Solid state welding was employed to join low intersolubility metal couple Cu–Fe, and the microstructure and mechanical properties of the joints were investigated. The interface was free of defects. Scanning electron microscopy, energy dispersive spectrometry, atomic force microscopy and nanoindentation results revealed that a potential area of pseudo-binary alloy was present at the faying surface, where nanoscale particles were moved to the opposite side by facilitated diffusion. Owing to the mechanism of microcontact and facilitated diffusion, the interfacial strength was improved.
RodriguezJ. A. and GoodmanD. W.:‘The nature of the metal–metal bond in bimetallic surfaces’, Science, 1992, 257, 897–903.
2.
KlagesK., RuettimannC., OlowinskyA. M., FronczekS. and StudtA.:‘Laser beam micro-welding of dissimilar metals’, Proc. 4th Int. Symp. on ‘Laser precision microfabrication’, Munich, Germany, June 2003, SPIE, 303–307.
3.
CalvoF. A., UreñaA., Gomez de SalazarJ. M., MolledaF. and CriadoA. J.:‘Solid-state transformations during diffusion bonding of copper to iron’, J. Mater. Sci., 1988, 23, 1231–1236.
4.
SabetghadamH., HanzakiA. Z. and AraeeA.:‘Diffusion bonding of 410 stainless steel to copper using a nickel interlayer’, Mater. Charact., 2010, 61, 626–634.
5.
GuogeZ., ChandelR. S., SeowH. P. and HoonH. H.:‘Microstructure of the interface of a solid state diffusion bond between Inconel alloy 718 and 17–4 PH stainless steel’, J. Mater. Sci. Lett., 2001, 20, 1937–1940.
6.
JurányiF., SuckJ. B. and JanssenS.:‘Vibrational and magnetic properties of supersaturated Cu100-xFex ’, Appl. Phys. A, 2002, 74A, S972–S974.
7.
KuprinA. P., ChengL., AltounianZ. and RyanD. H.:‘Influence of the interfaces on magnetic properties of Fe/Ag and Fe/Cu multilayers prepared by sputtering’, Hyperfine Interact., 2002, 144–145, 141–149.
8.
ChenS. D., KeF. J., ZhouM. and BaiY. L.:‘Atomistic investigation of the effects of temperature and surface roughness on diffusion bonding between Cu and Al’, Acta Mater., 2007, 55, 3169–3175.
9.
KrekelbergW. P., ShenV. K., ErringtonJ. R. and TruskettT. M.:‘Impact of surface roughness on diffusion of confined fluids’, J. Chem. Phys., 2011, 135, 154502.
10.
MyshkinN. K., PetrokovetsM. I. and KovalevA. V.:‘AFM applications for contact and wear simulation’, Nanosci. Technol., 2006, 299–326.
11.
ZhangR. G. and AcoffV. L.:‘Processing sheet materials by accumulative roll bonding and reaction annealing from Ti/Al/Nb elemental foils’, Mater. Sci. Eng. A, 2007, A463, 67–73.
12.
HebertR. J. and PerepezkoJ. H.:‘Deformation-induced synthesis and structural transformations of metallic multilayers’, Scr. Mater., 2004, 50, 807–812.
13.
WuH. Y., LeeS. and WangJ. Y.:‘Solid state bonding of iron-base alloy, steel-brass and aluminum alloy’, J. Mater. Process. Tech., 1998, 75, 173–179.
14.
ZiegelheimJ., HirakiS. and OhsawH.:‘Diffusion bondability of similar/dissimilar light metal sheets’, J. Mater. Process. Tech., 2007, 186, 87–93.
15.
TolaminejadB. and ArabiH.:‘A study of roll-bonding MS90 alloy to steel utilizing chromized interlayer’, Iran. J. Sci. Technol. B, 2008, 32B, 631–640.
16.
LuC., TieuK. and WexlerD.:‘Significant enhancement of bond strength in the accumulative roll bonding process using nano-sized SiO2 particles’, J. Mater. Process. Tech., 2009, 209, 4830–4834.