Influence of Pd and Ru additions on stress corrosion cracking of austenitic stainless steels

Abstract

The influence of minor alloying platinum group metal additions on stress corrosion cracking (SCC) of austenitic stainless steels has been investigated in simulated pressurised water reactor environments. Crack propagation studies, employing tensile specimens precracked in acidified potassium tetrathionate and subsequently loaded in proving rings revealed that 1 wt-% ruthenium additions improved the resistance of 304 stainless steels to SCC. Analytical transmission electron microscopy was used to characterise crack tips and surface oxides after high temperature SCC tests. Enrichment of ruthenium and molybdenum within the dual oxide surface layers was observed in the ruthenium modified stainless steel, which is likely to have occurred during potassium tetrathionate pre-exposure and promoted intergranular SCC mitigation. Palladium additions (1 wt-%) showed no beneficial effects to SCC, and this was associated with the formation of second phases PdMn particles upon sensitisation, which decreased the availability of Pd.

Keywords

Noble metal alloying Stress corrosion cracking ATEM Crack tip

Get full access to this article

View all access options for this article.

References

Tice

D. R.

Platts

Rigby

Stairmand

and Fairbrother

H. J.

: ‘Environmentally assisted crack growth of cold-worked type 304 stainless steel in PWR environments’ Proc. 12th Int. Conf. on ‘Environmental degradation of materials in nuclear systems – water reactors’, Salt Lake City, UT, USA, August 2005, TMS, 1037-1048.

Arioka

Yamada

Terachi

and Miyamoto

: ‘Temperature, potential and sensitization effects on intergranular crack growth and crack-tip appearance of cold worked 316’, Proc. 13th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems – water reactors’, Whistler, BC, Canada, August 2007, Canadian Nuclear Society.

Andresen

P. L.

: ‘Emerging issues and fundamental processes in environmental cracking in hot water’, Corrosion 2008 64 (5) 439–464.

Terachi

Yamada

Chiba

and Arioka

: ‘Influence of cold work on IGSCC of 316 stainless steel in hydrogenated high-temperature water’ Proc. Conf. Corrosion 2007, Nashville, TN, USA, March 2007, NACE International, Paper 07605.

Arioka

Yamada

Terachi and Chiba

: ‘Cold work and temperature dependence of stress corrosion crack growth of austenitic stainless steels in hydrogenated and oxygenated high-temperature water’, Corrosion 2007 63 (12) 1114.

MBoursier

SGallet Rouillon

and Bordes

: ‘Stress corrosion cracking of austenitic stainless steel in pwr primary water: an update of metallurgical investigations performed on French withdrawn components’ Proc. Int. Symp. Fontevraud V, Paris, France, September 2002, SFEN, Paper 021.

Higginson

Newman

R. C.

and Proctor

R. P. M.

: ‘The passivation of Fe–Cr–Ru alloys in acid solutions’, Corros. Sci. 1989 29 (11/12) 1293.

Tomashov

N. D.

and Chernova

G. P.

: ‘Electrochemical and surface analysis of the Fe–Cr–Ru system in non-oxidizing acid solutions’, Prot. Met. 1975 11 379.

Streicher

M. A.

: ‘Cathodic modification as a means of improving the corrosion resistance of alloys’, Platinum Met. Rev. 1977 21 (2) 51.

10.

Tjong

S. C.

J. S.

and Ho

N. J.

: ‘Laser surface alloying of ferritic Fe–40Cr alloy with ruthenium’, Surf. Coat. Technol. 1997 90 (3) 203–209.

11.

Potgieter

J. H.

Wentzel

and Myburg

: ‘Effect of vapour deposition and bulk alloyed ruthenium on corrosion resistance of a duplex stainless steel in suphuric acid’, Surf. Eng. 1992 8 (4) 289.

12.

Connolly

Cooper

Deng

Knott

Saxey

Cerezo

Smith

Grovenor

Necib

Govender

Lyon

Sherry

Fones

Pratt

and Rowsell

: ‘SCC and atom probe studies of 304 stainless steel as a function of palladium and ruthenium alloying additions’ Proc. Conf. Corrosion 2009, Atlanta, GA, USA, March 2009, NACE, Research in progress.

13.

Scenini

Govender

Lyon

S. B.

and Sherry

A. H.

: ‘Stress corrosion cracking of Ru doped 304 stainless steel in high temperature water’ Corros. Eng. Sci. Technol. 2012 47 (7) 498–506.

14.

Hettiarachchi

: ‘NobleChem^TM for commercial power plant application’ Proc. Int. Conf. on ‘Water chemistry in nuclear reactor systems’, Avignon France, April 2002, FNES, Paper 59.

15.

Andresen

P. L.

Kim

Y. J.

Diaz

T. P.

and Hettiarachchi

: ‘Mitigation of SCC by On-line Noblechem’ Proc. 13th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems – water reactors’, Whistler, BC, Canada, August 2007, Canadian Nuclear Society, 1465-1485.

16.

Andresen

P. L.

Kim

Y. J.

Diaz

T. P.

and Hettiarachchi

: ‘Online NobleChem mitigation of SCC’ Proc. 12th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems – water reactors’, Salt Lake City, UT, USA, August 2005, TMS727–743.

17.

