Influence of crack speed on fracture energy in amorphous and rubber toughened amorphous polymers

Abstract

To study the influence of the crack speed at initiation on measurements of the toughness of amorphous polymers such as polycarbonate (PC) and rubber toughened poly(methyl methacrylate) (RTPMMA), ‘compact tension’ specimens were tested at a medium loading rate (0·6 m s^-1 ). The specimens were equipped to allow location of the position of the crack tip and to trigger a photograph on passage of the crack. The experimental procedure was validated using PC for which the crack speed was found to change suddenly over very short distances, owing to stick–slip propagation. Conversely, fracture tests on RTPMMA showed that the acceleration of the crack tip, due to the decrease in fracture energy with crack speed, is controlled by a process zone, the size of which did not allow the systematic use of linear elastic fracture mechanics. The rapid crack propagation regime in RTPMMA corresponds to a propagation stabilised at the macroscopic crack branching velocity. This constant crack speed corresponds to frustrated microbranching and leads to non-unique values of the fracture energy at the macroscopic branching velocity.

Get full access to this article

View all access options for this article.

References

STOJIMIROVIC

and CHUDNOVSKI

: Int. J. Fract., 1992, 57, 281–289.

MAUZAC

and SCHIRRER

: J. Mater. Sci., 1992, 25, (12), 5125–5133.

BEGUELIN

Ph.

, FOND

, and KAUSCH

H.-H.

: J. Phys. IV France, 1997, 7, C3 867–872.

BEGUELIN

Ph.

, FOND

, and KAUSCH

H.-H.

: Int. J. Fract., 1998, 89, 85–102.

LAZZERI

and BUCKNALL

C. B.

: J. Mater. Sci., 1993, 28, 6799-6808.

DOMPAS

and GROENINCKX

: Polymer, 1994, 35, 4743–4749.

BUCKNALL

C. B.

, KARPODINIS

, and ZHANG

x C.

: J. Mater. Sci., 1994, 29, 3377-3383.

Ph. BÉGUELIN: Approche expérimentale du comporte-ment mécanique des polymeres en sollicitation rapide’, PhD thesis no. 1572, Swiss Federal Institute of Technology, Lausanne, Switzerland, 1996.

FREUND

L. B.

: J. Mech. Phys. Solids, 1972, 20, 129–140.

10.

BERTHET

: ‘Mesure de la ténacité des polymeres sous haute vitesse de sollicitation; validité de la mécanique linéaire de la rupture’, Mémoire de D.E.A. de physico-chimie macromoléculaire, Université Louis Pasteur, Strasbourg, France, 1993.

11.

FOND

, LOBBRECHT

, and SCHIRRER

: Int. J. Fract., 1996, 77, 141–159.

12.

SCHIRRER

, FOND

, and LOBBRECHT

: J. Mater. Sci., 1996, 31, 6409-6422.

13.

JOHNSON

F. A.

and RADON

: J. Polynt. Sci., 1973, 11, 1995-2020.

14.

TAKAHASHI

, MATSUSHIGE

, and SAKURADA

: J. Mater. Sci., 1984, 19, 4026-4034.

15.

SHIOYA

, KOGA

, FUJIMOTO

, and ISHIDA

: J. Phys. 1988, 49, (suppl. to 9), C3 253–260.

16.

SHENG

J. S.

and ZHAO

Y.-P.

: Lett. Fract. Micromech., 2000, 98, 9–14.

17.

NILSSON

: Int. J. Fract. Mech., 1972, 8, 403–411.

18.

POPELAR

C. H.

and ATKINSON

: J. Mech. Phys. Solids, 1980, 28, (14), 77–93.

19.

THESKEN

J. C.

: ‘A theoretical and experimental investi-gation of dynamic delamination in composites’, Report of The Aeronautical Research Institute of Sweden, FFA-TN, Vol. 57, 1994.

20.

FOND

and SCHIRRER

: J. Phys. IV France, 1997, 7, C3 969–974.

21.

FOND

and SCHIRRER

: in Proc. Conf. ESIS, Les Diablerets, Switzerland, September 1999, p. 145.

22.

FOND

and SCHIRRER

: in Proc. Conf. ‘Deformation, yield, and fracture of polymers’, Churchill College, Cambridge, UK, April 2000, Institute of Materials, pp. 37–40.

23.

FOND

: ‘Endommagement des polymeres “choc”: modélisations micromécaniques et comportements ala rupture’, Mémoire d'Habilitation àDiriger des Recherches, Université Louis Pasteur, Strasbourg, France, 2000.

24.

FOND

and SCHIRRER

: Notes aux GRAS, 2001, Hb, 5.

25.

SHARON

and FINEBERG

: Nature, 1999, 397, 333–335.