Investigation of effect of fineness dependent volume of fine aggregate on passive layer formation and corresponding corrosion of steel reinforced concrete using electrochemical approach

Abstract

This paper aims to determine the effect of the fineness modulus of fine aggregate on the quality and development of passive film and its subsequent effect on the corrosion of reinforced concrete structures. The study uses both electrochemical laboratory controlled experimentation and finite element modelling approach. Corrosion is an electrochemical process that requires an electrolyte for the occurrence of a corrosion reaction. Therefore, it is necessary to calculate the effective corrosion rate with reference to the saturated area of the concrete only when there is corrosion of reinforced concrete structures. Theoretically and numerically, the saturated area depends on the capillary zone porosity, gel zone porosity and degree of saturation in the aggregate free volume of concrete, which is a heterogeneous material. It is thus important to understand the effect of aggregate fineness on the corrosion of steel rebars. Therefore, detailed investigations were conducted using a variety of fine aggregates and combinations thereof. The initiative for this research came from the observation that the interfacial transition zone (ITZ) around the steel bar in concrete does not contain coarse aggregate, but could be surrounded by mortar and not only paste. Hence, the fine aggregate volume may also influence the corrosion rate. Some fine aggregate, which is finer than coarse aggregate, could be present in the vicinity of the steel bar surface, depending on the fineness modulus, which may affect both the development of the passive layer and the corrosion rate. The previous research data in this area were found to be limited. Hence, these factors have been investigated in the present study. Both mortar and concrete prismatic specimens were cast, and the quality of passive layer development and the corrosion severity were compared between specimens to determine the effect of fine aggregate volume with respect to the respective fineness modulus values. The corrosion potential, current and rate values obtained through experimentation showed significant differences in their magnitudes with respect to the variation in the fineness modulus. A directly proportional relation was observed between the fineness modulus of fine aggregate and the corrosion of rebars. Therefore, in the light of the experimental results obtained in this study, a finite element based numerical model incorporating the effect of the fineness modulus of fine aggregate on corrosion of steel rebars in concrete has been developed and successfully verified in this study.

Keywords

Fine aggregate Fineness modulus Passive layer Corrosion Steel rebar Mortar Concrete Experimentation FEM

Get full access to this article

View all access options for this article.

References

Rizwan

and Ishida

: ‘Investigation of volumetric effect of coarse aggregate on corroding steel reinforcement at the interfacial transition zone of concrete’ KSCE J. Civil Eng. 2011 15 (1) 153–160.

Maslehuddin

Al-Mehthel

Alidi

Shameem

and Ibrahim

: ‘Effect of dust in coarse aggregates on reinforcement corrosion in concrete’ Constr. Build. Mater. 2010 24 326–331.

Subramaniam

and Bi

: ‘Investigation of the local response of the steel–concrete interface for corrosion measurement’ Corros. Sci. 2009 51 (9) 1976–1984.

Yuan

and Ji

: ‘Modeling corroded section configuration of steel bar in concrete structure’ Constr. Build. Mater. 2009 23 (6) 2461–2466.

Chen

: ‘Computational framework model for durability assessment of reinforced concrete and mortars under corrosion deterioration processes’ PhD thesis, Vanderbilt University, Nashville, TN, USA 2006.

Bertolini

Elsener

Pedeferri

and Polder

: ‘Corrosion of steel in concrete’; 2000

Weinheim

Wiley-VCH Verlag GmbH and Co. KGaA.

Broomfield

: ‘Corrosion in steel reinforced concrete’; 1997

London

E & FN SPON.

Jones

: ‘Principles and prevention of corrosion’ 2nd edn; 1996

Englewood Cliffs, NJ

Prentice Hall.

Glass

Page

and Short

: ‘Factors affecting the corrosion rate models of steel in concrete mortars’ Corros. Sci. 1991 32 (12) 1283–1294.

10.

Piron

: ‘Electrochemistry of corrosion’; 1991

Houston, TX

NACE International.

11.

Tuutti

: ‘Corrosion of steel in concrete and mortars’ No. FO 4/82, Swedish Cement and Concrete Research Institute, Stockholm, Sweden 1982.

12.

Maekawa

Ishida

and Kishi

: ‘Multiscale modeling of concrete performance’ J. Adv. Concr. Technol. 2003 1 (2) 91–126.

13.

Ishida

and Maekawa

: ‘An integrated computational system for mass/energy generation, transport, and mechanics of materials and structures’ J. JSCE, Aug. 2000, No. 627/V-44.

14.

Ishida

: ‘An integrated computational system of mass/energy generation, transport and mechanics of materials and structures’ PhD thesis, University of Tokyo, Tokyo, Japan 1999.

15.

Uomoto

: ‘Non-destructive testing in civil engineering’671–678; 2000

New York

Elsevier.

16.

‘Standard test method for half-cell potentials of uncoated reinforcing steel in concrete’

ASTM C 876-09, ASTM, West Conshohocken, PA, USA 2009.

17.

‘Standard test practice for preparing, cleaning and evaluating corrosion test specimens’

ASTM G1-03, ASTM, West Conshohocken, PA, USA 2002.