Acicular ferrite development has been investigated in autogenous laser welds using cerium sulphide particle dispersed steels. Around 80% acicular ferrite has been obtained in weld metal irrespective of [Al]/[O] ratio. Acicular ferrite is high when combined sulphur and oxygen levels are between 200 and 550 ppm, but is markedly reduced below 200 ppm. Large acicular ferrite variations cannot be explained by changes in particle number density and austenite grain size, but may be attributed to changes in particle type. Phases promoting high acicular ferrite are (Ce,La)2O2S, Ce4O4S3, MnS and TiN, with some Al2O3, CeAlO3 and rare earth sulphides. Reduced acicular ferrite results from an absence of TiN or MnS. It is argued that phases may radically influence acicular ferrite content by altering the thermodynamic driving force for intragranular transformation and varying nucleation and growth kinetics through epitaxial relationships. Where aluminium is the primary deoxidising agent, loss of acicular ferrite at [Al]/[O] ratios greater than unity may potentially be explained by unfavourable Al2O3 clustering and formation of eutectic type II MnS colonies. When cerium is the primary deoxidising and desulphurising agent, this is not observed.
Klaestrup KristensenJ.: Proc. JOM-10, Int. Conf. on ‘Joining of materials’, Helsigor, Denmark, May 2001, JOM Institute,117–129.
2.
KocakM., KimY.-J., CamG., Dos SantosJ., RiekehrS., TotsterF., InstranA., CardinalN., WebsterS. E., Klaestrup KristensenJ. and BorgreenK.: Proc. Eur. Symp. on ‘Assessment of power beam welds’, Geesthacht, Germany, February 1999, GKSS-Forschungszentrum.
3.
KaplanD., HarrisonP. L., FersiniM., MateraS., WeldinghJ. and Klaestrup KristensenJ.: ‘Efficient welding with advanced steels and high power energy beams’, European Commission Report EUR 20507, Office for Official Publications of the European Communities, 2002.
4.
HarrisonP. L., AndrichM., LangenbergP., FersiniM., SorrentinoS., and WegmannH.: ‘Fracture Avoidance in Laser-Welded Thick Structural Steel Plates with Yield Strength Between 235 and 890MPa’, European Commission Report EUR 20951, Office for Official Publications of the European Communities, 2004, ISBN 92-894-7737-7.
5.
Laser Welding in Ship Construction — Classification Society Unified Guidelines for the Approval of CO2-Laser Welding, 1996.
6.
HallB. E. and WallachE. R.: Proc. Int. Conf. on ‘Advances in joining and cutting processes’, Abington, Cambridge, UK, 1989, The Welding Institute, Paper 21.
7.
DennyP. E. and MetzbowerE. A.: Proc. Int. Conf. on ‘Advances in joining and cutting processes’, Abington, Cambridge, UK, 1989, The Welding Institute, Paper 25.
8.
CochraneR. C., SenoglesD. J. and LloydL. J.: ‘Product development for power beam welding’, ECSC Agreement 7210.MC/802 (F5.4/91), Corus Swinden Technology Centre, Rotherham, UK, November 1994.
9.
HarrisonP. L. and WebsterS. E.: Proc. NPC 30, Dusseldorf, Germany, May 2005, CBMM/NPC,61–80.
10.
KosekiT. and ThewlisG.: Mater, Sci. Techol., 2005, 21, (8), 867–879.
11.
AbsonD. J. and PargeterR. J.: Int. Met. Rev., 1986, 31, (4), 141–194.
OharaM. and HommaH.: Proc. Int. Conf. on ‘Applications of electron and laser beam welding’, Hartford, USA, September 1987, AWS,75–85.
14.
OharaM., YuriokaN. and InoueT.: ‘A summary of micro-structures and toughness of electron beam welds in HSLA steels’, July 1992, IIW Document IX-1674-92.
15.
CochraneR. C. and SenoglesD. J.: Proc. Int. Conf. on ‘Titanium technology in microalloyed steels’, Sheffield, UK, December 1994, The Institute of Materials,207–233.
16.
GrongO. and MatlockD. K.: Int. Met. Rev., 1986, 31, 27–48.
CochraneR. C. and KirkwoodP. R.: Proc. Int. Conf. on ‘Trends in steels and consumables for welding’, Abington, Cambridge, UK, 1978, The Welding Institute, Paper no. 35.
