Iron ore pellets are a prepared burden material for ironmaking that are commonly sintered in a grate kiln furnace system. Deposited material can adhere in chunks to localised regions of the lining of such furnaces, causing lining depletion. Such deposits consist mainly of iron oxides, but alkali, alkaline earth and other oxides formed from disintegrated pellets and fly ash may also be present. In order to investigate methods of preventing such formations, tests have been performed using several different castables and coatings. Samples of liner castables with and without coatings, installed in an industrial furnace, were collected after 6 and 24 months in production use, and characterised using scanning electron microscopy to identify the materials, characterise morphological changes at the deposit-coating-lining interface, and to determine the active chemical reactions. An Al2O3 based coating applied to one of the fields was found to be in good condition after 6 months in use, but no traces of the coating were observed after 24 months in use. A carbon phosphate based coating was not intact after 6 months in use; it was probably burned-up as a result of the oxidising atmosphere. Hematite grains from the deposit material remained at the original deposit-lining interface, while calcium migrated further into the lining.
Get full access to this article
View all access options for this article.
References
1.
BryersRW: ‘Fireside slagging, fouling, and high-temperature corrosion of heat-transfer surface due to impurities in steam-raising fuels’, Progr. Energy Combust. Sci., 1996, 22, (1), 29–120.
2.
WallT: ‘Mineral matter transformations and ash deposits in pulverised coal combustion’, Sympos. (Int.) Combust., 1992, 24, (1), 1119–1126.
3.
KostakisG: ‘Mineralogical composition of boiler fouling and slagging deposits and their relation to fly ashes: the case of Kardia power plant’, J. Hazard. Mater., 2011, 185, (2–3), 1012–1018.
4.
GomesSFrançoisMAbdelmoulaMRefaitPhPellissierC and EvrardO: ‘Characterization of magnetite in silico-aluminous fly ash by SEM, TEM, XRD, magnetic susceptibility, and Mössbauer spectroscopy’, Cement Concrete Res., 1999, 29, (11), 1705–1711.
5.
LiGLiSDongMYaoQGuoCY and AxelbaumRL: ‘Comparison of particulate formation and ash deposition under oxy-fuel and conventional pulverized coal combustions’, Fuel, 2013, 106, (2), 544–551.
6.
PotgieterJ and WirthW: ‘An investigation into ash-ring formation in a rotary lime kiln’, ZKG Int., 1996, 49, (3), 166–171.
7.
UenakaTIsakoHTokutakeK and AketaK: ‘Coal firing in pelletizing plant developed by Kobe Steel’, Ironmak. Steelmak., 1983, 10, (5), 234–239.
8.
StjernbergJIonJCAnttiM.-LNordinL.-OLindblomB and OdénM: ‘Extended studies of degradation mechanisms in the refractory lining of a rotary kiln for iron ore pellet production’, J. Eur. Ceram. Soc., 2012, 32, (8), 1519–1528.
9.
JonssonCYCStjernbergJWiinikkaHLindblomBBoströmD and ÖhmanM: ‘Deposit formation in a grate–kiln plant for iron-ore pellet production. Part 1: Characterization of process gas particles’, Energy Fuels, 2013, 27, (10), 6159–6170.
10.
BurströmPLundströmSMarjavaaraD and TöyräS: ‘CFD-modelling of selective non-catalytic reduction of NOx in grate–kiln plants’, Progr. Comput. Fluid Dynam., 2010, 10, (5–6), 284–291.
11.
StjernbergJJonssonCYCWiinikkaHLindblomBBoströmD and ÖhmanM: ‘Deposit formation in a grate–kiln plant for iron-ore pellet production. Part 2: Characterization of deposits’, Energy Fuels, 2013, 27, (10), 6171–6184.
12.
KhinaBBVolochkoAT and ZhukovaAA: ‘Obtaining heatproof coatings on fireclay refractories by SHS’, Glass Ceram., 2011, 68, (1–2), 65–68.
13.
BolelliGCannilloVLugliCLusvarghiL and ManfrediniT: ‘Plasma-sprayed graded ceramic coatings on refractory materials for improved chemical resistance’, J. Eur. Ceram. Soc., 2006, 26, (13), 2561–2579.
14.
KulkarniTWangHZBasuSN and SarinVK: ‘Protective Al-rich mullite coatings on Si-based ceramics against hot corrosion at 1200°C’, Surf. Coat. Technol., 2011, 205, (10), 3313–3318.
15.
BasuSNKulkarniTWangHZ and SarinVK: ‘Functionally graded chemical vapor deposited mullite environmental barrier coatings for Si-based ceramics’, J. Eur. Ceram. Soc., 2008, 28, (2), 437–445.
16.
LiuX and ZhangS: ‘Low-temperature preparation of titanium carbide coatings on graphite flakes from molten salts’, J. Am. Ceram. Soc., 2008, 91, (2), 667–670.
