Several developments and novel applications of slow strain rate testing for stress corrosion cracking are described. Included are on site plant use, increasing pressure tests, component and hollow tensile specimens, and the incorporation of heat transfer effects into a specimen suitable for high pressure, high temperature applications. The application of slow strain rate testing, its advantages, disadvantages and some recent criticisms are also reviewed, together with its use as a tool for obtaining mechanistic insights.
KaneR D, (ed.): ‘Slow strain rate testing for the evaluation of environmentally induced cracking: research and engineering applications’ASTM STP 1210ASTMPhiladelphia, PA, USA1993.
5.
IndigMEVermilyeaDA: ‘High temperature, high pressure electrochemistry in aqueous solutions’(JonesD d e G, ..); 1976Houston, TXNACE.
GarzarolliFAlterDDewesP: Proc. 2nd Int. Symp. on ‘Environmental degradation of materials in nuclear systems – water reactors’Monterey, CA, USA, September 1985ANS451–461.
9.
PoulsonBArupH: Proc. 7th Scandinavian Corrosion Conf.Trondhiem, Norway, May 1975SINTEF661.
10.
LudwigsenPBArupH: Corrosion197632430.
11.
PoulsonB: Proc. Conf. on ‘Corrosion testing and monitoring’London, UKMarch-April1977Institute of Corrosion Science and Technology112–138.
NelsonJLFloreenS: Proc. 2nd Int. Symp. on ‘Environmental degradation in nuclear power systems – water reactors’Monterey, CA, USA September 1985ANS632–639.
PoulsonB: Presented at EFC Conf. on ‘Environmental sensitive cracking problems in nuclear installations containing high temperature water’Munich, Germany, September 1984EFC.
20.
YusudeMTokunayaSTazeTHineF: Corrosion198541720.
21.
GloverDM: Corros. Sci.1980201185–1193.
22.
GarnseyR: ‘Ferritic steels for fast reactor steam generators’383; 1978LondonBNES.
23.
SchroederWCBerkAA: US Bur. Mines Bull.194144383.
24.
MilletPJFentonJM: Proc. 5th Int. Conf. on ‘Environmental degradation of materials in nuclear power plants: water reactors’La Grange Park, IL, USAAugust1992ANS.
25.
EngelhardGRUrquidi-MacdonaldMSehgaAMacdonaldDDMilletPJ: ‘Control of corrosion on the secondary side of steam generators’(StaehleR W, ..); 1996Houston, TXNACE.
26.
ShodaYTakamatsuHKadakamiETakamiKKamioRAriokaKHattoriTOhtoHOkamotoS: ‘Control of corrosion on the secondary side of steam generators’(StaehleR W, ..); 1996Houston, TXNACE.
27.
LumsdenJBPollockGAStockyPJMilletPJFaschonC: Proc. 8th Int. Symp. on ‘En degradation of materials in NPS water’, La Grange IL, USA, August 1997, IS108–112.
BussertBHWKimbalKJ: ‘Control of corrosion on the secondary side of steam generators’(StaehleR W, ..); 1996Houston, TXNACE.
30.
RookeDPCartwrightDJ: ‘Compendium of stress intensity factors’; 1976LondonHMSO.
31.
PoulsonB: Corros. Sci.200446729–753.
32.
PoulsonB: ‘A laboratory stress corrosion test incorporating heat transfer’Proc. 13th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems’Whistler, BC, Canada August 2007CNS.
33.
PoulsonBEvansVBignoldG: ‘Possible alternatives to sodium phosphate for non-volatile pH control in steam generators’Proc. 14th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems’Virginia Beach, VA, USA, August 2009ANS1088–1099.
34.
BroadbentDLewisGGWettonEAM: J. Chem. Soc., 1977464–468.
35.
ParkinsRN: ‘SCC test methods: physical aspects’in ‘The theory of SCC in alloys’, (ed. ScullyJ C), 449–468; 1971BrusselsNATO.
36.
ParkinsRNMarshGPEvansJT: ‘Strain rate effects in environmental sensitive fracture’in ‘Predictive methods for assessing corrosion damage to BWR piping and PWR steam generators’, (ed. OkadaHStaehleR W), 249–260; 1982HoustonNACE.
37.
AndresenPLAngeliuTMYoungLM: ‘Immunity thresholds and other SCC fiction’in ‘Chemistry and electrochemistry of SCC: a symposium honouring the contributions of R. W. Staehle’, (ed. JonesR H); 2001Warrendale, PATMS.
38.
AgrawalAKWelchGBegleyJAStaehleRW: Proc. Conf. Corrosion ’78Houston, TX, USA, March 1978NACE187.
39.
SpiedelMOMagdowskiR: Proc. Int. Symp. on ‘Plant aging and life predictions of corrodible structures’, (ed. ShojiTShibataT), 951–955; 1997Houston, TXNACE.
40.
FordP: ‘Technical and management challengers associated with structural materials degradation in nuclear reactors in the future’Proc. 13th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems’Whistler, BC, Canada, August 2007CNS.
41.
BerrisfordRA: Private communication2007.
42.
NikiforovaVM: in‘Stress corrosion cracking of metals’(trans. V. V. Romanov)50; 1961JerusalemIsrael Programme for Scientific Translation.
IndigME: ‘SSRT for hydrogen water chemistry verification in BWRs’in ‘Slow strain rate testing for the evaluation of environmentally induced cracking, research and engineering applications’, (ed. KaneR D), ASTM STP 1210; 1993Philadelphia, PAASTM.
46.
ParkinsRN: Br. Corros.1972715–28.
47.
StaehleRW: ‘Critical analysis of tight cracks’Proc. 13th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems’Whistler, BC, Canada, August 2007CNS.
48.
BurkeMGHermerREPhaneufMW: ‘Evidence for a corrosion slot/tunneling mechanism for lead-induced transgranular SCC of alloy 690 in PbO+10% NaOH solution’Proc. 13th Int. Conf. on ‘Environmental degradation of materials in nuclear power systems’Whistler, BC, Canada, August 2007CNS.