Two types of rapidly solidified filler alloys of nominal composition Cu–40Mn–10Ni (C50) and Ni–7Cr–3·2B–4·5Si–3Fe (N82) were used for stainless steel (SS304) brazing joints. The C50 foil is crystalline in nature, whereas N82 foil shows amorphous structure. The SS304/C50/SS304 joint shows solid solution phases at interfacial area, with maximum bond strength of 500 MPa, which qualifies to 80% of base metal strength. Conversely, the SS304/N82/SS304 joint develops brittle CrxBy intermetallic phases, which lowers bond strength to 330 MPa.
ZhaoH, MaX, CaiZ, WangPC: ‘Effect of low temperature exposure on impact characteristics of epoxy bonded high strength steels’, Sci. Technol. Weld. Join., 2011, 16, 405–411.
SunQJ, LinSB, YangCL, ZhaoGQ: ‘Penetration increase of AISI 304 using ultrasonic assisted tungsten inert gas welding’, Sci. Technol. Weld. Join., 2009, 14, 765–767.
5.
YuanX., KimM.B., ChoY.H., KangC.Y., ‘Microstructures, mechanical and chemical propertiesof TLP-bonded joints in a duplex stainless steel withamorphous Ni-based insert alloys’, Metall. Mater. Trans. A, 2012, 43A, 1989–2001.
6.
KawashimaF, IgariT, MiyoshiY, KamitoY, TanihiraM: ‘High temperature strength and inelastic behavior of plate-fin structures for HTGR’, Nucl. Eng. Des., 2007, 237, 591–599.
7.
AquaroD, PieveM: ‘High temperature heat exchangers for power plants: performance of advanced metallic recuperators’, Appl. Therm. Eng., 2007, 27, 389–400.
8.
TraversoA, MassardoFA: ‘Optimal design of compact recuperators for microturbine application’, Appl. Therm. Eng., 2005, 25, 2054–2071.
SaidaK, SakataniT, SongW, NishimotoK: ‘Hot cracking in laser braze joint of high strength stainless steel using gold brazing filler metal – prevention of hot cracking by controlling thermal cycle’, Sci. Technol. Weld. Join., 2009, 14, 254–261
12.
JangJSC, ShihHP: ‘Evolution of microstructure of AISI 304 stainless steel joint brazed by mechanically alloyed nickel base filler with different silicon content’, J. Mater. Sci. Lett., 2003, 22, 79–82.
13.
RabinkinA: ‘New applications for rapidly solidified brazing foils’, J. Weld., 1989, 68, 39–46.
14.
RabinkinA, WenskiE, RibaudoA: ‘Brazing atainless steel using a new MBF series of Ni–Cr–B–Si amorphous brazing foils’, Weld. J., 1998, 77, 66s–74s.
PhilipsNR, LeviCG, EvansAG: ‘Mechanisms of microstructure evolution in an austenitic stainless steel bond generated using a quaternary braze alloy’, Metall. Mater. Trans. A, 2008, 39A, 142.
17.
KokawaH, LeeCH, NorthTH: ‘Effect of grain boundaries on isothermal solidification during transient liquid phase brazing’, Mater. Trans. A, 1991, 22A, 1627–1631.
18.
MullinsWW: ‘Theory of thermal grooving’, J. Appl. Phys, 1957, 28, 333–339.
19.
RoyRK, PandaAK, DasSK, Govind, MitraA: ‘Development of a copper-based filler alloy for brazing stainless steels’, Mater. Sci. Eng. A, 2009, A523, 312–315.
20.
XiongH, WanC, ZhouZ: ‘Joining of Si3N4 to Si3N4 using rapidly-solidified CuNiTiB brazing filler foils’, J. Mater. Process. Technol., 1998, 75, 137–142.
HumpstonG, JacobsonDM: ‘Principles of soldering and brazing’, 1993; Metals Park, OH, ASM International.
24.
ParravanoN: Int. Z. Metallogr., 1973, 4, 171.
25.
ChenH, GongJ.-M, TuST: ‘Numerical modelling and experimental investigation of diffusion brazing SS304/BNi-2/SS304 joint’, Sci. Technol. Weld. Join., 2009, 14, 32–41.
26.
JiangW, GongJ, TuST: ‘Effect of brazing temperature on tensile strength and microstructure for a stainless steel plate-fin structure’, Mater. Des., 2011, 32, 736–742.
27.
WangW, ZhangS, HeX: ‘Diffusion of boron in alloys’, Acta Metall. Mater., 1995, 43, 1693–1699.