AC–GTAW of aluminium – new perspective for evaluation of role of positive polarity time

Abstract

Experiments were carried out to determine the effect of the positive polarity time on cathodic cleaning, arc voltage, arc power and weld bead geometry on AC–GTAW of aluminium. Welding current was kept constant in both positive (EP) and negative polarity. During the experiments current and voltage monitoring was performed to further analysis of arc voltage and arc power. There was an increase in the weld depth and fusion areas when longer EP times were used. This behaviour differs from the traditional literature relating to welding processes with non-consumable electrodes. However, this increase occurs from a certain point, when the EP time is >4·0 ms over a total period of 20·0 ms. The use of a minimum EP time was found to be sufficient to perform the oxide removal, yielding weld beads with satisfactory fusion characteristics and minimum wear of the tungsten electrode.

Keywords

AC-TIG ALUMINIUM WELDING VARIABLE POLARITY CATHODIC CLEANING THERMIONIC EMISSION FIELD EMISSION

Get full access to this article

View all access options for this article.

References

Mathers

: ‘The welding of aluminium and its alloys’, 4–5; 2002, Cambridge, CRC Press.

Fuerschbach

P. W.

: ‘Cathodic cleaning and heat input in variable polarity plasma arc welding of aluminum’, Weld. J., 1998, 77, (2), 76s–85s.

Rocha

V. S.

and Scotti

: ‘Development and implementation of an oxide selective removal control in aluminum TIG-Welding’, Soldag. Insp. (Portugal), 2005, 10, (1), 2–9.

Seshagiri

P. C.

, Nair

B. S.

, Reddy

G. M.

, Rao

K. S.

, Bhattacharyal

S. S.

and Rao

K. P.

: ‘Improvement of mechanical properties of aluminium–copper alloy (AA2219) GTA welds by Sc addition’, Sci. Technol. Weld. Join., 2008, 2, 146–158.

Nair

B. S.

, Phanikumar

, Rao

K. P.

and Sinha

P. P.

: ‘Improvement of mechanical properties of gas tungsten arc and electron beam welded AA2219 (Al–6 wt-%Cu) alloy’, Sci. Technol. Weld. Join., 2007, 12, 579–585.

Lancaster

J. F.

: ‘The physics of welding’, 124–125; 1986, Oxford, Pergamom Press.

Scotti

, Dutra

J. C.

and Ferraresi

V. A.

: ‘The influence of parameter settings on cathodic self-etching during aluminum welding’, J. Mater. Process. Technol., 2000, 100, 179–187.

Guile

A. E.

: ‘Processes at arc cathode roots on nonrefractory metals having films of their own oxide’, in ‘Arc physics and weld pool behavior’, 79–86; 1979, Cambridge, The Welding Institute.

American Welding Society: ‘Welding handbook’, 8th edn, Vol. 2, 84–85; 1991, Miami, FL, AWS.

10.

American Society for Metals: ‘Metals handbook’, 8th edn, Vol. 6, 114–116; 1971, Metal Park, OH, ASM.

11.

Yarmuch

M. A. R.

and Patchett

B. M.

: ‘Variable AC polarity GTAW fusion behavior in 5083 aluminum’, Weld. J., 2007, 86, (7), 196s–200s.

12.

IMC-Soldagem , available at: http://www.imc-soldagem.com.br/inversal.html, 2008.

13.

SAP

LABSOLDA

, available at: http://www.labsolda.ufsc.br/projetos/projetos_viabilizados/sap_1.php, 2008.

14.

Mathers

: ‘Welding of aluminium and its alloys’, 22–24; 2002, Cambridge, CRC Press.

15.

Marya

, Edwards

G. R.

and Liu

: ‘An investigation on effects of gases in GTA welding of a wrought AZ80 magnesium alloy’, Weld. J., 2004, 83, (7), 203s–212s.

16.

Saedi

H. R.

: ‘Transient response of plasma arc and weld pool geometry for GTAW process’, PhD thesis, Massachusetts Institute of Technology, Cambridge, MA, USA, 1996.