A finite element model has been established and used to predict the temperature history of direct laser fabricated (DLFed) Ti–6Al–4V thin wall samples. The effects of laser power and the effect of location within a sample on its temperature history have been modelled and compared with temperatures measured during DLF using thermocouples. The thermal history of the material has been correlated with the observed differences in the microstructures obtained at different locations in a given sample or for a given location in samples obtained at different laser powers.
GriffithM. L., EnszM. T., PuskerJ. D., RobinoC. V., BrooksJ. A., PhiliberJ. A., SmugereskyJ. E. and HofmersterW. H.: in ‘Solid freeform and addititive fabrication 2000’, Mater. Res. Soc. Symp. Proc.Vol. 625, (ed. DanforthS. C. et al.), 9-20; 2000, Warrendale, PA, MRS.
2.
CostaL., RetiT., MeusA. M. and VilarR.: Proc 2002 Int Conf. on ‘Metal powder deposition for rapid manufacturing’, (ed.KeicherD. M. et al.), 172-179; 2002, Princeton, NJ, Metal Powder Industries Federation.
3.
HofmeisterW. H., GriffithM. H., EnsnM. T. and SmugereskyJ. E.: J. Met., 2001, 53, (9), 30–34.
4.
WuX., R Sharman, J. Mei and W. Voice: Mater. Design, 2004, 25, (2), 137–144.
5.
WuX., LiangJ., MeiJ., MitchellC., P. S.Goodwin and W. Voice: Mater. Design, 2004, 25, (2), 103–109.
6.
WuX. and MeiJ.: J. Mater. Process. Technol., 2003, 135, 266–270.
7.
XueL. and IslamM.: Proc 2002 Int Conf. on ‘Metal powder deposition for rapid manufacturing’, (ed.KeicherD. M. et al), 61-69, 2002, Princeton, NJ, Metal Powder Industries Federation.
8.
SearsJ. W.: Proc 2002 Int Conf. on ‘Metal powder deposition for rapid manufacturing’, (ed.KeicherD. M.et al), 77-84; 2002, Princeton, NJ, Metal Powder Industries Federation.
9.
KeicherD. M. and MillerW. D.: Met. Powder Rep., 1998, 53, 26.
10.
LewisG. K. and SchliengerE.: Mater. Design, 2002, 21, 417–423.