Weld decay, a severe type of intergranular corrosion in the heat affected zone (HAZ), is a common and serious problem during welding of austenitic stainless steels. Grain boundary engineering (GBE) has been attracting attention as an effective method to prevent weld decay. Remarkably high resistance to weld decay has been reported for grain boundary engineered (GBEed) austenitic stainless steels. In practical applications, however, deformation and welding after the GBE process during manufacturing may alter the grain boundary character distribution and the resistance to weld decay. This study examined the effect of strain plus welding on the intergranular corrosion resistance in the weld HAZ of GBEed 304 austenitic stainless steel. The results show that the GBEed steel retained a much higher corrosion resistance than as received and non-GBEed steel during the same strain plus welding process, even though for both steels the corrosion resistance exhibited a gradual decrease with increasing strain.
KaurisI. and GustW.: ‘Fundamentals of grain and interphase boundary diffusion’, 1988, Stuttgart, Ziegler Press.
2.
Le CozeJ. and BiscondiM.: ‘Précipitation intergranulaire dans des bicristaux orientés d'aluminium-cuivre’, Can. Metall. Q., 1974, 13, 59–63.
3.
FromentM.: ‘Sur le mécanisme de la corrosion intergranulaire des matériaux métalliques’, J. Phys., 1975, 36, 371–385.
4.
QianX. R. and ChouY. T.: ‘Correlation between grain boundary corrosion and grain boundary energy in niobium bicrystals’, Philos. Mag. A, 1982, 45, 1075–1079.
5.
KokawaH., WatanabeT. and KarashimaS.: ‘Sliding behaviour and dislocation structures in aluminium grain boundaries’, Philos. Mag. A, 1981, 44, 1239–1254.
6.
PumphreyP. H.: ‘Special high angle boundaries’, in ‘Grain boundary structure and properties’, (ed. ChadwickG. A. and SmithD. A.., 139–200; 1976, London, Academic Press.
7.
PalumboG. and AustK. T.: ‘Structure-dependence of intergranular corrosion in high purity nickel’, Acta Metall. Mater., 1990, 38, 2343–2352.
8.
KokawaH., ShimadaM. and SatoY. S.: ‘Grain-boundary structure and precipitation in sensitized austenitic stainless steel’, JOM, 2000, 52, 34–37.
9.
WatanabeT.: ‘An approach to grain boundary design for strong and ductile polycrystal’, Res. Mech., 1984, 11, 47–84.
10.
PalumboG., LehockeyE. M. and LinP.: ‘Applications for grain boundary engineered materials’, JOM, 1998, 50, 40–43.
11.
ShimadaM., KokawaH., WangZ. J., SatoY. S. and KaribeI.: ‘Optimization of grain boundary character distribution for intergranular corrosion resistant 304 stainless steel by twin-induced grain boundary engineering’, Acta Mater., 2002, 50, 2331–2341.
12.
KokawaH.: ‘Weld decay-resistant austenitic stainless steel by grain boundary engineering’, J. Mater. Sci., 2005, 40, 927–932.
13.
KokawaH.: ‘Potential of grain boundary engineering to suppress welding degradations of austenitic stainless steels’, Sci. Technol. Weld. Join., 2011, 16, 357–362.
14.
WatanabeT.: ‘Grain boundary engineering: historical perspective and future prospects’, J. Mater. Sci., 2011, 46, 4095–4115.
15.
KobayashiS., TsurekawaS., WatanabeT. and PalumboG.: ‘Grain boundary engineering for control of sulfur segregation-induced embrittlement in ultrafine-grained nickel’, Scr. Mater., 2010, 62, 294–297.
16.
LehockeyE. M. and PalumboG.: ‘On the creep behaviour of grain boundary engineered nickel 1’, Mater. Sci. Eng. A, 1997, A237, 168–172.
17.
QianM. and LippoldJ. C.: ‘The effect of annealing twin-generated special grain boundaries on HAZ liquation cracking of nickel-base superalloys’, Acta Mater., 2003, 51, 3351–3361.
18.
SaitoS., KikuchiK., HamaguchiD., TezukaM., MiyagiM., KokawaH. and WatanabeS.: ‘Corrosion–erosion test of SS316L grain boundary engineering material (GBEM) in lead bismuth flowing loop’, J. Nucl. Mater., 2012, 431, 91–96.
19.
KuriharaK., KokawaH., SatoS., SatoY. S., FujiiH. T. and KawaiM.: ‘Grain boundary engineering of titanium-stabilized 321 austenitic stainless steel’, J. Mater. Sci., 2011, 46, 4270–4275.
20.
YamadaG., KokawaH., YasudaY., TokitaS., YokoyamaT., SatoY. S., FujiiH. T. and TsurekawaS.: ‘Effect of post-GBE strain-sensitisation on corrosion resistance of grain boundary engineered 304 austenitic stainless steel’, Philos. Mag., 2013, 93, 1443–1453.
21.
LeeJ. B.: ‘Modification of the ASTM standard ferric sulfate–sulfuric acid test and copper–copper sulfate–sulfuric acid test for determining the degree of sensitization of ferritic stainless steels’, Corrosion, 1983, 39, 469–474.
22.
JonesR. and RandleV.: ‘Sensitisation behaviour of grain boundary engineered austenitic stainless steel’, Mater. Sci. Eng. A, 2010, A527, 4275–4280.
SchuhC. A., KumarM. and KingW. E.: ‘Analysis of grain boundary networks and their evolution during grain boundary engineering’, Acta Mater., 2003, 51, 687–700.
25.
SchuhC. A., MinichR. W. and KumarM.: ‘Connectivity and percolation in simulated grain-boundary networks’, Philos. Mag., 2003, 83, 711–726.
26.
WellsD. B., StewartJ., HerbertA. W., ScottP. M. and WilliamsD. E.: ‘The use of percolation theory to predict the probability of failure of sensitized, austenitic stainless steels by intergranular stress corrosion cracking’, Corrosion, 1989, 45, 649–660.
27.
MiyazawaK., IwasakiY., ItoK. and IshidaY.: ‘Combination rule of Σ values at triple junctions in cubic polycrystals’, Acta Crystallogr., 1996, A52, 787–796.
28.
FraryM. and SchuhC. A.: ‘Connectivity and percolation behaviour of grain boundary networks in three dimensions’, Philos. Mag., 2005, 85, 1123–1143.
29.
MichiuchiM., KokawaH., WangZ. J., SatoY. S. and SakaiK.: ‘Twin-induced grain boundary engineering for 316 austenitic stainless steel’, Acta Mater., 2006, 54, 5179–5184.
30.
BriantC. L. and RitterA. M.: ‘The effect of gold work on the sensitization of 304 austenitic stainless steel’, Scr. Metall., 1979, 13, 177–181.
31.
BriantC. L. and RitterA. M.: ‘The effects of deformation induced martensite on the sensitization of austenitic stainless steels’, Metall. Trans. A, 1980, 11, 2009–2017.
32.
KainV., ChandraK., AdheK. N. and DeP. K.: ‘Effect of cold work on low-temperature sensitization behaviour of austenitic stainless steels’, J. Nucl. Mater., 2004, 334, 115–132.
33.
PadilhaA. F., PlautR. L. and RiosP. R.: ‘Annealing of cold-worked austenitic stainless steels’, ISIJ Int., 2003, 43, 135–143.