Abstract
The processability, curing characteristics, and mechanical properties of a window seal compound based on highly filled and oil extended EPDM rubber (R-EPDM) containing ground EPDM vulcanisate of known composition (W-EPDM) simulating the waste window seal product have been studied. A conventional mechanical grinder with a rotating abrasive wheel was used for grinding the aged vulcanisate. The Mooney viscosity of R-EPDM increased linearly with volume fraction of W-EPDM. Rheological behaviour, studied using a Monsanto processability tester in the shear rate range of 306 7 to 1533 s-1, showed that the surface smoothness of the R-EPDM extrudates was slightly impaired by the addition of W-EPDM, although the die swell remained almost constant. Mooney scorch time decreased with progressive addition of W-EPDM, presumably owing to the migration of accelerators from W-EPDM to R-EPDM. While the minimum rheometric torque M L increased, the maximum rheometric torque M H and Deltatorque (i.e. M H-M L) decreased with increasing loading of W-EPDM. The decrease in Δtorque may be due to the migration of sulphur from R-EPDM to W-EPDM. Although the tensile strength and elongation at break remained almost constant, the modulus, hardness, abrasion resistance, and tear strength of the vulcanisates progressively decreased with W-EPDM loading. While hysteresis loss of the vulcanisates decreased, resilience increased slightly and the tension set remained constant as the W-EPDM loading increased. The deterioration in some physical properties on incorporation of the ground vulcanisate up to a loading of 200 phr is marginal compared with previously reported results on utilisation of ground waste rubbers such as cryoground rubber tyres in virgin rubbers.
Get full access to this article
View all access options for this article.