To evaluate the influence of minor and impurity elements on the solidification cracking susceptibility in austenitic stainless steel welds, the transverse Varestraint test was conducted using several extra high purity type 310 stainless steels with different amounts of C, Mn, P and S. The characteristic influence on solidification cracking could be expressed by the ratio of P/S/C≈1∶1·3∶0·56, while Mn affected solidification cracking to a negligible extent. A theoretical approach revealed that the reduced solidification cracking susceptibility with decreasing C, P and S contents could be attributed to the suppression of solidification segregation.
KujanpääVP, DavidSA, WhiteCL: ‘Formation of hot cracks in austenitic stainless steel welds – solidification cracking’, Weld. J., 1986, 65, (8), 203s–212s.
7.
KujanpääVP: ‘Effect of steel type and impurities in solidification cracking of austenitic stainless steel welds’, Metal Constr., 1985, 17, (1), 40R–46R.
8.
GoochTG, HoneycombeJ: ‘Welding variables and microfissuring in austenitic stainless steel weld metal’, Weld. J., 1980, 59, (8), 233s–241s.
9.
RabensteinerG, ToschJ, SchabereiterH: ‘Hot cracking problems in different fully austenitic weld metals’, Weld. J., 1983, 62, (1), 21s–27s.
KatayamaS: ‘Improvement in solidification cracking of fully austenitic stainless steels SUS310S’, PhD thesis, Osaka University, Osaka, Japan, 1981.
12.
LiL, MesslerRW: ‘The effect of phosphorus and sulfur on susceptibility to weld hot cracking in austenitic stainless steels’, Weld. J., 1999, 78, (12), 387s–396s.
13.
LiL, MesslerRW: ‘Segregation of phosphorus and sulfur in heat-affected zone hot cracking of type 308 stainless steel’, Weld. J., 2002, 81, (5), 78s–84s.
HullFC: ‘Effects of alloying additions on hot cracking of austenitic chromium–nickel stainless steels’, Am. Soc. Test. Mater. Proc., 1960, 60, 667–690.
16.
SaidaK, NomotoY, OkauchiH, OgiwaraH, NishimotoK: ‘Influences of phosphorus and sulphur on ductility-dip cracking susceptibility in multipass weld metal of alloy 690’, Sci. Technol. Weld. Join., 2012, 17, (1), 1–8.