The impact of Mg addition to Al7Si alloy is investigated using thermal and image analyses. It is shown that Mg expands α-Al solidification range and eutectic forms over a thermal range. For alloys containing less than 0·6%Mg, differential scanning calorimetry analysis and thermodynamic calculations are incapable of predicting the formation of Mg2Si phase during solidification. Furthermore, Mg addition leads to the formation of greater percentage of α-Al primary phase which is beneficial during semisolid processing of hypoeutectic Al–Si alloys.
NafisiS. and GhomaschiR.: Can. Metall Q., 2005, 44, 289–303.
2.
BackerudL., ChaiG. and TamminenJ.: ‘Solidification character-istics of aluminum alloys’,Vol. 2, ‘Foundry alloys’; 1990, Des Plaines, IL, American Foundry Society Inc.
3.
TuttleB. L.: Modern Cast., 1985, 77, 39–41.
4.
MartinezR. A. and FlemingsM. C.: J. Met. Trans. A, 2005, 36A, 2205.
5.
EmadiD., WhitingL. V., NafisiS. and GhomashchiR.: J. Therm. Anal. Calorim., 2005, 81, 235.
6.
JoenoesA. and GruzleskiJ.: Cast Met., 1991, 4, 62.
7.
HeuslerL. and SchneiderW.: J. Light Met., 2002, 2, 17.
8.
NafisiS. and GhomashchiR.: J. Alloys Compd,2008, (436), 86–90.