25.
ItoY., NakanishiM. and KomizoY.: Met. Const., 1982, 14, (9), 472–478.
26.
HarrisonP. L. and FarrarR. A.: J. Mater. Sci., 1981, 16, (8), 2218–2226.
27.
FleckN. A., GrongO., EdwardsG. R. and MatlockD. K.: Am. Weld J., May 1986, 113s-121s.
28.
LiuS. and OlsenD. L.: Weld. J. Res. Supp., 1986,65, (6), 139s-149s.
29.
BarritteG. S. and EdmondsD. V.: Proc. Int. Conf. on ‘Advances in the physical metallurgy and applications of steel’, Liverpool, UK, September 1981, The Metals Society,126–135.
30.
ThewlisG.: Join. Mater., 1989, 2, (3), 125–129.
31.
HellmanP. and HillertM.: Scand J. Met., 1975, 4, (5), 211.
32.
FullmanR. L.: Trans. AIME, 1953, 197, 447–452.
33.
BhadeshiaH. K. D. H, SvensonL. E. and GretoftB.: J. Mater. Sci., 1986, 21, 3947-3951.
34.
BramfittB. L.: Met. Trans., 1970, 1, 1987–1995.
35.
ThewlisG.: Proc. Int. Conf. on ‘Welding and performance of pippelines’, Abington, Cambridge, UK, 1986, The Welding Institute, Paper no. 9.
36.
MillsA. R., ThewlisG. and WhitemanJ. A.: Mater. Sci Technol., 1987, 3, 1051–1061.
37.
GrongO., KlukenA. O., HylundH. K., DonsA. L. and HjelenJ.: Met. Mat. Trans. A, 1995, 26A, 525–533.
38.
StrangwoodM. and BhadeshiaH. K. D. H.: Proc. Int. Conf. on ‘Advances in welding science and technology’, Gatlinberg, TN, USA, 1986, ASM International,209–213.
39.
YangJ. R. and BhadeshiaH. K. D. H.: Mater. Sci. Technol., 1989, 5, 93–97.
40.
KlukenA. O., GrongO. and HjelenJ.: Met. Trans. A, 1991, 22A, 657–663.
41.
MabuchiH., R. Uemori and M Fujioka: ISIJ Int., 1996, 36, (11), 1406–1412.
42.
TakamuraJ. and MizoguchiS.: Proc. 6th Iron Steel Cong., 591-597; 1990, Tokyo, ISIJ.
43.
ShigesatoG. and SugiyamaM: J. Elect. Microsc., 2002, 51, (6), 359–367.
44.
van der EijkC., LassilaI., GrongO., Svein KlevenO. and HolappaL.: Proc. Int. Conf. on ‘Materials science and technology’, September 2004, New Orleans, LA, USA, AIST/TMS, 199–206.
ZhangZ. and FarrarR. A.: Mater. Sci. Technol., March 1996, 12, 237–260
48.
MabuchiH. and NakaoH.: Trans. Iron Steel Inst. Jpn, 1981, 21, 495–501.
49.
MabuchiH. and NakaoH.: Trans. Iron Steel Inst. Jpn, 1983, 23, 504–512.
50.
EldridgeM. F.: ‘Transformation behaviour of low aluminium ferritic steel’, PhD Thesis, University of Leeds, UK, 2000.
51.
SimsC. E. and DahleF. B.: Trans. Am. Found. Ass., 1938, 46, 65–104.
52.
CraftsW. and HiltyD. C.: AIME Proc. Elec. Furn. Steel Conf., 1953, 11, 121–145.
53.
SimsC. E., SallersH. A. and BoulgerF. W.: Trans. Am. Found. Ass., 1949, 185, 233–247.
54.
DahlW., H. Hengstenberg and C Duren: Stahl und Eisen, 1966, 86, 782–795.
55.
WakohM., SawaiT. and MizoguchiS: ISIJ Int. 1996, No 8, 1014–1021.
56.
GrangeR. A, ShortsleeveF. J., HiltyD. C., BinderW. O., MotockG. T. and OffenhauerC. M.: ‘Boron, calcium, columbium and zirconium in iron and steel’; 1957, New York, Wily and Sons.