The corrosion resistance of nanometallic zinc, obtained by twisting specimens under hydrostatic pressure, has been evaluated. It was found that the corrosion rate was practically the same for both deformed and non-deformed zinc. The factor that changed was the nature of the corrosion, which in case of deformed zinc was quasi-uniform.
Get full access to this article
View all access options for this article.
References
1.
ERBELS.: Pr. Nauk. Politech. Warszawskiej, Mech., 1976, 381—92.
2.
ERBELS.: Mechanik196639, (10), 535–538.
3.
‘Maly poradnik mechanika’ ; 1960WarszawaParistowe Wydawnictwo Techniczne.
4.
SHREIRL. L.: in ‘Korozja’ Vol. 1‘Korozja Metali i Stopow’; 1966Warszawa Wydawnictwo Naukowo Techniczne.
5.
AKIMBOG. W.:, ‘Podstawy nauki o korozji i ochronie metali’; 1952KatowicePaiistowe Wydawnictwo Techniczne.
6.
COXG. L.: Ind. Eng. Chem. Res., 193123902.
7.
POURBAIXM.: ‘Wyklady z korozji elektrochemicznef; 1978WarszawaPaiistowe Wydawnictwo Naukowe.
8.
CERNYAKOLEKTIVM.: ‘Korozni vlastnosti kovovych kons-truksénich materialu’; 1986PrahaNakladatelstvi Technicke Literatury.
9.
TOMASZOWN. D.: ‘Teoria korozji i ochrony metali’; 1962WarszawaPaiistowe Wydawnictwo Naukowe.
10.
BLICHARSKIM.: ‘Wst,ep do materialoznawstwa’; 2000KrakowWydawnictwo AGH.