, KnablW, ClemensH, HebesbergerT and TabernigB: ‘Fatigue threshold and crack propagation in γ-TiAl sheets’, Intermetallics, 2001, 9, 89–96.
10.
FilippiniM, BerettaS, PatriarcaL, PasqueroG and SabbadiniS: ‘Defect tolerance of a gamma titanium aluminide alloy’, Procedia Eng., 2011, 10, 3677–3682.
11.
MineY, TakashimaK and BowenP: ‘Effect of lamellar spacing on fatigue crack growth behaviour of a TiAl-based aluminide with lamellar microstructure’, Mater. Sci. Eng. A, 2012, A532, 13–20.
12.
KishidaK, InuiH and YamaguchiM: ‘Deformation of lamellar structure in TiAl-Ti3Al two-phase alloys’, Philos. Mag. A, 1998, 78A, (1), 1–28.
13.
InuiH, OhMH, NakamuraA and YamaguchiM: ‘Room-temperature tensile deformation of polysynthetically twinned (PST) crystals of TiAl’, Acta Metall. Mater., 1992, 40, (11), 3095–3104.
14.
YokoshimaS and YamaguchiM: ‘Fracture behavior and toughness of PST crystals of TiAl’, Acta Mater., 1996, 44, (3), 873–883.
15.
UmakoshiY, YasudaHY and NakanoT: ‘Plastic anisotropy and fracture behavior of cyclically deformed TiAl polysynthetically twinned crystals’, Mater. Sci. Eng. A, 1995, A192/193, 511–517.
16.
YangJ, LiH, HuD and DixonM: ‘Microstructural characterisation of fatigue crack growth fracture surfaces of lamellar Ti45Al2Mn2Nb1B’, Intermetallics, 2014, 45, 89–95.
17.
HuangZW, BowenP and JonesIP: ‘Transmission electron microscopy investigation of fatigue crack tip plastic zones in a polycrystalline γ-TiAl-based alloy’, Philos. Mag., 2001, 81, (9), 2183–2197.
18.
LuYH, ZhangYG, QiaoLJ, WangYB, ChenCQ and ChuWY: ‘In-situ TEM study of fracture mechanisms of polysynthetically twinned (PST) crystals of TiAl alloys’, Mater. Sci. Eng. A, 2000, A289, 91–98.
19.
YaoK, XiaoJ and ZhangJ: ‘In-situ deformation of TiAl PST crystals in TEM’, Intermetallics, 2000, 8, 569–573.
20.
SimkinBA, NgBC, CrimpMA and BielerTR: ‘Crack opening due to deformation twin shear at grain boundaries in near-γ TiAl’, Intermetallics, 2007, 15, 55–60.