In this paper, the influence of the tin content on the corrosion behaviour of copper alloys was investigated. Three different bicomponent bronze alloys were exposed to a natural urban environment. The kinetic corrosion processes and the patina properties were monitored using the open circuit potential, electrochemical impedance spectroscopy and spectrocolorimetry. Results show that the bronze corrosion behaviour improves upon increasing the tin content. In addition, the mechanism of the patina formation is different for the three alloys.
ChiavariCColledanAFrignaniABrunoroG: ‘Corrosion evaluation of traditional and new bronzes for artistic casting’Mater. Chem. Phys.200695252–259.
2.
ReidMPunchJGarfias-MesiasLFShannonKBelochapkineSTannerDA: ‘Study of mixed flowing gas exposure of copper’J. Electrochem. Soc.2008155(4)c147–c153.
3.
XuNZhaoLDingCZhangCLiRZhongQ: ‘Laboratory observation of dew formation at an early stage of atmospheric corrosion of metals’Corros. Sci.200244163–170.
4.
BartuliCCignaRColomboB: ‘Valutazione dei fenomeni corrosive in corso sulla superficie della statua equestre dell'Imperatre Marco Aurelio’, Mater. Strut.1996AnnoVI(3)127–136.
5.
ChiavariCRahmouniKTakenoutiHJoiretSVermautaPRobbiolaL: ‘Composition and electrochemical properties of natural patinas of outdoor bronze monument’Electrochim. Acta200752, 7760-7769.
6.
AngeliniEGrassiniSCorbelliSIngoGMde CaroTPlesciaPRicucciCBiancoAAgostiniS: ‘Potentialities of XRF and EIS portable instrument for the characterization of ancient artefacts’Appl. Phys. A200683A643–649.
7.
CicileoGPCrespoMARosalesBM: ‘Comparative study of patinas formed on statuary alloy by means of electrochemical and surface analysis techniques’Corros. Sci.200446929–953.
8.
WallinderIOBertlingSZhangXLeygrafC: ‘Predictive models of copper runoff from external structures’J. Environ. Monit.20046(8)704–712.
9.
SandbergJWallinderIOLeygrafCle BozecN: ‘Corrosion-induced copper runoff from naturally and pre-patinated copper in a marine environment’Corros. Sci.200648, 4316-4338.
10.
RobbiolaLPortierR: ‘A global approach to the authentication of ancient bronzes based on the characterization of the alloy–patina–environment system’J. Cult. Heritage200671–12.
11.
GalleseFLaguzziGLuvidiLFerrariVTakacsSVenturi Pagani CesaG: ‘Comparative investigation into the corrosion of different bronze alloys suitable for outdoor sculptures’Corros. Sci.200850954–961.
12.
ScottDAPodanyJConsidineBB (eds.): ‘Ancient and historical metals: conservation and scientific research’; 1994Los Angeles, CAGetty Institute Publication.
13.
ScottDADoddLS: ‘Examination, conservation and analysis of gilded Egyptian bronze Osiris’J. Cult. Heritage20023333–345.
14.
D'ErcoliGGuidaGMarabelliMSantinV: ‘Non-distructive testing by the Rp method of bronze monuments: three case studies’in ‘Cultural heritage conservation and environment impact assessment by non-destructive testing and micro-analysis’, (van GriekenRJanssensK), 19–25; 2005LondonTaylor & Francis Group.
15.
LetardiPTrentinICutugnoG: ‘Monumenti in Bronzo all’Aperto. Esperienze di Conservazione a Confronto’; 2004FirenzeNardini Editore.
16.
DilmannPBérangerGPiccardoPMatthiesenH: ‘Corrosion of metallic heritage artefacts. Investigations, conservations, and prediction for long-term behaviour’; 2007Cambridge, MAWoodhead Publishing Materials.
17.
HassairiHBousselmiLKhosrofSTikiE: ‘Characterization of archeological bronze and evalutation of the benzotriazolenefficency in alkali medium’Mater. Corros.200859(1)32–40.
18.
ScottD A‘Copper and bronze in art: corrosion, colorants’; 2002Los Angeles, CA, ConservationGetty Institute Publication.
19.
LeygrafC: ‘Atmospheric corrosion’in ‘Corrosion mechanisms in theory and practice’ (MarcusP), 2nd edn529–562; 2002Boca Raton, FLCRC Press.
20.
HernandezRPBPasztiZde MeloHGAokiIV: ‘Chemical characterization and anticorrosion properties of corrosion products formed on pure copper in synthetic rainwater of Rio de Janeiro and Sao Paulo’Corros. Sci.201052826–837.
21.
WatanabeMHigashiYIchinoT: ‘Surface observation and profiling analysis studies of corrosion products on copper exposed outdoors’J. Electrochem. Surf.2003150(2)B37–B44.
22.
FaneyJPDavisME: ‘Metallographic studies of the copper patina formed in atmosphere’Corros. Sci.198727(7)659–668.
23.
ErikssonPJohanssonLGGullmanJ: ‘A laboratory study of corrosion reactions on statue bronze’Corros. Sci.199334, 1083-1097.
24.
GraedelTENassauKFraneyJP: ‘Copper patina formed in the atmosphere – I’Corros. Sci.198727(7)639–657.
25.
PayerJHBallGRickettBIKimHS: ‘Role of transport properties in corrosion product growth’Mater. Sci. Eng. A1995A19891–102.
26.
KrätschmerAWallinderIOLeygrafC: ‘The evolution of outdoor copper patina’Corros. Sci.200244425–450.
27.
OrganRM: ‘Aspects of bronze patina and its treatment’Stud. Conserv.196381–9.
28.
ScottDA: ‘Bronze disease: a review of some chemical problems and the role of relative humidity’J. Am. Inst. Cons.199029(2)193–206.
29.
MorselliLBernardiEChivariCBrunoroG: ‘Corrosion of 85-5-5-5 bronze in natural and synthetic acid rain’Appl. Phys. A200479A363–367.
30.
WattJTidbladJKuceraVHamilton (eds.)R: ‘The effects of air pollution on cultural heritage’; 2009New YorkSpringer.
31.
OeschenSFallerM: ‘Environmental effects on materials: the effects of the pollutants SO2, NO2, NO and O3 on the corrosion of copper, zinc and aluminum. A short literature survey and results of laboratory exposure’Corros. Sci.199739(9), 1505-1530.
32.
StrandbergHJohanssonLG: ‘Role of O3 in the atmospheric corrosion of copper in the presence of SO2’J. Electrochem. Soc.1997144(7), 2334-2342.
33.
SamieFTidbladJKurceraVLeygrafC: ‘Atmospheric corrosion effects of HNO3’J. Electrochem. Soc.2007154(5)C249–C254.
34.
KhaledKFAminMA: ‘Dry and wet lab studies for some benzotriazole derivates as possible corrosion inhibitors for copper in 1 MHNO3’Corros. Sci.200951, 2098-2106.
35.
TidbladJLeygrafC: ‘Atmospheric corrosion effects of SO2 and NO2: a comparison of laboratory and field exposed copper’J. Electrochem. Soc.1995142(3)749–756.
36.
de RyckIvan BiezenELeyssensKAdriaensAStormePAdamsF: ‘Study of tin corrosion: the influence of alloying elements’J. Cult. Heritage20045189–195.
37.
IngelbrechtCAdriaensAMaierEA: ‘Certification of arsenic, lead, tin and zinc (mass fractions) in five copper alloys CRM 691’, EUR 19778/1, Office for Official Publications of the European Communities, Luxembourg2001.