Laser GMA hybrid welds, producing partial penetration, were conducted on stiff tubes made of S460NH. Experiments, using a design-of-experiments plan were conducted to examine the influence of the welding parameters on the occurrence of solidification cracks. Results say that cracks diminish, when high levels of arc power are applied, while their number increases with rising laser beam power. The weld velocity had no measurable impact.
GebhardtM., GumenyukA. and RethmeierM.:‘Hybrid process welds — thick-walled tubes’, Weld. J., 2012, 91, 55–61.
2.
MooreP. L., HowseD. S. and WallachE. R.:‘Microstructures and properties of laser/arc hybrid welds and autogeneous laser welds in pipeline steels’, Sci. Technol. Weld. Join., 2004, 9, 314–322.
3.
KellyS. M., BrownS. W., TresslerJ. F., MartukanitzR. P. and LudwigM. J.:‘Laser-arc welding to reduce distortion in ship panels’, Weld. J., 2009, 88, 32–36.
4.
ReutzelE. W., SullivanM. J. and MikesicD. A.:‘Joining pipe with the hybrid laser-GMAW process: weld test results and cost analysis’, Weld. J., 2006, 85, 66–71.
5.
TusekJ. and SubanM.:‘Hybrid welding with arc and laser beam’, Sci. Technol. Weld. Join., 1999, 4, 308–311.
6.
MahrleA. and BeyerE.:‘Hybrid laser beam welding – classification, characteristics and applications’, J. Laser Appl., 2006, 18, 169–178
7.
BaggerC. and OlsenF.:‘Review of laser hybrid welding’, J. Laser Appl., 2005, 17, 2–14.
RibicB., PalmerT. A. and DebRoyT.:‘Problems and issues in laser-arc hybrid welding’, Int. Mater. Rev., 2009, 54, 223–244.
10.
CrossC. E.:‘On the origin of weld solidification cracking’, in ‘Hot cracking phenomena in welds II’; 2005, Berlin/Heidelberg, Springer Verlag.
11.
CrossC. E., ConiglioN., SchemppP. and MoussaviM.:‘Critical conditions for weld solidification crack growth’, in ‘Hot cracking phenomena in welds III’; 2011, Berlin/Heidelberg, Springer Verlag.
12.
EskinD. G. and KatgermanL.:‘A quest for a new hot tearing criterion’, Metall. Mater. Trans. A, 2007, 38A, 1511–1519.
13.
BorlandJ. C. and YoungerR. N.:‘Some aspects of cracking in welded Cr–Ni austenitic steels’, Brit. Weld., 1960, 7, 22–59.
14.
NishimotoK., SaidaK., Kiuchi undK.NakayamaJ.:‘Influence of minor and impurity elements on hot cracking susceptibility of extra high-purity type 310 stainless steels’, in ‘Hot cracking phenomena in welds III’; 2011, Berlin/Heidelberg, Springer Verlag.
15.
‘Preliminary guidelines for the approval of CO2 -laser welding, Germanischer Lloyd, 1998.
16.
ShankarV., GillT. P. S., Mannan undS. L.SundaresanS.:‘Solidification cracking in austenitic stainless steel welds’, Sadhana, 2003, 28, 359–382.
17.
RaoZ. H., LiaoS. M. and TsaiH. L.:‘Modelling of hybrid laser-GMA welding: review and challenges’, Sci. Technol. Weld. Join., 2011, 16, 300–305
18.
WeiseS.:‘Heißrissbildung beim Laserstrahlschweißen von Baustählen’, PhD thesis, Universität Bremen, Bremen, Germany, 1998.
19.
MatsudaF., NakagawaH. and UeyamaT.:‘Solidification crack susceptibility in laser beam weld metal of 0·2C-low alloy steel’, Trans. JWRI, 1987, 16, 103–114.
20.
FuhrmannC.:‘Laser-Lichtbogen-Hybridschweißen bis zu Blechdicken von 25 mm’, PhD thesis, RWTH Aachen, Aachen, Germany, 2007.
21.
TsukamotoS., Irie undH.InagakiM.:‘Welding defects and molten metal behaviour in electron beam welding’, Proc. 4th Int. Symp. of J. Weld. Soc., Osaka, Japan, November 1985, S. 115–120.
22.
AbeN. and HayashiM.:‘Trends in laser arc combination welding methods’, Weld. Int., 2002, 16, 94–98.
23.
GoosP. and JonesB.:‘Optimal design of experiments: a case study approach’, 1st edn, 29; 2011, Chichester, John Wiley & Sons.