C/SiC composites and Nb were vacuum brazed with the Ti39·4Ni39·4Nb21·2 alloy being the active filler metal. The mechanical properties of the filler material, the microstructure and the strength of brazing joints were investigated. The results showed that the filler TiNiNb alloy has a tensile strength of 860 MPa, an elongation of 51% and an elastic modulus of 78 GPa. Both Ti and Nb elements in the filler reacted with C/SiC during the brazing process, and a well bonded C/SiC–Nb joint was obtained. The ductile filler metal released the thermal stress in the joint. When the brazing was performed at 1220°C for 20 min, the shear strength of brazed joints reached 149, 120 and 73 MPa at 20, 600 and 800°C respectively.
SchmidtS, BeyerS, KnabeH, ImmichH, MeistringR, GesslerA: ‘Advanced ceramic matrix composite materials for current and future propulsion technology applications’, Acta Astronaut., 2004, 55, 409–420.
2.
ZhouCC, ZhangCR, HuHF, ZhangYD, WangZY: ‘Preparation of 3D‐Cf/SiC composites at low temperatures’, Mater. Sci. Eng. A, 2008, A488, 569–572.
3.
LinGB, HuangJH, ZhangH, LiuHY: ‘Microstructure and mechanical performance of brazed joints of Cf/SiC composite and Ti alloy using Ag–Cu–Ti–W’, Sci. Technol. Weld. Join., 2006, 11, (4), 379–383.
4.
XiongJH, HuangJH, ZhangH, ZhaoXK: ‘Brazing of carbon fiber reinforced SiC composite and TC4 using Ag–Cu–Ti active brazing alloy’, Mater. Sci. Eng. A, 2010, A527, 1096–1101.
5.
AsthanaR, SinghM: ‘Joining of partially sintered alumina to alumina, titanium, Hastealloy and C–SiC composite using Ag–Cu brazes’, J. Eur. Ceram. Soc., 2008, 28, (3), 617–631.
6.
SinghM, AsthanaR, ShpargelTP: ‘Brazing of ceramic–matrix composites to Ti and Hastealloy using Ni‐base metallic glass interlayers’, Mater. Sci. Eng. A, 2008, A498, 19–30.
7.
XiongJT, LiJL, ZhangFZ, HuangWD: ‘Joining of 3D C/SiC composites to niobium alloy’, Scr. Mater., 2006, 55, (2), 151–154.
8.
LiuHL, LiSJ, ChenZJ: ‘Joining of Cf/SiC ceramic matrix composite using SiC–Si3N4 preceramic polymer’, Mater. Sci. Forum, 2005, 475–479, 1267–1270.
9.
SuoJ, ChenZH, HanWM, ZhengWW: ‘Joining of ceramic materials by ceramic bonding transformed from silicone resin at high temperature’, J. Chin. Ceram. Soc., 2005, 33, 386–390.
10.
ZhangJ, NakaM, FangHY, ZhouY: ‘Properties and fracture processes of Si3N4/Si3N4 joints brazed using Cu–Zn–Ti filler alloy’, Sci. Technol. Weld. Join., 2004, 9, (2), 158–162.
11.
ChenJC, HaoCY, ZhangJS: ‘Wetting behaviour of Cu based active brazing alloys on siliconised graphite’, Sci. Technol. Weld. Join., 2006, 11, (5), 600–605.
12.
MirsalehiSE, HadianAM: ‘Investigation on wetting behaviour of B4C by Ni based brazing alloys’, Sci. Technol. Weld. Join., 2010, 15, (1), 48–53.
13.
HafezKM, El‐SayedMH, NakaM: ‘Joining of alumina ceramics to metals’, Sci. Technol. Weld. Join., 2005, 10, (2), 125–130.
14.
ZhangL, FengJ, LiZ, LiuH: ‘Interface structure and strength of brazed joints between TiC ceramic and iron’, Sci. Technol. Weld. Join., 2004, 9, (3), 280–282.
15.
ZhengYF, CaiW, ZhangJX, ZhaoLC, YeHQ: ‘Microstructural development inside the stress induced martensite variant in a Ti–Ni–Nb shape memory alloy’, Acta Mater., 2000, 48, 1409–1425.
16.
XiaoF, ZhaoXQ, XuHB, JiangHC, RongLJ: ‘Damping capacity and mechanical property of NiTiNb shape memory alloys’, Acta Metall. Sin. 2009, 45, 18–24.
17.
XuJ, ZhaoXQ, GongSK: ‘Effect of Nb on oxidation behavior of NiTiNb alloys’, Trans. Nonferrous Met. Soc. China, 2006, 16, s31–s36.
18.
TaoBW, LiuJH, LiSM: ‘Oxidation behaviors of Ti44Ni47Nb9 shape memory alloy at high temperature’, Acta Metall. Sin., 2005, 41, 633–637.
19.
PiaoM, MiyazakiS, OtsukaK, NishidaN: ‘Effects of Nb addition on the microstructure of Ti–Ni alloys’, Mater. Trans., JIM, 1992, 33, 337–345.
20.
GrummonDS, ShawJA, FoltzJ: ‘Fabrication of cellular shape memory alloy materials by reactive eutectic brazing using niobium’, Mater. Sci. Eng. A, 2006, A438–A440, 1113–1118.
21.
IshikawaK, TokuiS, AokiK: ‘Microstructure and hydrogen permeation of cold rolled and annealed Nb40Ti30Ni30 alloy’, Intermetallics, 2009, 17, 109–114.
22.
LeeHK, LeeJY: ‘A study of the wetting, microstructure and bond strength in brazing SiC by Cu–X (X = Ti, V, Nb, Cr) alloys’, J. Mater. Sci., 1996, 31, 4133–4140.
23.
PrimaSB, Tret'yachenkoLA, PetyukhVM: ‘Phase relations in the Ti–TiNi–NbNi–Nb region of the ternary system Ti–Nb–Ni’, Powder Metall. Met. Ceram., 1995, 34, 155–160.
24.
YeDL, HuJH: ‘Handbook of thermodynamics data for inorganic compounds’; 2002, Beijing, Metallurgical Industry Press.
25.
ZhengHX, MentzJ, BramM, BuchkremerHP, StöverD: ‘Powder metallurgical production of TiNiNb and TiNiCu shape memory alloys by combination of pre‐alloyed and elemental powders’, J. Alloys Compd, 2008, 463, 250–256.
26.
ZhangZH, FrenzelJ, NeukingK, EggelerG: ‘On the reaction between NiTi melts and crucible graphite during vacuum induction melting of NiTi shape memory alloys’, Acta Mater., 2005, 53, 3971–3985.
27.
XuHH, DuY, ChenHL, HeYH, PanZ, SchusterJC, WangRC: ‘Isothermal section at 1000°C of the Nb–Ti–Si system’, J. Alloys Compd, 2005, 394, 235–239.
28.
LiZ, PengLM: ‘Microstructural and mechanical characterization of Nb‐based in situ composites from Nb–Si–Ti ternary system’, Acta Mater., 2007, 55, 6573–6585.
29.
GengT, LiCR, BaoJ, ZhaoXQ, DuZM, GuoCP: ‘ Thermodynamic assessment of the Nb–Si–Ti system’, Intermetallics, 2009, 17, 343–357.