Abstract
Plates of 3–5 mm in thickness were extracted from an AZ91D ingot and then butt joints of the plates were produced using tungsten inert gas (TIG) welding method. The TIG arc was also used to deposit welding beads on some of the thin plates. No cracking was found in the butt joints. However, hot cracking was always observed to propagate from the heat affected zone (HAZ) under the welding bead into the weld metal right after a welding bead was deposited on the thin plate. Metallographic and fractographic evidence was obtained to show that the hot cracking is ‘liquation cracking’ in the partially melted HAZ under the high thermal stresses. In the butt joints, the weld metal has the finest grains, highest strength and best ductility, and the HAZ was found to be the ‘weakest link’.