Abstract
In this study, the Ti–6Al–4V alloy was diffusion bonded to austenitic stainless steel at temperatures of 820, 885, 930 and 980°C, under a pressure of 5 MPa for 30 min. The effect of temperature on interface formations and microstructure was investigated using a scanning electron microscope (SEM), energy dispersive spectrograph (EDS) microanalyses, X-ray diffraction and shear strength of bonded specimens. The results showed that intermetallic phases and σ-phase formed in the interface region.
Get full access to this article
View all access options for this article.
References
1.
Schwartz
M. M.
and
Paulonis
D. F.
‘Welding handbook’, Vol. 3 , 311-317; 1980, Miami, FL, American welding society.
2.
Cox
M. J.
,
Kim
M. J.
and
Carpenter
R. W.
Metall Mater. Trans. A ., 2002 , 33 , 437 –442 .
3.
Ghosh
M.
,
Bhanumurthy
K.
,
Kale
G. B.
,
Krishnan
J.
and
Chatterjee
S.
J. Nucl. Mater ., 2003 , 322 , 235 –241 .
4.
Kliauga
A. M.
,
Travessa
D.
and
Ferrante
M.
Mater. Charact ., 2001 ,46 ,65 –74 .
5.
Ghosh
M.
and
Chatterjee
S.
Mater. Charact ., 2005 , 54 , 327 –337 .
6.
Ghosh
M.
,
Chatterjee
S.
and
Mishra
B.
Mater. Set Eng. A , 2003 , 363 , 268 –274 .
7.
Orhan
N.
,
Khan
T. I.
and
Eroglu
M.
Scr. Mater ., 2001 , 45 , 441 –446 .
8.
Aleman
B.
,
Gultierrez
I.
and
Urcola
J. J.
Scr. Mater ., 1997 , 36 , 509 –515 .
9.
He
P.
,
Feng
J. C.
,
Zhang
B. G.
and
Qian
Y. Y.
Mater. Charact ., 2002 , 48 , 401 –406 .
10.
Blachowski
A.
,
Cieslak
J.
,
Dubiel
S. M.
and
Zukrowski
J.
J. Alloys Compd , 2000 , 308 , 189 –192 .