17.
Aćimović-PavlovićZAndrićLMiloševićV and MilićevićS: ‘Refractory coating based on cordierite for application in new evaporate pattern casting process’, Ceram. Int., 2011, 37, (1), 99–104.
18.
MukhopadhyaySAbdul AnsarSkPaulDBhowmickG and SenguptaS: ‘Characteristics of refractory castables containing mullite and spinel coated graphites’, Mater. Manuf. Process., 2012, 27, (2), 177–184.
19.
MukhopadhyayS: ‘Nanoscale calcium aluminate coated graphite for improved performance of alumina based monolithic refractory composite’, Mater. Res. Bull., 2013, 48, (7), 2583–2588.
20.
WellsJRileyG and WilliamsonJ: ‘Interactions between coal-ash and burner quarls. Part 2: resistance of different refractory materials to slag attack in a combustion test facility’, Fuel, 2003, 82, (15–17), 1867–1873.
21.
Garbers-CraigAM: ‘How cool are refractory materials?’, J. South. Afr. Inst. Min. Metall., 2006, 108, 1–16.
ZhuBZhuYLiX and ZhaoF: ‘Effect of ceramic bonding phases on the thermo-mechanical properties of Al2O3-C refractories’, Ceram. Int., 2013, 39, (6), 6069–6076.
24.
SchachtC: ‘Refractories handbook’; 2004, New York, Marcel Dekker.
25.
ISO standard, Iron ores – Determination of acid-soluble iron(II) content – Titrimetric method, ISO 9035:1989 (reviewed and confirmed in 2012).
26.
Osborn and MuanA: ‘Phase equilibrium diagrams of oxide systems’, Am. Ceram. Soc. Edward Orton Jr, 1960.
27.
BaspinarM and KaraF: ‘Optimization of the corrosion behavior of mullite refractories against alkali vapour via ZrSiO4 addition to the binder phase’, Ceramics—Silikáty, 2009, 53, (4), 242–249.
28.
RendtorffNGrassoSHuCSuarezGAgliettiE and SakkaY: ‘Zircon–zirconia (ZrSiO4–ZrO2) dense ceramic composites by spark plasma sintering’, J. Eur. Ceram. Soc., 2012, 32, (4), 787–793.
29.
LeeWE and ZhangS: Direct and indirect slag corrosion of oxide and oxide-c refractories, VII International Conference on Molten Slags Fluxes and Salts, The Southern African Institute of Mining and Metallurgy, 2004, 309–320.
30.
DouyA and GervaisM: ‘Crystallization of amorphous precursors in the calcia-alumina system: a differential scanning calorimetry study’, J. Am. Ceram. Soc., 2000, 83, (1), 70–76.
31.
StjernbergJLindblomBWikströmJAnttiM.-L and OdénM: ‘Microstructural characterization of alkali metal mediated high temperature reactions in mullite based refractories’, Ceram. Int., 2010, 36, (2), 733–740.
32.
CnareRF: ‘Coal firing in the grate-kiln system’, Min. Congr. J., 1977, 63, (9), 79–82.
33.
NaritaKOnoyeTSatohYMiyamotoMTaniguchiKKamatani SSSatoT and FukiharaS: ‘Effects of alkalis and zinc on the wear of blast furnace refractories and the tuyere displacement’, ISIJ, 1981, 21, (12), 839–845.
34.
IshiiA and GotoK: ‘Wear of refractories in secondary steelmaking’, Taikabutsu Overseas, 1993, 13, (4), 30–35.
35.
PetkovVJonesPTBoydensEBlanpainB and WollantsP: ‘Chemical corrosion mechanisms of magnesia–chromite and chrome-free refractory bricks by copper metal and anode slag’, J. Eur. Ceram. Soc., 2007, 27, (6), 2433–2444.
36.
Van EndeM.-AGuoMJonesPTBlanpainB and WollantsP: ‘Degradation of MgO-C refractories by MnO-rich stainless steel slags’, Ceram. Int., 2009, 35, (6), 2203–2212.
37.
ChoM.-KVan EndeM.-AEunT.-H and JungI.-H: ‘Investigation of slag-refractory interactions for the Ruhrstahl Heraeus (RH) vacuum degassing process in steelmaking’, J. Eur. Ceram. Soc., 2012, 32, (8), 1503–1517.
38.
GuoMParadaSJonesPTBoydensEDyckJVBlanpainB and WollantsP: ‘Interaction of Al2O3-rich slag with MgO–C refractories during VOD refining—MgO and spinel layer formation at the slag/refractory interface’, J. Eur. Ceram. Soc., 2009, 29, (6), 1053–1060.
39.
KasimagwaIBrabieV and JönssonPG: ‘Slag corrosion of MgO–C refractories during secondary steel refining’, Ironmak. Steelmak., 2014, 41, (2), 121–131.