The effect of weld filler metal austenite to acicular ferrite transformation temperature on the residual stresses that arise during the gas metal arc welding of a low carbon steel has been examined using a finite element model. It was found that the stress levels in the weld can be tailored by the appropriate selection of the filler metal and compressive, near zero or tensile residual stresses produced. Reasonable agreement was obtained between the model and the stresses measured using neutron diffraction both in welds using conventional and low transformation temperature filler metal.
MurakawaH., LuoY. and UedaY.: ‘Inherent strain as an interface between computational welding mechanics and its industrial application’, in ‘Mathematical modelling of weld phenomena’, (ed. H. Cerjak), Vol. 4, 597–619; 1998, London, Institute of Materials.
2.
DengD. and MurakawaH.: ‘Finite element analysis of temperature field, microstructure and residual stress in multi-pass butt-welded 2·25Cr–1Mo steel pipes’, Comput. Mater. Sci., 2008, 43, (4), 681–695.
3.
StoneH. J., RobertsS. M. and ReedR. C.: ‘A process model for the distortion induced by the electron-beam welding of a nickel-based superalloy’, Metall. Mater. Trans. A, 2000, 31A, (9), 2261–2273.
4.
KorsunskyA. M., JarnesK. E. and DaymondM. R.: ‘Intergranular stresses in polycrystalline fatigue: diffraction measurement and self-consistent modelling’, Eng. Fract. Mech., 2004, 71, (4–6), 805–812.
5.
PreussM., PangJ. W. L., WithersP. J. and BaxterG. J.: ‘Inertia welding nickel-based superalloy. Part II. Residual stress characterization’, Metall. Mater. Trans. A, 2002, 33A, 3227–3234.
6.
PorowskiJ. S., O'DonnellW. J., BadlaniM. L. and HamptonE. J.: ‘Use of mechanical stress improvement process to mitigate stress corrosion cracking in BWR piping systems’, Nucl. Eng. Des., 1990, 124, 91–100.
7.
ESI Group: ‘SYSWELD user manual’, ESI Group, Paris, France, 2004.
8.
LeblondJ. B., MottetG., DevauxJ. and DevauxJ. C.: ‘Mathematical models of anisothermal phase transformations in steels, and predicted plastic behaviour’, Mater. Sci. Technol., 1985, 1, 815–822.
9.
BabuS. S. and BhadeshiaH. K. D. H.: ‘Stress and the acicular ferrite transformation’, Mater. Sci. Eng. A, 1992, A156, (1), 1–9.
10.
OhtaA., SuzukiN., MaedaY., HiraokaK. and NakamuraT.: ‘Superior fatigue crack growth properties in newly developed weld metal’, Int. J. Fatigue, 1999, 21, 113–118.
11.
ShirzadiA. A., BhadeshiaH. K. D. H., KarlssonL. and WithersP. J.: ‘Stainless steel weld metal designed to mitigate residual stresses’, Sci. Technol. Weld. Join., 2009, 14, 559–565.
12.
EckerlidJ., NilssonT. and KarlssonL.: ‘Fatigue properties of longitudinal attachments welded using low transformation temperature filler’, Sci. Technol. Weld. Join., 2003, 8, 353–359.
13.
ZenitaniS., HayakawaN., YamamotoJ., HiraokaK., MorikageY., YaudaT. and AmanoK.: ‘Development of new low transformation temperature welding consumable to prevent cold cracking in high strength steel welds’, Sci. Technol. Weld. Join., 2007, 12, 516–522.
14.
Payares-AsprinoM. C., KatsumotoH. and LiuS.: ‘Effect of martensite start and finish temperature on residual stress development in structural steel welds’, Weld. J., 2008, 87, 279–289.
15.
MikamiY., MorikageY., MochizukiM. and ToyodaM.: ‘Angular distortion of fillet welded T joint using low transformation temperature welding wire’, Sci. Technol. Weld. Join., 2009, 14, 97–105.
16.
DyeD., HunzikerO. and ReedR. C.: ‘Numerical analysis of the weldability of superalloys’, Acta Mater., 2001, 49, (4), 683–697.
17.
GoldakJ., ChakravartiA. and BibbyM.: ‘A new finite element model for welding heat sources’, Metall. Trans. B, 1984, 15B, 299–305.
18.
LindgrenL. E.: ‘Finite element modelling and simulation of welding. Part 2. Improved material modelling’, J. Therm. Stresses, 2001, 24, (3), 195–231.
19.
DongP. and ZhangJ.: ‘Residual stresses in strength-mismatched welds and implications on fracture behaviour’, Eng. Fract. Mech., 1999, 64, 485–505.