Kim

Y. J.

Niedrach

L. W.

and Andresen

P. L.

: ‘Corrosion potential behavior of noble metal-modified alloys in high-temperature water’, Corrosion 1996 52 (10) 738–743.

18.

Kim

Y-J

Niedrach

L. W.

and Andresen

P. L.

: ‘Recombination kinetics on catalytic surface of noble metal alloy in high temperature water’ Proc. Conf. Corrosion ’96, Denver, CO, USA, March 1996, NACE, Paper 104.

19.

Kim

Y.-J.

: ‘Effect of noble metal addition on electrochemical polarization behavior of hydrogen oxidation and oxygen reduction on type 304 stainless steel in high-temperature water’, Corrosion 1999 55 (5) 456–461.

20.

Andresen

P. L.

Diaz

T. P.

and Hettiarachchi

: ‘Resolving electrocatalytic SCC mitigation issues in high temperature water’ Proc. Conf. Corrosion 2004, New Orleans, LA, USA, March–April 2004, NACE, Paper 0466816.

21.

Kim

Y. J.

Andresen

P. L.

Gray

D. M.

Lau

Y. C.

and Offer

H. P.

: ‘Corrosion potential behavior in high-temperature water of noble metal-doped alloy coatings deposited by underwater thermal spraying’ Proc. Conf. Corrosion’96, Denver, CO, USA, March 1996, NACE, Paper 107440–446.

22.

Indig

M. E.

and Nelson

J. L.

: ‘Electrochemical measurements and modelling predictions in boiling water reactors under various operating conditions’, Corrosion 1991 47 (3) 202–209.

23.

Arioka

Yamada

Terachi

and Staehle

R. W.

: ‘Intergranular stress corrosion cracking behavior of austenitic stainless steels in hydrogenated high-temperature water’, Corrosion 2006 61 (01) 74–83.

24.

Arioka

Yamada

Terachi

and Miyamoto

: ‘Dependence of stress corrosion cracking for cold-worked stainless steel on temperature and potential, and role of diffusion of vacancies at crack tips’, Corrosion 2008 64 (9) 691–706.

25.

Andresen

P. L.

and Young

L. M.

: ‘Characterization of the roles of electrochemistry, convection and crack chemistry in stress corrosion cracking’ Proc. 7th Int. Symp. on ‘Environmental degradation of materials in nuclear power system – water reactor’, Breckenridge, CO, USA, August 1995, NACE579–596.

26.

Scenini

and Sherry

A. H.

: ‘SCC of sensitized 304SS in high temperature water with anionic impurities contamination’ Corrosion to be published.

27.

Horner

D. A.

: ‘Application of noble metal technology to a pressurised water reactor to mitigate stress corrosion cracking in dead spaces’ PhD thesis, UMIST, Manchester, UK 2002.

28.

Sieradzki

and Newman

R. C.

: ‘A percolation model for passivation in stainless steels’, J. Electrochem. Soc. 1986 133, 1979-1980.

29.

Staehle

R. W.

: ‘Critical analysis of “tight cracks”’ Proc. 13th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems – water reactors’, Whistler, BC, Canada, August 2007, Canadian Nuclear Society.

30.

Thomas

L. E.

and Bruemmer

S. M.

: ‘Microstructural and microchemical characterization of intergranular stress corrosion cracks in irradiated type 304SS removed from a BWR top guide’ Proc. 11th Int. Conf. on ‘Environmental degradation of materials in nuclear systems – water reactors’, Stevenson, WA, USA, August 2003, American Nuclear Society.

31.

Bruemmer

S. M.

and Thomas

L. E.

: ‘Comparison of IGSCC crack-tip characteristics produced in BWR oxidizing water and BWR hydrogen water chemistry conditions’ Proc. 13th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems – water reactors’, Whistler, BC, Canada, August 2007, Canadian Nuclear Society.

32.

Macdonald

D. D.

: ‘Critical issues in the use of metals and alloys in sulphur-containing aqueous systems’ OSTI Governament Report, DOE, Washington, DC, USA 1983.

33.

Oudar

and Marcus

: ‘Role of adsorbed sulphur in the dissolution and passivation of nickel and nickel–sulfur alloys’, Appl. Surface Sci. 1979 3 48.

34.

Scott

P. M.

: ‘2000 F. N. Speller Award Lecture: stress corrosion cracking in pressurized water reactors – interpretation, modelling and remedies’, Corrosion 2000 56 (8) 771.

35.

Ford

P. F.

and Andresen

P. L.

‘Corrosion mechanisms in theory and practice corrosion in nuclear systems: environmentally assisted cracking in light water reactors’; 1994

New York

Marcel Dekker.

36.

Govender

Lindsay

Walton

and Lyon

S. L.

: ‘Surface characterisation studies of films deposited on virgin and ruthenium-modified austenitic stainless steels in acidified tetrathionate solution’ to be published.

37.

Betts

A. J.

and Newman

R. C.

: ‘The effect of alloyed molybdenum on the activation of anodic dissolution by reduced sulphur compounds’, Corros. Sci. 1993 34 (9), 1551-1555.

38.

Lozano-Perez

Yamada

Terachi

Schroder

English

C. A.

Smith

G. D. W.

Grovenor

C. R. M.

and Eyre

B. L.

: ‘Multi-scale characterization of stress corrosion cracking of cold-worked stainless steels and the influence of Cr content’, Acta Mater. 2009 57 (18), 5361-5381.