Abstract
Aim
The aim of this study was to assess the effects of four enamel preparation techniques on shear bond strength (SBS) of brackets bonded with a resin-modified glass ionomer cement (RMGIC). Adhesive Remnant Index (ARI) and enamel surface roughness (Ra) were also investigated after cement removal.
Materials and methods
One hundred and forty-four human premolars were divided into four groups (n = 36 in each group) as follows: Group 1, 37% phosphoric acid (i.e. conventional); Group 2, sandblasting; Group 3, sodium hypochlorite and 37% phosphoric acid; and Group 4, sodium hypochlorite and sandblasting. Twenty-four hours after bonding, the brackets were debonded with an Instron machine using a crosshead speed of 1·0 mm/min; the ARI was evaluated by an image analyser system; the Ra was measured by profilometry; and the morphology of the tooth enamel surface was observed by scanning electron microscope evaluation. Data were submitted to ANOVA and the Kruskal–Wallis test (α = 0·05).
Results
Mean SBS values for Groups 1–4 were 13·86, 9·08, 17 and 9·63 MPa, respectively. Mean ARI for Groups 1–4 were 11·16, 2·06, 20·66 and 3·73%. The SBS and ARI showed statistically significant differences between the four groups (P<0·001). The Ra (μm) showed no significant differences between groups.
Conclusions
Bracket bonding using RMGIC showed adequate adhesion for clinical use, and the type of enamel preparation had a significant influence.
Keywords
Get full access to this article
View all access options for this article.