20.
JensenM. V. R. S., DyeD., JamesK. E., KorsunskyA. M., RobertsS. M. and ReedR. C.: ‘Residual stresses in a welded superalloy disc: characterization using synchrotron diffraction and numerical process modelling’, Metall. Mater. Trans. A, 2002, 33A, (9), 2921–2931.
21.
StoneH. J., WithersP. J., HoldenT. M., RobertsS. M. and ReedR. C.: ‘Comparison of three different techniques for measuring the residual stresses in an electron beam-welded plate of WASPALOY’, Metall. Mater. Trans. A, 1999, 30A, 1797–1808.
22.
DaviesC. M., WimporyR. C., BérešM., LightfootM. P., DyeD., OliverE., O'DowdN. P., BruceG. J. and NikbinK. M.: ‘The effect of residual stress and microstructure on distortion in thin welded steel plates’, Proc. PVP2007 ASME Pressure Vessels and Piping Division Conf., San Antonio, TX, USA, July 2007, ASME. vol 6, 851–858.
23.
DaviesC. M., WimporyR. C., DyeD. and NikbinK. M.: ‘The effects of plate dimensions on residual stresses in welded thin steel plates’, Proc. PVP2008 ASME Pressure Vessels and Piping Division Conf., Chicago, IL, USA, July 2008, ASME. Vol 6 Pt A and B, 309–319.
24.
PangJ. W. L., HoldenT. M. and MasonT. E.: ‘The development of intergranular strains in a high-strength steel’, J. Strain Anal., 1998, 33, (5), 373–383.
25.
BhadeshiaH. K. D. H.: in ‘Handbook of residual stress and deformation of steel’, (ed. G. E. Totten et al.), 3–10; 2002, Materials Park, OH, ASM International.
26.
NishikawaH., SerizawaH. and MurakawaH.: ‘Development of a large-scale FEM for analysis mechanical problems in welding’, J. Jpn Soc. Naval Archit., 2005, 1, (2), 379–385.
27.
MurakawaH., BérešM., VegaA., RashedS., DaviesC. M., DyeD. and NikbinK. M.: ‘Effect of phase transformation onset temperature on residual stress in welded thin steel plates’, Trans. JWRI, 2008, 37, (1), 75–80.
28.
TsunoriM., DaviesC. M., DyeD. and NikbinK. M.: ‘Numerical modelling of residual stress and distortion in welded thin steel plates’, Proc. PVP2008 ASME Pressure Vessels and Piping Division Conf., Chicago, IL, USA, July 2008, ASME. Vol 6 Pt A and B, 299–307.
29.
KunduS., HaseK. and BhadeshiaH. K. D. H.: ‘Crystallographic texture of stress-affected bainite’, Proc. R. Soc. A, 2007, 463A, 2309–2328.
30.
StoneH. J., BhadeshiaH. K. D. H. and WithersP. J.: ‘In situ monitoring of weld transformations to control weld residual stresses’, Mater. Sci. Forum, 2008, 571–572, 393–398.
31.
BhadeshiaH. K. D. H., AbreuH. and KunduS.: ‘Calculation of crystallographic texture due to displacive transformations’, Int. J. Mater. Res., 2008, 99, 342–346.
32.
KunduS.: ‘Transformation strain and crystallographic texture in steels’, PhD thesis, University of Cambridge, Cambridge, UK, 2007.
33.
ChangS. H. and WuS. K.: ‘Effect of cooling rate on transformation temperature measurements of Ti50Ni50 alloy by differential scanning calorimetry and dynamic mechanical analysis’, Mater. Charact., 2008, 59, (8), 987–990.
34.
SatohK.: ‘Transient thermal stresses of weld heat-affected zone by both-ends-fixed bar analogy’, Trans. Jpn Weld. Soc., 1972, 3, (1), 125–134.
35.
JonesW. K. C. and AlberryP. J.: ‘A model for stress accumulation in steels during welding’, Proc. Conf. on ‘Residual stresses in welded construction and their effects’, Vol. 1, 15–26; 1977, London, TWI.
36.
BhadeshiaH. K. D. H.: ‘Possible effects of stress on steel weld microstructures’, in ‘Mathematical modelling of weld phenomena’, (ed. H. Cerjak), Vol. 2, 71–119; 1998, London, Institute of Materials.
37.
FrancisJ. A., StoneH. J., KunduS., BhadeshiaH. K. D. H., RoggeR. B., WithersP. J. and KarlssonL.: ‘The effects of filler metal transformation temperature on residual stresses in a high strength steel weld’, J. Press. Vessel Technol., 2009, 131, 041401.1.