Preparation of semisolid A356 alloy feedstock cast through vertical pipe

Abstract

It is demonstrated that the fine spheroidal and equiaxed non-dendritic microstructures required for semisolid casting can be formed by using a vertical pipe. Various pouring temperatures (615–660°C) and cooling rates of the vertical pipe (no, 200, 400°C preheat) were used to investigate their influence on the semisolid microstructure of an A356 alloy. The results indicate that suitable semisolid billets can be generated at both lower and higher pouring temperatures; thus the vertical pipe technique may be readily exploited in industrial applications. The results also reveal that the microstructure is affected significantly by the cooling effect of the vertical pipe. Furthermore, in the longitudinal section, non-uniform grain sizes were observed, namely the primary α-Al at the bottom of the billet was coarser than that at the top, an effect attributed to the differences of solidification time and cooling rate. The relevant mechanisms are discussed.

Keywords

SEMISOLID VERTICAL PIPE POURING TEMPERATURE MICROSTRUCTURE

Get full access to this article

View all access options for this article.

References

Flemings

M. C.

: Metall Trans. A, 1991, 22A, 957–981.

Xia

and Tausig

: Mater. Sei. Eng. A, 1998, A246, 1–10.

Brusethaug

and Vole

: Proc. 6th Int. Conf. on ‘Processing of semi-solid alloys and composites’, Turin, Italy, September 2000, Polytechnic of Turin,451–456.

Loue

W. R.

and Suery

: Mater. Sei. Eng. A, 1995, A203, 1–13.

Lukasson

, Apelian

and Dasgupta

: AFS Trans., 2002, 110, 271–284.

Kaufmann

, Wabusseg

and Uggowitzer

P. J.

: Aluminum, 2000, 76, 70–79.

Potzinger

, Kaufmann

and Uggowitzer

P. J.

: Proc. 6th Int. Conf. on ‘Processing of semi-solid alloys and composites’, Turin, Italy, September 2000, Polytechnic of Turin,85–90.

Haga

: Proc. 7th Int. Conf. on ‘Processing of semi-solid alloys and composites’, Tsukuba, Japan, September 2002, National Institute of Advanced Industrial Science and Technology,107–112.

Apelian

: Proc. 7th Int. Conf. on ‘Processing of semi-solid alloys and composites’, Tsukuba, Japan, September 2002, National Institute of Advanced Industrial Science and Technology,25–30.

10.

Apelian

, Pan

Q. Y.

and Findon

: Die Cast. Eng., 2004, 1, 22–29.

11.

Forn

and Baile

M. T.

: Proc. 8th Int. Conf. on ‘Processing of semi-solid alloys and composites’, Limassol, Cyprus, September 2004, University of Cyprus, Worcester Polytechnic Institute (USA), Paper16–1.

12.

Wang

, StJohn

D. H.

, Davidson

C. J.

and Ning

: Proc. 8th Int. Conf. on ‘Processing of semi-solid alloys and composites’, Limassol, Cyprus, September 2004, University of Cyprus, Paper14–3.

13.

Cai

W. H.

, Yang

X. J.

, Guo

H. M.

, Wei

R. J.

, Zhang

and Li

H. C.

: J. Nanchang Univ. (Eng. Technol) (China), 2003, 25, (3), 13–17.

14.

Motegi

and Tanabe

: Proc. 8th Int. Conf. on ‘Processing of semi-solid alloys and composites’, Limassol, Cyprus, September 2004, University of Cyprus, Paper16–4.

15.

Pahlevani

, Salarfar

and Nili-Ahmadabadi

: Proc. 8th Int. Conf. on ‘Processing of semi-solid alloys and composites’, Limassol, Cyprus, September 2004, University of Cyprus, Paper11–2.

16.

Mao

W. M.

, Cui

C. L.

, Zhao

A. M.

, Yang

J. L.

and Zhong

X. Y.

: J. Mater. Sci. Technol, 2001, 17, (6), 615–619.

17.

Hutt

J. E. C.

, StJohn

D. H.

, Hogan

and Dahle

A. K.

: Mater. Sci. Technol., 1999, 15, 495–500.

18.

Falak

and Niroumand

: Scr. Mater., 2005, 53, 53–57.

19.

Niroumand

and Xia

: Mater. Sci. Eng. A, 2000, A283, 70–75.

20.

Chalmers

: J. Aust. Inst. Met., 1963, 8, 255–263.

21.

Ohno

: ‘The solidification of metals’; 1976, Tokyo, Chijin Shokan.

22.

Jackson

K. A.

, Hunt

J. D.

, Uhlmann

D. R.

and Seward

T. P.

III: Trans. Metall. Soc. AIME, 1966, 236, 149–158.