Stress corrosion cracking (SCC) tests were conducted on American Petroleum Institute (API) grade X-70 line pipe steel using smooth specimens in a standard near neutral pH solution, NS4. Both constant loading and cyclic loading conditions were employed. There were some SCC cracks on the surfaces of specimens under constant loading conditions when the applied load and test duration were appropriate. These cracks were related to stress concentration at corrosion pits. Generally, the local strain rate around corrosion pits in constant load tests was not high enough for the transition from pits to cracks to take place, and so long test times were needed for crack initiation. In contrast, cyclic loading tests facilitated near neutral pH SCC by making the local strain rate at the crack tip change under the applied load spectrum and by enhancing the crack tip local strain rate, which appreciably shortened the crack initiation incubation.
DelantyB. and J. O'Beirne: Oil Gas J., 199290, (24), 39.
4.
ParkinsR. N.: in ‘Research topical symosia’1; 1996Houston, TXNACE.
5.
WenkR. L.: Proc. 5th Symp. (November) on ‘Line pipe research’Arlington, VA, USA1974American Gas AssociationT–1.
6.
ParkinsR. N.: ‘A review of stress corrosion cracking of pipelines in contact with near-neutral (low) pH solutions’Report PR-232-9701 toPRCI at the American Gas AssociationHouston, TX, USA1999.
7.
Gonzalez-RodrguezJ. G.CasalesM.Salinas-BravoV. M.AlbarranJ. L. and MartinezL.: Corrosion200258584–590.
8.
MeyerM.ScoppioL.RuddB.Lo PiccoloE.MattewsS. and JansenJ. P.Proc. 14th Biennal Joint Technical Meet. on ‘Pipeline research’Berlin, Germany2003Pipeline Research Council InternationalMay 2003 paper 5.
9.
EadieR. L.SzklarzK. E. and SutherbyR. L.: Corrosion200561167–173.
10.
WilliamsB. W.LambertS. B.SutherbyR. and PlumtreeA.: Corrosion20046095–103.
11.
BeenJ.LuH.EadieR.ShenG. and SutherbyR.: ‘Corrosion 2004’; 2004Houston, TXNACE InternationalPaper No. 40552.
12.
FesslerR. R. and KristK.: ‘Corrosion 2000’; 2000Houston, TXNACE InternationalPaper No. 00370.
13.
GabettaG.DilibertoS.BennardoA. and ManciniN.: Brit. Corros. 12001, 36 24–28.
14.
ElboujdainiM.WangY. Z.RevieR. W.ParkinsR. N. and ShehataM. T.‘Corrosion 2000’; 2000Houston, TXNACE International.
15.
WangS. H.ChenW.JackT.KingF.FesslerR. R. and KristK.: Proc. 2000 Int. Pipeline Conf.New York, NY October 2000ASME1005.
16.
GuB.YuW. Z.LuoJ. L. and MaoX.: Corrosion199955, (3), 312.
17.
BeaversJ. A. and HarleB. A.Proc. 1996 Int. Pipeline Conf.New York, NY, USA1996ASME555June.
18.
National Energy Boad: ‘Report of public inquiry concerning stress corrosion cracking on canadian oil and gas pipelines’MH-2-95, Canada1996.
19.
RebakR. B.XiaZ. and Szklarska-SmialowskaS.: Corrosion199652, (5), 396.
20.
Office of Pipeline Safety: ‘Stress corrosion cracking Study’TTO Number 8Integrity Management ProgramMoon Township, PA2005.
21.
WangY. Z.RevieR. W. and ParkinsR. N.‘Corrosion 99’1999Houston, TXNACEPaper No. 143.
22.
Canadian Energy Pipeline Association: Proc. Public Inquiry Concern. SCC on ‘Canadian oil and gas pipelines’ Vol. 28; 1996CalgaryCEPA.
23.
HanE.FangB.WangJ. and KeW.: Proc. 30 Anniversary of Japan Society of Corrosion EngineeringTokyo, Japan April 2004JSCE pp 23–30.
24.
FangB.HanE.WangJ. and KeW.: Acta Metall Sin., 2005, 411174–1182.
25.
ParkinsR. B.BlanchardW. K.JR, and DelantyB. S.: Corrosion199450394.
26.
‘Standard practice for slow strain rate testing to evaluate the susceptibility of metallic materials to environmentally assisted cracking’129–200ASTMWest Conshohocken, PA, USA2000.
27.
FangB.: ‘Stress corrosion cracking of high-strength pipeline steels in near-neutral pH environments’PhD thesisInstitute of Metal Research, Chinese Academy of Sciences, Shenyang, China2005.
28.
FangB.AtrensA.WangJ.HanE.ZhuZ. and KeW.: J. Mater. Sci., 200338127–132.
29.
LideD. R.: ‘Handbook of chemistry and physics’78th edn; 1997–1998New YorkCRC.
30.
DeanJ. A.: ‘Lange's handbook of chemistry’13th edn; 1985New YorkMcGraw-Hill.
31.
EvansU. R.: Corrosion19517238–244.
32.
GalveleJ. R.: J. Electrochem. Soc., 1976123464–474.
33.
PistoriusP. C. and BursteinG. T.: Philos. Trans. Royal Soc. (London) A1992341A531–559.
34.
LiW.WangX. and NobeK.: J. Electrochem. Soc., 19901371184–1188.
35.
GalveleJ. R.: Corros. Sci., 198121551–579.
36.
EvansU. R.: ‘The corrosion and oxidation of metals’383; 1960LondonEdward Arnold.
37.
WangY. Z.RevieR. W.ShehataM. T.ParkinsR. N. and KristK.: Int. Pipeline Conf. Vol. 1529; 1998New YorkASME.
38.
WangS. H. and ChenW.: Mater. Sci. Eng. A2002325, (1-2), 144.
39.
WangS. H.ZhangY. and ChenW.: J. Mater. Sci., 200136, (8), 1931.
ZhengW.MacleodF. A.RevieR. W.TysonW. R.ShenG.KiffD.SkaffM. and WongE. W.: in ‘European Federation of corrosion publications’; 1996Nice, France The Institute of Materialspp. 282–292.