In this study, to clarify the behaviour of micro- and macro-creep damage progression for P92 under multiaxial stress field, interrupted creep tests, analysis of multiaxial stress and detailed the cross-sectional observations were conducted on a circular notched round bar specimen which produces the multiaxial stress field due to the plastic constraint. As a result, creep voids were initiated at the early stage and they were formed up to the final fracture. These phenomena were found to be detected using direct current potential drop (DCPD) method. These results concern the development of the measurement of creep crack initiation. The distribution of high void area fraction was in good agreement with that of high hydrostatic stress and high multiaxial stress. This result indicates that multiaxial stress affects the void formation. Furthermore, the micro-creep damage of each interrupted specimen was evaluated by using the electron backscatter diffraction (EBSD) method which can analyse crystallographic misorientation caused by creep strain. The results of EBSD analyses indicated that the value of grain reference orientation deviation (GROD) closely concerns the void initiation.
EnnisP.J., Zielinska-LipiecA., WachterO. and Czyrska-FilemonowiczA.: ‘Microstructural stability and creep rupture strength of the martensitic steel P92 for advanced power plant’, Acta Mater., 1997, 45, 4901–4907.
2.
CerjakH., HoferP. and SchaffernakB.: ‘The influence of microstructural aspects on the service behaviour of advanced power plant steels’, ISIJ Int., 1999, 39, 874–888.
3.
KorcakovaL., HaldJ. and SomersM.A.J.: ‘Quantification of laves phase particle size in 9CrW steel’, Mater. Character., 2001, 47, 111–117.
4.
HattestrandM. and AndrenH.-O: ‘Influence of strain on precipitation reactions during creep of an advanced 9 chromium steel’, Acta Mater., 2001, 49, 2123–2128.
5.
SawadaK., KuboK. and AbeF.: ‘Creep behavior and stability of MX precipitates at high temperature in 9Cr–0·5Mo–1·8W–VNb steel’, Mater. Sci. Eng. A, 2001, 319–321, 784–787.
6.
SawadaK., KuboK. and AbeF.: ‘Contribution of coarsening of MX carbonitrides to creep strength degradation in high chromium ferritic steel’, Mater. Sci. Technol., 2003, 19, 732–738.
7.
AbeF.: ‘Bainitic and martensitic creep-resistant steels’, Curr. Opin. Solid State Mater. Sci., 2004, 8, 305–311.
8.
MasuyamaF.: ‘Creep rupture life and design factors for high-strength ferritic steels’, Int. J. Press. Vessel. Pip., 2007, 84, 53–61.
9.
WilshireB., ScharningP.J. and HurstR.: ‘A new approach to creep data assessment’, Mater. Sci. Eng. A, 2009, 510–511, 3–6.
10.
GirouxP.F., DalleF., SauzayM., MalaplateJ., FournierB. and Gourgues-LorenzonA.F.: ‘Mechanical and microstructural stability of P92 steel under uniaxial tension at high temperature’, Mater. Sci. Eng. A, 2010, 527, 3984–3993.
11.
KimuraK., TabuchiM., TakahashiY., YoshidaK. and YagiK.: ‘Long-term creep strength and strength reduction factor for welded joints of ASME grades 91, 92 and 122 type steels’, Int. J. Microstruct. Mater. Prop., 2011, 6, 72–90.
12.
YokoboriA.T.Jr, SugiuraR., TabuchiM., FujiA., AdachiT. and YokoboriT.: ‘The effect of multi-axial stress component on creep crack growth rate concerning structural brittleness’, Proc. 11th Int. Conf. on ‘Fracture’, 2005, CD-ROM.
13.
SugiuraR., YokoboriA.T.Jr, TabuchiM., FujiiA. and AdachiT.: ‘Characterization of structural embrittlement of creep crack growth for W-added 12Cr ferritic heat-resistant steel related to the multiaxial stress’, J. Eng. Mater. Technol. Trans. ASME, 2009, 131, 011004.
14.
AdachiT., YokoboriA.T.Jr, TabuchiM., FujiA. and YokoboriT.: ‘The proposal of Q* parameter and derivation of the law of creep crack growth life for a round bar specimen with a circular notch for Cr-Mo-V steel’, Mater. High Temp., 2004, 21, 95–100.
15.
JohnsonH.H.: ‘Calibrating the electric potential method for studying slow crack growth’, Mater. Res. Stand., 1965, 5, 442–445.
16.
SchwalbeK.H. and HellmannD.: ‘Application of the electrical potential method to crack length measurements using Johnson's formula’,J. Test. Eval., 1981, 9, 218–221.
17.
HumphreysF.J.: ‘Grain and subgrain characterisation by electron backscatter diffraction’, J. Mater. Sci., 2001, 36, 3833–3854.
18.
WilkinsonA.J. and DingleyD.J.: ‘Quantitative deformation studies using electron back scatter patterns’, Acta Metall. Mater., 1991, 39, 3047–3055.
19.
KamayaM., WilkinsonA.J. and TitchmarshJ.M.: ‘Measurement of plastic strain of polycrystalline material by electron backscatter diffraction’, Nucl. Eng. Des., 2005, 235, 713–725.
20.
BrewerL.N., FieldD.P. and MerrimanC.C.: ‘Mapping and assessing plastic deformation using EBSD’, in ‘Electron backscatter diffraction in materials science’, (ed. SchwartzA. J. .), 2nd edn, 251–262; 2009, New York, Springer.
21.
WrightS.I., NowellM.M. and FieldD.P.: ‘A review of strain analysis using electron backscatter diffraction’, Microsc. Microanal., 2011, 17, 316–329.
22.
MimoK., ImamuraR., KoiwaiH. and FukuokaC.: ‘Residual life prediction of turbine blades of aeroderivative gas turbines’, Adv. Eng. Mater., 2001, 3, 922–924.
23.
FujiyamaK., MoriK., KanekoD., KimachiH., SaitoT., IshiiR. and HinoT.: ‘Creep damage assessment of 10Cr-1Mo-1W-VNbN steel forging through EBSD observation’, Int. J. Press. Vessel. Pip., 2009, 86, 570–577.
24.
KobayashiD., MiyabeM., KagiyaY., NagumoY., SugiuraR., MatsuzakiT. and YokoboriA.T.Jr: ‘Creep damage evaluation of IN738LC based on the EBSD method by using a notched specimen’, Strength Fract. Complex., 2011, 7, 157–167.
25.
YokoboriA.T.Jr, AbeK., TsukidateH., OhmiT., SugiuraR. and IshikawaH.: ‘Micro mechanics based on vacancy diffusion coupled with damage mechanics related to creep deformation and prediction of creep fracture life’, Mater. High Temp., 2011, 28, 126–136.
26.
NemotoT., YokoboriA.T.Jr, MurakawaT. and MiuraH.: ‘Numerical analysis of vacancy transport by residual stress in electromigration on LSI interconnects’, Jpn J. Appl. Phys., 2010, 49, 024301.
27.
ShigeyamaH., NemotoT. and YokoboriA.T.Jr: ‘Prediction of stress induced voiding reliability in Cu damascene interconnect by computer aided vacancy migration analysis’, Jpn J. Appl. Phys., 2011, 50, 05EA05.
28.
YuT. and ShiH.: ‘Effects of grain size distribution on the creep damage evolution of polycrystalline materials’, J. Phys. D: Appl. Phys., 2010, 43, 165401.